A New Class of Oxyhalide Solid Electrolytes NaNbCl 6‐2x O x for Solid‐state Sodium Batteries

Abstract Sodium‐based batteries are gaining momentum due to the abundance and lower cost of sodium compared to lithium. Solid‐state sodium batteries can also provide further safety advantages. However, sodium‐based solid‐state electrolytes (SSEs) that meet all the rigorous requirements, such as high ionic conductivity, oxidative stability with the cathode, and ease of processability, are lacking. We present here a new class of sodium‐based oxyhalide electrolytes NaNbCl 6‐2x O x with a facile mechanochemical synthesis. The oxyhalide NaNbCl 4 O exhibits close to two orders of magnitude higher ambient‐temperature sodium‐ion conductivity (1.03×10 −4 S cm −1 ) compared to the halide counterpart NaNbCl 6 (3×10 −6 S cm −1 ). Structural motifs unique to the oxygen content in NaNbCl 6‐2x O x are identified with 23 Na and 93 Nb magic angle spinning nuclear magnetic resonance (MAS NMR) spectroscopy and x‐ray diffraction (XRD). Solid‐state sodium batteries assembled with NaNbCl 4 O electrolyte and the cobalt‐ and nickel‐free layered Na 0.70 Fe 0.3 Mn 0.65 Al 0.05 O 2 cathode exhibit a maximum discharge capacity of 155 mAh g −1 with good cycle life at ambient temperature.

Kmiec, Steven↗
DOE OSTI2024

A New Class of Oxyhalide Solid Electrolytes NaNbCl 6‐2x O x for Solid‐state Sodium Batteries

Abstract Sodium‐based batteries are gaining momentum due to the abundance and lower cost of sodium compared to lithium. Solid‐state sodium batteries can also provide further safety advantages. However, sodium‐based solid‐state electrolytes (SSEs) that meet all the rigorous requirements, such as high ionic conductivity, oxidative stability with the cathode, and ease of processability, are lacking. We present here a new class of sodium‐based oxyhalide electrolytes NaNbCl 6‐2x O x with a facile mechanochemical synthesis. The oxyhalide NaNbCl 4 O exhibits close to two orders of magnitude higher ambient‐temperature sodium‐ion conductivity (1.03×10 −4 S cm −1 ) compared to the halide counterpart NaNbCl 6 (3×10 −6 S cm −1 ). Structural motifs unique to the oxygen content in NaNbCl 6‐2x O x are identified with 23 Na and 93 Nb magic angle spinning nuclear magnetic resonance (MAS NMR) spectroscopy and x‐ray diffraction (XRD). Solid‐state sodium batteries assembled with NaNbCl 4 O electrolyte and the cobalt‐ and nickel‐free layered Na 0.70 Fe 0.3 Mn 0.65 Al 0.05 O 2 cathode exhibit a maximum discharge capacity of 155 mAh g −1 with good cycle life at ambient temperature.

Kmiec, Steven↗
DOE OSTI2023

Polycarbonate‐Based Solid‐Polymer Electrolytes for Solid‐State Sodium Batteries

Solid-polymer electrolytes comprised of polypropylene carbonate (PPC) and varied sodium bis(fluorosulfonyl)imide (NaFSI) salt concentrations are investigated for implementation as a conductive solid polymer electrolyte into solid-state cathode composites utilizing a sodium-layered oxide active material. The ionic conductivity generally increases with NaFSI salt content, reaching ≈1 mS cm −1 at 80 °C at the highest salt concentration (PPC:NaFSI = 0.5:1). Through an all-in-one slurry casting method, Na 2/3 Ni 1/3 Mn 2/3 O 2 cathode composites are fabricated in which the dispersed PPC electrolyte acts as the primary binder. Enabled by a bilayer polymer electrolyte system, cycling performance with the PPC cathode electrolyte is optimized with respect to salt concentration and anode material. The best cyclability is achieved with a moderate salt concentration electrolyte (PPC:NaFSI = 5:1), showcasing an initial capacity of 83 mA h g −1 with a remarkable 80% capacity retention after 150 cycles at C/5 rate and 60 °C. The superior performance of the lower salt concentration electrolyte is attributed to better electrochemical stability, as confirmed by linear sweep voltammetry and online electrochemical mass spectrometry measurements. In conclusion, these results underscore the potential of carbonate-based polymer electrolytes and the importance of balancing electrolyte conductivity and stability in cell design.

25 ENERGY STORAGE↗