NASA NTRS2023

Dynamic Crush Performance of Thermoplastic and Resin Infused Thermoset Triaxially Braided Composite Structures

Dynamic crush tests were conducted on triaxially braided composite tubes and C-channel structural elements to measure their relative energy absorbing characteristics. The elements were manufactured from triaxially braided [0/+60/-60] T700 fiber preforms with two different resin systems, a PR520 thermoset resin and a LM-PAEK thermoplastic resin. T700/PR520 composite tubes and C-channel elements were manufactured using a resin infusion process. T700GC/LMPAEK composite tubes were manufactured by braiding slit tape prepreg onto cylindrical mandrels. Consolidation pressure was applied through thermally activated shrink tape in an oven. The energy absorbing characteristics of the composite elements were measured using a pneumatically actuated sled with a flat-faced impacting mass, which provided several independent measurements of force, displacement, and energy absorption. The parameter primarily used for comparison between the systems was the specific energy absorption (SEA), a measure of energy absorbed per unit crushed length. The T700/LMPAEK tubes performed slightly better than T700/PR520 tubes, with an approximately 9% higher SEA. T700/PR520 tubes had over 20% higher SEA than C-channels made from the same material. Additional tests were conducted on tubes using a tapered-conical impactor to force the tubes to fail in circumferential tension. This type of impact significantly reduced the energy absorption.

Composite Materials↗
NASA NTRS2023

Manufacturing and Mechanical Testing of TC1225/LM-PAEK and TC1200/PEEK Thermoplastic Composite Panels

Development of thermoplastic composites (TPCs) for aerospace structures is experiencing renewed enthusiasm attributed to the availability of rapid manufacturing technology, ease of joining through fusion welding processes, and the successful utilization of the material in flight critical structures. Semicrystalline thermoplastics such as polyether ether ketone (PEEK), polyether ketone ketone (PEKK), and polyphenylene sulfide (PPS) have been successfully demonstrated as thermoplastic skins, keel beams, and angle brackets for commercial aircraft. Composite specimens were fabricated from the Toray TC1225 and TC1200 unidirectional prepreg systems and tested to gain confidence with NASA in-house TPC processing as part of the Thermoplastics Development for Exploration Application (TDEA) project. TC1225 is a relatively new material system that uses T700GC fibers and low-melt polyaryl ether ketone (LM-PAEK) resin. TC1200 is the latest version of a material system that has been available for several decades with AS4 fibers and PEEK resin. Results for ultrasonic inspection, optical microscopy, acid digestion, and differential scanning calorimetry establish the quality of the panels. Mechanical test data for unnotched and notched laminate tension and compression as well as compression after impact provide data for equivalency assessment and support material selection in TDEA. Satisfactory equivalence of the TC1225 results and the National Center for Advanced Materials Performance (NCAMP) database was found. The results indicate high-quality manufacturing was achieved, and the resulting mechanical test data are in agreement with that in the literature.

Thermoplastic Composites↗
NASA NTRS2023

Experimental Tests to Characterize the Behavior and Properties of IM7-8552 Composite

This document summarizes the test procedures for characterizing the quasi-static (QS), room temperature (RT) behavior of IM7/8552 unidirectional composite material. All testing reported in this document follow applicable ASTM1 test standards as closely as possible, with any deviations reported. The overall objective is to develop a framework for the creation of MAT213 material input for use in the LS-DYNA program (LSTC, 2016). Details of the MAT213 material model and its implementation are available publicly (Goldberg et al., 2015; Harrington et al., 2016; Hoffarth et al., 2016). However, the measured properties can be utilized by most composite impact models.

Mechanical Properties↗
NASA NTRS2022

Multiscale Progressive Failure Analysis of 3D Woven Composites

Application of three-dimensional (3D) woven composites is growing as an alternative to the use of ply-based composite materials. However, the design, analysis, modeling, and optimization of these materials is more challenging due to their complex and inherently multiscale geometries. Herein, a multiscale modeling procedure, based on efficient, semi-analytical micromechanical theories rather than the traditional finite element approach, is presented and applied to a 3D woven carbon–epoxy composite. A crack-band progressive damage model was employed for the matrix constituent to capture the globally observed nonlinear response. Realistic microstructural dimensions and tow-fiber volume fractions were determined from detailed X-ray computed tomography (CT) and scanning electron microscopy data. Pre-existing binder-tow disbonds and weft-tow waviness, observed in X-ray CT scans of the composite, were also included in the model. The results were compared with experimental data for the in-plane tensile and shear behavior of the composite. The tensile predictions exhibited good correlations with the test data. While the model was able to capture the less brittle nature of the in-plane shear response, quantitative measures were underpredicted to some degree.

