DOE OSTI2022

Fracture behavior of a melt-infiltration-processed SiC/Si composite at 900°C in argon, air, and steam

The fracture behavior of a melt-infiltration-processed SiC/Si composite, used to mimic the matrices of industrial fiber-reinforced ceramic composites, was examined in different atmospheres and temperatures. Specimens tested in four-point bending at 900 °C in oxygen-gettered argon, dry air, or steam-rich atmospheres exhibited higher average fracture strengths than specimens tested at 25°C. Higher mean fracture strength values were obtained for specimens tested in dry air or in a steam-rich atmosphere at 900°C than for specimens tested in high-purity, oxygen-gettered argon at this temperature. The increased fracture strengths obtained in air and in steam-rich atmospheres coincided with increased specimen oxidation and apparent oxide filling and blunting of flaws in these composites. Further, a transition in the location of catastrophic failure, from sites of preexisting damage created by Vickers indentations for tests in argon to other locations for tests in air or steam-rich atmospheres, was also consistent with such apparent oxide filling/blunting of indentation-induced flaws.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Residual elastic strain evolution due to thermal cycling of a ceramic-metal composite (WC-Cu) via high energy X-ray diffraction and analytical modeling

Residual stress, when superimposed with in-service loading, can significantly reduce the lifetime and performance of a component. Ceramic-metal composites are susceptible to residual stresses due to the thermal expansion mismatch of the ceramic and metallic phases. The WC-Cu composite explored in the present study provides a promising combination of thermal conductivity and strength properties, while exhibiting counterintuitive improvements in strength and ductility after thermal cycling. Further, this work quantifies the evolution of the residual elastic strains as a result of processing and cyclic thermal loading in a co-continuous WC-Cu composite through experimental high energy X-ray diffraction and kinetics-based modeling. Both analyses indicate that processing-induced residual tensile stress in the copper phase is relieved upon subsequent thermal cycling, with kinetics modeling revealing the cyclic-dependent nature of the active power-law creep mechanisms. The results indicate that, through stress relaxation, this material system maintains structural stability during thermal cycling. The illustrated kinetics of relaxation can inform general material processors and designers of ceramic-metal composites to minimize detrimental residual stress and improve performance of these material systems.

36 MATERIALS SCIENCE↗
DOE OSTI2022

The importance of maldistribution matching for thermal performance of compact heat exchangers

Compact heat exchangers have gained increased attention in recent years, particularly in demanding applications where high temperatures, high pressures, and/or high power densities are required. For decades, the heat exchanger (HX) community believes that flow maldistribution is a key factor for HX effectiveness, that is, reducing the degree of flow maldistribution (MALD) can help increase the HX effectiveness. Therefore, significant efforts have been devoted in the past to optimizing the header geometry to minimize flow maldistribution. This work was initially motivated by this, and the original goal was to figure out a HX header design with the lowest maldistribution. However, by systematically constructing a comprehensive maldistribution matrix, the analysis revealed that the HX effectiveness is not actually determined by the MALD, but instead dominated by the degree of maldistribution mismatch (MISM). This conclusion was also theoretically generalized, which indicated that matching of the local heat capacity rate is key for achieving maximum performance. The MISM provides a local means of tracking this information, while the MALD only provides a global approximation of the maldistribution itself. With this new perspective, flow maldistribution needs not necessarily be avoided, but instead matched between two fluid streams, to improve the HX performance. We demonstrated that by carefully designing the header geometry to match the velocity profiles of the two fluids in a 2 MW PCHE with molten salt and supercritical carbon dioxide (sCO2) as the heat transfer fluids, the HX could achieve a higher effectiveness even when the maldistribution increased. Finally, a technoeconomic study using a CSP system as an example revealed that the use of this new HX design paradigm could result in CSP capital cost savings as large as 16.6%.

