Rulison, A. J.

Publications and source records attributed to Rulison, A. J..

6 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1997

Measurements of Thermophysical Properties of Molten Silicon by a High-Temperature Electrostatic Levitator

Several thermophysical properties of molten silicon measured by the high-temperature electrostatic levitator at JPL are presented. They are density, constant-pressure specific heat capacity, hemispherical total emissivity, and surface tension. Over the temperature range investigated (1350 less than T(sub m) less than 1825 K), the measured liquid density (in g/cc) can be expressed by a quadratic function, pi(P) = p(sub m) - 1.69 x 10(exp -4)(T - T(sub m)) - 1.75 x 10(exp -7)((T - T(sub m))(exp 2) with T(sub m) and p(sub m) being 1687 K and 2.56 g/cc, respectively. The hemispherical total emissivity of molten silicon at the melting temperature was determined to be 0.18, and the constant-pressure specific heat was evaluated as a function of temperature. The surface tension (in 10(exp -3) N/m) of molten silicon over a similar temperature range can be expressed by sigma(T) = 875 - 0.22( T - T(sub m)).

Rhim, W. K.↗
NASA NTRS1997

Containerless Liquid to Solid Nucleation Pathways in Two Representative Grades of Commercially Available Zirconium

Experimental measurements were conducted to determine the solid metal nucleation pathways of radiatively cooling, molten zirconium spheres of two different commercially available purity grades in a high-vacuum, high-temperature electrostatic levitator. The ensemble distribution of maximum undercooling temperatures was interpreted using Poisson statistics to determine the temperature dependence of the solid metal nucleation rate. For a sample of nominally 99.95% pure zirconium, the results are consistent with heterogeneous solid metal nucleation either on static catalyst particles at least approx. 30 nm diameter or on a surface coating. For a sample of nominally 99% pure zirconium, however, it appears that heterogeneous solid metal nucleation occurred either on a polydispersion of approx. 10 nm (mean diameter) static catalyst particles or on dynamic catalyst particles that precipitated from a solution that became supersaturated as the melt cooled.

Rulison, A. J.↗
NASA NTRS1995

(abstract) Determination of the Specific Heat and Total Hemispherical Total Emissivity of the Highly Undercooled Zr(sub 41.2)Ti(sub 13.8)Cu(sub 12.5)Ni(sub 10.0)Be(sub 22.5) Alloy

High temperature high vacuum electrostatic levitation was combined with DSC experiments to determine the specific heat C(sub p) of the undercooled Zr(sub 41.2)Ti(sub 13.8)Cu(sub 12.5)Ni(sub 10.0)Be(sub 22.5) liquid as a function of temperature. The containerless approach made it possible to undercool the melt to the glass transition temperature without inducing nucleation. Because the cooling process was purely radiative, noncontact temperature measurement techniques could be used to determine the specific heat to total hemispherical emissivity ratio, C(sub p)/epsilon(sub t), for the undercooled liquid region. Using C(sub p) values which were independently obtained by DSC, epsilon(sub t) could be determined. With knowledge of C(sub p) of the undercooled liquid it was possible to determine other thermodynamic properties such as Gibbs free energy and entropy as a function of undercooling.

levitation thermodynamic properties undercooled al↗
NASA NTRS1995

(abstract) Undercooling Studies of the Bulk Metallic Glass Forming Zr(sub 41.2)Ti(sub 13.8)Cu(sub 12.5)Ni(sub 10.0)Be(sub 22.5) Alloy During Containerless Electrostatic Levitation Processing

Bulk glass forming metallic alloys have long been desired for technological applications and for investigation into liquid undercooling, solidification processes, and thermophysical properties. A glass forming alloy Zr(sub 41.2)Ti(sub 13.8)Cu(sub 12.5)Ni(sub 10.0)Be(sub 22.5) was used to investigate the thermal treatments affecting undercooling and vitrification. The experiments were performed using the high temperature high vacuum electrostatic levitator at JPL. A sample approximately 3 mm in diameter was melted, superheated, undercooled, and solidified while levitated in high vacuum. The results show that when the sample was held above its melting temperature for a sufficient period of time to dissolve oxides and then cooled faster than a critical cooling rate, it undercooled to the glass transition temperature, T(sub g), and formed a glassy alloy. The required critical cooling rate for metallic glass formation was obtained to be between 0.9 K per second and 1.2 K per second for the 42.4 mg sample.

levitation vitrification↗