Temperature Dependent E2 Raman Modes in the ZnCoO Ternary Alloy
The anharmonic properties of low and high frequency E2 modes of ZnO and Co doped ZnO were investigated using Raman scattering spectroscopy. We have determined the behavior of frequency, linewidths, and lifetime of E2 modes in the temperature range from 80 to 800 K. In the case of E2(high) mode the frequency shift towards the lower energy side was analyzed in light of the theory of anharmonic phonon-phonon interaction and thermal expansion of the lattice, and the linewidth behavior was analyzed in terms of anharmonic effect of three-phonon decay mechanism. But in the case of E2(low), the linewidth and frequency behaved practically harmonic with respect to temperature and independent of Co substitutions. It is found that the E2(high) phonon anharmonicity is higher for ZnCoO alloys than in pure ZnO and it increases with the compositional disorder. The low temperature lifetime of E2 phonon in ZnO, 1 % and 3% Co doped ZnO were found to be 1.S2, 1.74, and 1.54 ps, respectively.