32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗
DOE OSTI2022

Mechanically-, Thermally, and Chemically-Robust High-Temperature Ceramic Composites

In an effort to lower the levelized cost of electricity generated by Concentrated Solar Power (CSP) plants, the heat-to-electricity conversion efficiency may be increased by operating such plants with higher turbine inlet temperatures using closed Brayton cycles with high-pressure, supercritical carbon dioxide (sCO 2 ) as the working fluid. For example, if the turbine inlet temperature is raised to ≥750°C, in combination with sCO2 closed Brayton cycles, the relative heat-to-electricity efficiency may be raised by more than 20% (compared to subcritical steam Rankine cycles operating with turbine inlet temperatures ≤550°C). The associated reduction in the cost of dispatchable electricity from such CSP plants (utilizing high-temperature thermal energy storage) would be an important breakthrough on the path towards direct competition with fossil-fuel-based plants. A key barrier to achieve such high-temperature efficient operation has been the limited thermomechanical performance of metal alloys used in compact, primary printed circuit- type heat exchangers (PCHEXs) for heat transfer to high-pressure sCO 2 . The maximum allowed stresses for the use of conventional stainless steels and nickel-based superalloys at high sCO 2 pressures (≥20 MPa) decline rapidly at temperatures ≥550°C. This project has been focused on demonstrating the desired high-temperature properties and attractive manufacturing characteristics of mechanically-, thermally-, and chemically-robust ceramic/metal composites (cermets), in order to allow for the use of such composites in primary PCHEXs for heat transfer to sCO 2 at ≥750°C and ≥20 MPa in CSP plants. Prior work with high-temperature, co-continuous carbide/refractory metal cermets, such as ZrC/W composites, has already demonstrated: i) the attractive combination of high-temperature properties exhibited by such materials (e.g., high values of stiffness, failure strength, and thermal conductivity at 800°C), and ii) cost-effective processes for manufacturing PCHEX plates comprised of such cermets with tailorable channel patterns. However, ZrC/W cermets were not found to be inherently corrosion resistant in sCO 2 at 750°C and 20 MPa. While the application of a Cu coating to ZrC/W surfaces, along with a modest addition (50 ppm) of CO to CO 2 , rendered such composites resistant to corrosion for 1000 h in such sCO 2 -based fluids at 750°C, such additional steps would increase the design complexity of such cermet-based components. An alternative approach (the focus of this project) is to develop mechanically-robust, cost- effective cermets that are inherently resistant to high-temperature oxidation in air and CO 2 . The overall goals of this project have been to demonstrate: i) the oxidation resistance of at least one cermet at 750°C in air and in CO 2 (i.e., with a projected annual corrosion ≤30 μm), ii) the mechanically robust nature of at least one cermet at 750°C (i.e., with an average failure strength ≥200 MPa), and iii) that the selected cermet can be manufactured via low-cost forming techniques.

14 SOLAR ENERGY↗
DOE OSTI2022

Mitigation of Molten Salt Corrosion

The desire to increase the peak operational temperature of Concentrated Solar Power (CSP) plants to lower the levelized cost of CSP-derived electricity, has led to consideration of an earth-abundant, low-cost, thermally-stable, molten MgCl 2 -KCl-NaCl (40-40-20 mole%) salt for high-temperature thermal energy storage and heat transfer. The reliable, long-term containment of such a molten salt is challenging, however, due to the corrosion of cost-effective, high-temperature structural metal alloys in this salt (particularly if this salt is contaminated with oxygen-bearing species). This project has been focused on: i) development of equipment for evaluating corrosion kinetics in molten chlorides under well-controlled thermal, fluid dynamic, and atmospheric conditions at CSP-relevant temperatures, ii) use of such equipment to evaluate the influence of forced convection on corrosion kinetics (to determine the role of liquid phase diffusion on such corrosion), and iii) identifying a corrosion-mitigation strategy that can be industrially applied to achieve a projected annual corrosion ≤30 μm at CSP-relevant temperatures. The overall goals of this project have been: i) to understand the rate-limiting step(s) and associated kinetic laws governing corrosion in molten chlorides at 750°C, ii) to determine key operational parameters affecting the corrosion kinetics in molten salts, and iii) to demonstrate the tailoring of such parameters to appreciably reduce such corrosion.

14 SOLAR ENERGY↗
DOE OSTI2022

Validation of the Porous Medium Approximation for Hydrodynamics Analysis in Compact Heat Exchangers

Compact heat exchangers (HXs) have gained attention in recent years in various fields such as solar and nuclear power generation, oil and gas, and refrigeration due to their low cost, high power density, and robustness in high-pressure and/or high-temperature environments. However, the large difference between a compact HX's overall dimensions (~m) and the much smaller scale of its channels (~mm) makes it challenging to model the entire HX at once, due to computational limitations. In this work, we treat the channeled region of a compact HX as a porous medium (PM) to circumvent the need to model/mesh each individual channel. This allows us to simulate the entire HX, including both the header and channeled regions while maintaining the computational cost at a practical level. Although the porous medium approach has been used to model heat exchangers, its validity is still questionable because (1) the resistance coefficients are heavily data-based and thus difficult to be applied to new heat exchangers and (2) the validation has been focused on matching the overall pressure drop in the channel region, which does not address whether such model can predict detailed pressure and velocity field. For the first time, this work addresses under what circumstances and with what uncertainty does the PM approach work for hydrodynamics modeling in compact HXs. By answering these questions, we introduce the PM approach as a powerful tool for HX hydrodynamics modeling that can predict not only the overall pressure drop but also the detailed pressure and velocity distributions.

