NASA NTRS2014

Laser Ablation Cleaning of Self-Reacting Friction Stir Weld Seam Surfaces: A Preliminary Evaluation

Anodized aluminum panels were cleaned by three lasers at three separate sites with a view to determining whether more economical laser cleaning might supplant current manual cleaning methods for preparation of surfaces to be welded by the self-reacting friction stir process. Uncleaned panels yielded welds exhibiting residual oxide defect (ROD) and failing at very low stresses along the trace of the weld seam. Manually cleaned panels yielded welds without ROD; these welds failed at nominal stress levels along an angled fracture surface not following the weld seam trace. Laser cleaned panels yielded welds failing at intermediate stress levels. The inadequacy of the laser cleaning processes leaves questions: Was the anodized aluminum test too stringent to represent actual cleaning requirements? Were the wrong laser cleaning techniques/parameters used for the study? Is the laser cleaning mechanism inadequate for effective preweld surface cleaning?

Nunes, A. C., Jr.↗

NASA NTRS2012

Effects of Fusion Tack Welds on Self-Reacting Friction Stir Welds

In order to know whether fusion tack welds would affect the strength of self-reacting friction stir seam welds in 2195-T87 aluminum alloy, the fracture stresses of 144 tensile test coupons cut from 24 welded panels containing segments of friction stir welds were measured. Each of the panels was welded under unique processing conditions. A measure of the effect of the tack welds for each panel was devised. An analysis of the measures of the tack weld effect supported the hypothesis that fusion tack welds do not affect the strength of self-reacting friction stir welds to a 5% level of confidence.

Nunes, A. C., Jr.↗

NASA NTRS2007

Study of Radiographic Linear Indications and Subsequent Microstructural Features in Gas Tungsten Arc Welds of Inconel 718

This study presents examples and considerations for differentiating linear radiographic indications produced by gas tungsten arc welds in a 0.05-in-thick sheet of Inconel 718. A series of welds with different structural features, including the enigma indications and other defect indications such as lack of fusion and penetration, were produced, radiographed, and examined metallographically. The enigma indications were produced by a large columnar grain running along the center of the weld nugget occurring when the weld speed was reduced sufficiently below nominal. Examples of respective indications, including the effect of changing the x-ray source location, are presented as an aid to differentiation. Enigma, nominal, and hot-weld specimens were tensile tested to demonstrate the harmlessness of the enigma indication. Statistical analysis showed that there is no difference between the strengths of these three weld conditions.

Walley, J. L.↗

NASA NTRS2005

Welding in Space: Lessons Learned for Future In Space Repair Development

Welds have been made in the harsh environment of space only twice in the history of manned space flight. The United States conducted the M5 12 experiment on Skylab and the former Soviet Union conducted an Extravehicular Activity. Both experiments demonstrated electron beam welding. A third attempt to demonstrate and advance space welding was made by the Marshall Space Flight Center in the 90's but the experiment was demanifested as a Space Shuttle payload. This presentation summarizes the lessons learned from these three historical experiences in the areas of safety, design, operations and implementation so that welding in space can become an option for in space repair applications.

Russell, C. K.↗

NASA NTRS2004

Evaluation of Training Samples Manually Welded With the Universal Handtool in a Space Simulation Chamber

The international space welding experiment was designed to evaluate the universal handtool (UHT) functions as a welding, brazing, coating, and cutting tool for in-space operations. The UHT is an electron beam welding system developed by the Paton Welding Institute (PWI), Kiev, Ukraine, and operated a 8 kV with up to 1 kW of power. In preparation for conducting the space welding experiment, cosmonauts were trained to properly operate the UHT and correctly process samples. This Technical Memorandum presents the results of the destructive and nondestructive evaluation of the training samples made in Russia in 1998. It was concluded that acceptable welds can be made with the UHT despite the constraints imposed by a space suit. The lap joint fillet weld configuration was more suitable than the butt joint configuration for operators with limited welding experience. The tube braze joint configuration designed by the PWI was easily brazed in a repeatable manner.

Russell, C. K.↗

NASA NTRS1999

Low-Pressure Gas Effects on the Potency of an Electron Beam Against Ceramic Cloth

An 8-kv electron beam with a current in the neighborhood of 100 mA from the Ukrainian space welding "Universal Hand Tool" (UHT) burned holes in Nextel AF-62 ceramic cloth designed to withstand temperatures up to 1,427 C. The burnthrough time was on the order of 8 scc at standoff distances between UHT and cloth ranging from 6-24 in. At both closer (2 in.) and farther (48 in.) standoff distances the potency of the beam against the cloth declined and the burnthrough time went up significantly. Prior to the test it had been expected that the beam would lay down a static charge on the cloth and be deflected without damaging the cloth. The burnthrough is thought to be an effect of partial transmission of beam power by a stream of positive ions generated by the high-voltage electron beam from contaminant gas in the "vacuum" chamber. A rough quantitative theoretical computation appears to substantiate this possibility.

Nunes, A. C., Jr.↗

NASA NTRS1999

How an Electron Beam (Eventually) Penetrates Ceramic Cloth

In anticipation of the International Space Welding Experiment (ISWE) the effect of an electron beam was investigated on Nextel AF-62 ceramic cloth designed to withstand temperatures up to 1427 C. It was anticipated that the cloth would take a static charge that would repel the beam and remain undamaged. It was found that after some seconds the impinging beam penetrated penetrated the cloth. Further, the penetration time went up significantly both at longer and at closer standoff distances. A tentative explanation appears to fit the observed facts. The electrons in the beam generate positive ions by collisions with the contaminant gas molecules in the vacuum chamber. The positive ions transfer a small but significant fraction of the beam power to the cloth. Under the impingement of the positive ions the cloth heats up until sufficient outgassing occurs to initiate arcing. Once arcing occurs the full beam power impinges on the cloth and, almost instantaneously, burns a hole.

Nunes, A. C., Jr.↗

NASA NTRS1991

The effects of multiple repairs on Inconel 718 weld mechanical properties

Inconel 718 weldments were repaired 3, 6, 9, and 13 times using the gas tungsten arc welding process. The welded panels were machined into mechanical test specimens, postweld heat treated, and nondestructively tested. Tensile properties and high cycle fatigue life were evaluated and the results compared to unrepaired weld properties. Mechanical property data were analyzed using the statistical methods of difference in means for tensile properties and difference in log means and Weibull analysis for high cycle fatigue properties. Statistical analysis performed on the data did not show a significant decrease in tensile or high cycle fatigue properties due to the repeated repairs. Some degradation was observed in all properties, however, it was minimal.

Russell, C. K.↗