Russell, Dennis A. | Search NASA

NASA NTRS2001

Effects of Electrons, Protons, and Ultraviolet Radiation on Thermophysical Properties of Polymeric Films

The response of coated thin polymer films to ultraviolet (UV), electron and proton radiation simultaneously has been evaluated, with selected measurements in situ. Exposure was intended to simulate the electron and proton radiation environment near the Earth-Sun Lagrangian points (LI and L2) for five years and approximately 1000 equivalent solar hours (ESH) UV. These orbital environments are relevant to several potential missions such as the Next Generation Space Telescope and Geomagnetic Storm Warning, both of which may use thin film based structures for a sunshade and solar sail, respectively. The thin film candidates (12.5 micrometers thick) consisted of commercially available materials (Kapton(R) E, HN, Upilex(R) S, CP-1, CP-2, TOR-RC, and TOR-LMBP) that were metalized on one side with vapor deposited aluminum. All of the films are aromatic polyimides, with the exception of TORLMBP, which is a copoly(arylene ether benzimidazole). The films were exposed as second surface mirrors and the effects of the exposure on solar absorptance, thermal emittance, and tensile properties were determined. The in situ changes in solar absorptance from Kapton(R) and Upilex(R) were less than 0. 1, whereas the solar absorptance of TOR and CP films increased by more than 0.3 without saturating. The thermal emittance measurements also showed that the Kapton(R) and Upilex(R) materials increased only 1-2%, but the remaining materials increased 5-8%. Based on tensile property measurements made in air following the test, the failure stress of every type of polymer film decreased as a result of irradiation. The polymers most stable in reflectance, namely Upilex(R) and Kapton(R), were also the strongest in tension before irradiation, and they retained the greatest percentage of tensile strength. The films less stable in reflectance were also weaker in tension, and lost more tensile strength as a result of irradiation. The apparent failure strain (as a percent of original gage length) of every type of polymer film except TOR-RC, decreased as a result of irradiation.

Russell, Dennis A.↗

NASA NTRS2000

Simulated Space Environmental Testing on Thin Films

An exploratory program has been conducted, to irradiate some mature commercial and some experimental polymer films with radiation simulating certain Earth orbits, and to obtain data about the response of each test film's reflective and tensile properties. Protocols to conduct optimized tests were considered and developed to a "prototype" level during this program. Fifteen polymer film specimens were arranged on a specially designed test fixture. The fixture featured controlled exposure areas, and protected the ends of the samples for later gripping in tensile tests. The fixture featured controlled exposure areas, and protected the ends of the samples for later gripping in tensile tests. The fixture containing the films was installed in a clean vacuum chamber where protons, electrons and solar ultraviolet (UV) radiation could simultaneously irradiate the specimens. Near realtime UV rates were used, whereas proton and electron rates were accelerated appreciably to simulate 5 years in orbit during a two month test. Periodically, the spectral reflectance of each film was measured in situ. After the end of the irradiation, final reflectance measurements were made in situ, and solar absorptance values were derived for each specimen. These samples were then measured in air for thermal emittance and for tensile strength. Most specimens withstood the irradiation intact, but with reduced reflectance (increased solar absorptance). Thermal emittance changed slightly in several materials, as did their tensile strength and elongation at break. Conclusions are drawn about the performance of the films. Simulated testing to an expected 5 year dose of electrons and protons consistent with those expected at L2 and 0.98 AU orbits and 100 equivalent solar hours exposure.

Russell, Dennis A.↗