DOE OSTI2023

Improved Thermal Stability of Oxysulfide Glassy Solid-State Electrolytes

In this study, the crystallization kinetics of (oxy)sulfide 70Li 2 S·(30-x)P 2 S 5 ·xP 2 O 5 (x = 0, 2, 5) solid-state electrolytes are reported. It was found that 5 mol% P 2 O 5 glass co-former slowed the crystallization rate of the Li 7 P 3 S 11−x/4 O x/4 ceramic phase by a factor of 10. After 10 min at 230 °C, a 70Li 2 S·30P 2 S 5 sulfide glass was 92% devitrified whereas a 70Li 2 S·25P 2 S 5 ·5P 2 O 5 oxysulfide glass was only 8% devitrified. The improved thermal stability of oxysulfide glasses was then utilized to demonstrate the fabrication of a standalone, reinforced SSE separator by hot pressing. More importantly, it was recognized that the microstructure of 70Li 2 S·25P 2 S 5 ·5P 2 O 5 oxysulfide SSE separators could be modified by hot pressing without changing ionic conductivity. This result was achieved because the precipitation of a superionically conductive Li 7 P 3 S 11−x/4 O x/4 ceramic phase was limited. A study was then conducted to determine what effect microstructure has on the susceptibility of SSE separators to shorting by lithium metal penetration. Hot-pressed separators were found to be more susceptible to shorting than cold-pressed separators. X-ray Computer Tomography (XCT) of post-mortem samples showed that hot-pressed samples failed by transverse microcrack pathways, which underscores the importance of low defect density in dense SSE separators.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

Sulfide glass solid-state electrolyte separators for Li metal batteries: using an interlayer to increase rate performance and reduce stack pressure

We report on the solubility of (Li 2 S) 60 (SiS 2 ) x (P 2 S 5 ) 40–x , (0 ≤ x ≤ 40) sulfide glass solid-state electrolytes in the 1:1 (v/v) DME:DOL solvent mixture, a popular choice for lithium metal battery liquid electrolytes. SiS 2 -rich glasses within the compositional range of (Li 2 S) 60 (SiS 2 ) x (P 2 S 5 ) 40–x (28 ≤ x ≤ 40) were found to be functionally insoluble in DME:DOL. Hybrid symmetric test cells with a thin liquid electrolyte layer (0.6 M LiTFSI + 0.4 M LiNO 3 in 1:1 (v/v) DME:DOL) at the interface between lithium metal electrodes and an insoluble (Li 2 S) 60 (SiS 2 ) 28 (P 2 S 5 ) 12 glass wafer were tested. Hybrid test cells delivered a critical current density of 3.0 mA cm –2 at 25 °C and 0.1 MPa, which is nearly double the CCD of comparable dry symmetric test cells cycled at 10× higher stack pressure.

25 ENERGY STORAGE↗

DOE OSTI2022

Consolidation of composite cathodes with NCM and sulfide solid-state electrolytes by hot pressing for all-solid-state Li metal batteries

In this study, hot pressing was evaluated as a method of cell fabrication to increase the energy density of next-generation all-solid-state batteries with NCM active material and sulfide solid-state electrolyte. Hot pressing involves consolidating glassy sulfide electrolyte by the application of pressure at a temperature above the electrolyte’s glass transition temperature. Typically, cell stacks are formed at room temperature and retain 15–30% porosity that limits cell energy density. On the other hand, the porosity of hot-pressed cell stacks is reduced to less than 10%. The electrochemical function of hot-pressed cathode composites was assessed as a function of active material and solid-state electrolyte compositions. Specifically, LiNi 0.85 Co 0.10 Mn 0.05 O 2 and LiNi 0.6 Co 0.2 Mn 0.2 O 2 were studied in combination with either glassy Li 7 P 3 S 11 , glassy Li 3 PS 4 , or β-Li 3 PS 4 solid-state electrolytes. Cathode composites composed of LiNi 0.6 Co 0.2 Mn 0.2 O 2 and Li 3 PS 4 maintained the best function after hot pressing at 200 °C and 370 MPa for 10 min. It was found that LiNi 0.6 Co 0.2 Mn 0.2 O 2 ’s resistance to microcracking and the inherent stability of Li 3 PS 4 ’s fully de-networked local structure are critical to maintain good electrochemical function after hot pressing. Furthermore, the results of this study show that hot pressing reduces porosity in the cathode composite and confirms the feasibility of cathode support of consolidated, reinforced glass separators.

25 ENERGY STORAGE↗