Engineering↗
DOE OSTI2021

Design of a 2 MW ZrC/W-based molten-salt-to-sCO 2 PCHE for concentrated solar power

To increase the power cycle efficiency and lower the levelized cost of electricity (LCOE) of concentrated solar power (CSP) plants, printed circuit heat exchangers (PCHEs) capable of operating above 700 °C with molten chloride salt and a sCO 2 -based fluid are needed. In this paper, the design of a high-pressure, high-temperature, 2 MW PCHE comprised of a thermomechanically-robust, zirconium carbide/tungsten (ZrC/W) composite is conducted for CSP plants. The ZrC/W composite is a material with high thermal conductivity, high stiffness, and high failure strength at high temperatures, along with excellent resistance to thermal cycling and thermal shock. In this work, a thermomechanical design analysis was conducted to select appropriate material thicknesses of the ZrC/W plates, and to determine the geometrical dimensions and the thermal performance of the PCHE. The influences of the plate number and heat exchanger length on power density and pressure drop have also been systematically investigated. Economic analyses were conducted to compare the cost of ZrC/W-based PCHEs to those comprised of IN740H (a state-of-the-art, nickel-based superalloy) and 316 stainless steel (316SS). Finally, at a sufficiently high plate production rate, the manufacturing cost of ZrC/W-based PCHEs can be significantly lower, while achieving a much higher power density, compared with state-of-the-art, nickel alloy-based and stainless steel-based PCHEs.

14 SOLAR ENERGY↗
DOE OSTI2021

Air-stable, earth-abundant molten chlorides and corrosion-resistant containment for chemically-robust, high-temperature thermal energy storage for concentrated solar power

A dramatic reduction in man-made CO 2 emissions could be achieved if the cost of electricity generated from concentrated solar power (CSP) plants could become competitive with fossil-fuel-derived electricity. The solar heat-to-electricity conversion efficiency of CSP plants may be significantly increased (and the associated electricity cost decreased) by operating CSP turbines with inlet temperatures ≥750 °C instead of ≤550 °C, and by using thermal energy storage (TES) at ≥750 °C to allow for rapidly dispatchable and/or continuous electricity production. Unfortunately, earth-abundant MgCl 2 -KCl-based liquids currently being considered as low-cost media for large-scale, high-temperature TES are susceptible to oxidation in ambient air, with associated undesired changes in liquid composition and enhanced corrosion of metal alloys in pipes and tanks containing such liquids. In this paper, alternative high-temperature, earth-abundant molten chlorides that are resistant to oxidation in ambient air are identified via thermodynamic calculations. Here, the oxidation resistance, and corrosion-resistant containment, of such molten chlorides at 750 °C are then demonstrated. Such an air-tolerant strategy, involving chemically-robust, low-cost TES media paired with effective containment materials, provides a critical advance towards the higher-temperature operation of, and lower-cost electricity generation from, CSP plants.

14 SOLAR ENERGY↗
DOE OSTI2020

Corrosion of Al 2 O 3 /Cr and Ti 2 O 3 /Cr composites in flowing air and CO 2 at 750°C

Hot-pressed Al 2 O 3 /Cr and Ti 2 O 3 /Cr composites were exposed to synthetic air or CO 2 at 750 °C. The Al 2 O 3 /Cr composites formed external Cr 2 O 3 scales, and exhibited slow parabolic oxidation kinetics, in both gases. The Cr 2 O 3 scales formed in CO 2 possessed finer grains, and thickened at a faster rate, than Cr 2 O 3 scales formed in air. The Ti 2 O 3 /Cr composites formed thick external TiO 2 scales with internal oxidation zones that also contained Cr 2 O 3 scales on subsurface Cr grains. After 20 h at 750 °C, the Ti 2 O 3 /Cr composites exhibited parabolic oxidation kinetics in both gases, although the oxidation rates were significantly higher than for the Al 2 O 3 /Cr composites.