Search NASA⌕ Search

Engineering topics

S. M. Arnold

Publications and source records attributed to S. M. Arnold.

Micromechanics-based Modeling of Laminated SiC/SiC Ceramic Matrix Composites

The behavior and response of ceramic matrix composites (CMCs), in particular silicon carbide fiber reinforced silicon carbide matrix (SiC/SiC), is affected by many factors such as variation of fiber volume fraction, residual stresses resulting from processing of the composites at high temperature, random microstructures, and the presence of matrix flaws (e.g., voids, pores, cracks etc.) as well as general material nonlinearity and heterogeneity that occurs randomly in a composite. Residual stresses arising from the phase change of constituents are evaluated in this paper and it is shown that they do influence composite strength and need to be properly accounted for. Additionally, the microstructures (location of fiber centers, coating thickness etc.) of advanced CMCs are usually disordered (or random) and fiber diameter and strength typically have a distribution. They rarely resemble the ordered fiber packing (square, rectangular, or hexagonal) that is generally assumed in micromechanics-based models with periodic boundary conditions for computational expediency. These issues raise the question of how should one model such systems effectively? Can an ordered hexagonal packed repeating unit cell (RUC) accurately represent the random microstructure behavior? How many fibers need to be included to enable accurate representation? Clearly, the number of fibers within an RUC must be limited to insure a balance between accuracy and efficiency. NASA’s in-house micromechanics-based code MAC/GMC provides a framework to analyze such RUCs for the overall composite behavior and the FEAMAC computer code provides linkage of MAC/GMC to the commercial FEA code, ABAQUS. The appropriate level of discretization of the RUC as well as the analysis method employed, i.e., Generalized Method of Cells (GMC) or High Fidelity Generalized Method of Cells (HFGMC), is investigated in this paper in the context of a unidirectional as well as a cross-ply laminated CMC. Results including effective composite properties, proportional limit stress (an important design parameter) and fatigue are shown utilizing both GMC as well as HFGMC. Finally, a few multiscale analyses are performed on smooth bar test coupons as well as test coupons with features such as open-hole and double notches using FEAMAC. Best practices and guidance are provided to take these phenomena into account and keep a proper balance between fidelity (accuracy) and efficiency. Following these guidelines can account for important physics of the problem and provide significant advantages when performing large multiscale composite structural analyses.

Ceramic Matrix Composites↗

Reduction of Thermal Residual Stresses in Advanced Metallic Composites Based upon a Compensating/Compliant Layer Concept

High residual stresses within metal and intermetallic matrix composite systems can develop upon cooling from the processing temperature to room temperature due to the coefficient of thermal expansion (CTE) mismatch between the fiber and matrix. As a result, within certain composite systems, radial, circumferential, and/or longitudinal cracks have been observed to form at the fiber-matrix interface region. The compliant layer concept (insertion of a compensating interface material between the fiber and matrix) has been proposed to reduce or eliminate the residual stress buildup during cooling, and thus minimize cracking. The present study investigates elastic-plastically the viability of the proposed compliant layer concept. A detailed parametric study was conducted utilizing a unit cell model consisting of three concentric cylinders to determine the required character (i.e., thickness and mechanical properties) of the compliant layer as well as its applicability. The unknown compliant layer mechanical properties were expressed as ratios of the corresponding temperature dependent Ti-24Al-11Nb (a/o) matrix properties. The fiber properties taken were those corresponding to SCS-6 (SiC). Results indicated that the compliant layer can be used to reduce, if not eliminate, radial and circumferential residual stresses within the fiber and matrix and therefore also reduce or eliminate the radial cracking. However, with this decrease in in-plane stresses, one obtains an increase in longitudinal stress, thus potentially initiating longitudinal cracking. Guidelines are given for the selection of a specific compensating/ compliant material, given a perfectly bonded system.

S. M. Arnold↗