DOE OSTI2024

High-pressure phase transitions in a laser directed energy deposited Fe-33Cu Alloy

Here, additively manufactured Fe-Cu alloys contain both equilibrium face-centered cubic (FCC) and metastable body-centered cubic (BCC) crystal structure Cu precipitates depending on their size. However, the stability of these nanoscale precipitates under extreme conditions such as high pressures has not been reported. This study investigates the phase transformations and microstructural stability of laser directed energy deposition (DED-LB) made Fe67Cu33 alloy (nominal composition in at.%) under high static pressure deformation using in-situ synchrotron X-ray diffraction under pressure, postmortem high-resolution scanning transmission electron microscopy (HR-STEM), and molecular dynamics (MD) simulations. In-situ XRD results reveal a reversible phase transformation from BCC to the hexagonal close-packed (HCP) structure in the Fe grains at an onset pressure of 16.4 GPa, significantly higher than reported in the literature for pure Fe. Although no high-pressure phase transition was observed in the FCC Cu grains through XRD, HR-STEM analysis uncovers a phase transition to the HCP structure in nanoscale metastable BCC Cu precipitates within the BCC Fe matrix. After decompression, the Fe matrix reverted back to the BCC structure with periodic lath martensite, while regions of the nanoscale BCC Cu precipitates retained the metastable HCP structure. MD simulations support the BCC → HCP transition in the embedded nanoscale coherent Cu precipitates, consistent with the classical Burgers mechanism. Thus, by leveraging in-situ XRD observation, postmortem high-resolution S/TEM microscopy, and MD simulations, this study offers profound insights into the distinctive phase transformations induced by high pressure in DED-LB Fe67Cu33 alloy, which is distinguished by its hierarchical microstructure.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Nanoscale phase transition in impact indented Mo/Cu thin films

The study reveals a size effect in deformation mechanisms via unique structural transitions in sputter deposited fcc/bcc nanolayers under high strain rate impact nanoindentation as layer thickness is reduced from around 100-200 nm to around 5 nm. Here, the indented 5 nm Cu/5 nm Mo multilayer films characterized via cross-sectional scanning/transmission electron microscopy have revealed a phase transition in the 5 nm thick Mo layers from BCC to a coherent metastable FCC structure and fine deformation twins in the 5 nm Cu layers inside a shear band that is approximately 500 nm long and inclined to the layer interfaces. In contrast, thicker layers, 80 nm Cu/180 nm Mo, show different deformation behavior with uneven layer thickness reduction, shearing of Cu layers, and bending of the columnar Mo grains beneath the indentation without any sign of shear band and localized phase transformation.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Deformation behavior of crystalline/amorphous Al-Si nanocomposites with nanolaminate or nanofibrous microstructures

Deformation mechanisms in sputter-deposited crystalline Al/amorphous Si nanocomposites with nanolaminate or nanofibrous morphology are characterized by nanoindentation, micropillar compression testing and transmission electron microscopy (TEM). The nanofibrous composite having crystalline Al nanofibers with ~40–50 nm in length and 15–20 nm in diameter embedded in amorphous Si exhibits strain hardening to a maximum flow stress of 2.9 GPa and no shear band (SB) formation in compression up to plastic strain exceeding 24%. On the other hand, nanolaminate composite that is composed of 80 nm crystalline Al layers and 20 nm amorphous Si layers exhibits catastrophic SBs starting at plastic strains in the range of 5–10%. Cross-sectional TEM of the deformed samples reveals a high density of stacking faults and twin boundaries in Al nanofibers and no microshear bands in the nanofibrous composite, suggesting plastic deformation in amorphous Si phase and crystalline Al nanofibers. Further, molecular dynamics simulations revealed that the plastic deformation in amorphous Si phase in the cosputtered films could be favored by the decrease in flow strength of amorphous Si with increasing Al solute concentration trapped in Si.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

Strain-rate dependent deformation mechanisms in single-layered Cu, Mo, and multilayer Cu/Mo thin films

Here, strain-rate sensitivity and rate-dependent hardness, over a range of 10 -2 to 10 2 s -1 , of sputter-deposited single-layered Cu, Mo, and 5 nm Cu/ 5 nm Mo, and 100 nm Cu/ 100 nm Mo multilayer films with a total film thickness of 5 μm were measured using nanoindentation. The plastic zone underneath the nanoindents was characterized via cross-sectional transmission electron microscopy (XTEM). The multilayer films exhibited enhanced hardness but slightly reduced strain-rate sensitivity with decreasing layer thickness from 100 nm to 5 nm. Only the 5 nm Cu/ 5 nm Mo multilayer film exhibited shear bands underneath the nanoindents, and the size of the shear bands increased with increasing strain rate. In contrast, the 100 nm Cu/ 100 nm Mo multilayer film exhibited material pile-up around the indents and significant nanotwinning within Cu grains. The effect of strain rate and layer thickness on the hardness and strain rate sensitivity of the multilayer thin films is interpreted using a modified confined layer slip (CLS) model. The reduced rate sensitivity at 5 nm as compared to 100 nm correlates with abundant growth nanotwins in the Cu grains in 100 nm and formation of shear bands in 5 nm multilayers. In single layer films, a substructure with a high density of dislocations was observed consistent with the plastic strain gradient in the indent plastic zone. No evidence of deformation twins was noted in any of the samples.

36 MATERIALS SCIENCE↗