3D woven composites↗
NASA NTRSDate not supplied

Crash Sled Testing of Triaxially-Braided CFRP for Improved Vehicular Crashworthiness

The Impact Dynamics Laboratory at NASA Glenn Research Center recently developed a pneumatically-actuated crash sled for investigating the crush behavior of structural elements for vehicular applications. The apparatus includes an adjustable striker mass and specimen support mass, which are mounted on separate rails. This setup provides two advantages over crash sleds with so-called fixed specimen supports: (i) it allows for multiple independent measurements of the crush response using different instruments, and (ii) the specimen support can be varied and its reaction can be explicitly measured. This paper describes the experimental setup and data analysis methodology and illustrates the capability of the sled for measuring the specific energy absorption (SEA) of triaxially-braided carbon/epoxy composite C-channels and corrugated plates. The corrugated plate had a higher SEA than the C-channel and the SEAs did not vary when the striker mass and velocity were changed so that incident energy was constant.

Energy absorption↗
NASA NTRSDate not supplied

NASA's Composite Overwrap Lessons Learned on 40k Thrust Chamber Assemblies

Filament wound carbon fiber/polymer composite overwraps combined with additively manufactured (AM) copper alloy combustion chambers are a critical part of NASA’s Rapid Analysis and Manufacturing Propulsion Technology (RAMPT) project. The composite overwrap is a high strength-to-weight material and allows for significant weight reduction of the high-pressure thrust chamber assembly, reduction of overall cost, and reduced fabrication time while offering structural robustness. Integrated AM/composite overwrap chamber assemblies using 2,000 lbf (2k) and 7,000 lbf (7k) thrust were successfully hot fire tested at NASA Marshall Space Flight Center (MSFC). These assemblies allowed the team to learn lessons related to the design, analysis, and manufacturing of these integrated assemblies. A final goal of the RAMPT project is to design and test a 40,000 lbf (40k) thrust chamber assembly. The40k chamber presented the team several new challenges including an integral inlet port in the main body of the composite overwrap. Through multiple iterations of manufacturing techniques, varied materials, and Non-Destructive Evaluations (NDE), many lessons were learned to obtain a final design solution that would not only allow for the interrupted port inlet but also allow for sufficient material margins for the most critically stressed part of the chamber. This paper will cover the manufacturing techniques exploring fabric designs to help subsidize the coverage in the areas left bare by the inlet port during the filament winding process and custom tooling needed for the final full chamber processing. The original material choice of bismaleimide (BMI) 5250-4 from the 7k chamber performed well for the extreme environment of hot fire testing but proved to be difficult with the increased scale and interrupted port design of the 40kchamber. Discussion in this paper will cover these changes, including evaluation of the design, comparison to the prior 2k and 7k designs, and show the final hardware that will be tested. One primary goal of this work and RAMPT project is to provide this development process and data to industry for infusion into future engine designs.

Filament Wound↗
NASA NTRSDate not supplied

Consolidation of Braided Carbon Fiber/ Thermoplastic Tubes by Induction Heating

Thermoplastic composites have experienced renewed enthusiasm within the U.S. aerospace industry, due in part to opportunities for rapidly manufacturing large structures. Unlike the lengthy cure cycles required by thermosets, the thermoplastic matrix prepreg requires only heat and pressure to consolidate consecutive layers of material; with sufficient inter-ply contact time to develop a strong interface. The manufacturing requirements for thermoplastics provide manufacturing flexibility and of particular interest are in-situ consolidation processes; i.e consolidation during layup on a tool. In-situ consolidation removes the time-consuming and costly secondary processing step of autoclave or press consolidation. Process variables which contribute to laminate quality include temperature, heat transfer, inter-ply contact time, and consolidation pressure. Most of the work to date related to in-situ consolidation has been in conjunction with automated fiber placement (AFP), where prepreg tows are consolidated when placed on the tool. Considering this process for a braided structure adds complexity relative to AFP due to the rapid lay-down rate of the braider and simultaneous placement of a multiple prepreg tows. Processes considered for consolidation during AFP could not be applied to a braided part. Alternatively, a fully braided preform could be consolidated on the tool using well established thermoplastic welding techniques. The goal of this effort was to evaluate the effectiveness of induction welding to consolidate braided carbon fiber/thermoplastic composite tubes up to eight plies in thickness. The manufacturing process, thermal characterization, and initial mechanical property data of the consolidated tubes are reported.

In-situ consolidation, induction heating/welding, ↗
NASA NTRSDate not supplied

Comparison of Micromechanics Theories for Modeling Discontinuous Long Fiber Reinforced Composites

Two micromechanics theories, the high fidelity generalized method of cells and Carrera Unified Formulation, are used to model a repeating unit cell of a discrete long fiber composite. The models are used to predict the effective properties of a single fiber with varying fiber-to-fiber end gap lengths, as well as the local stresses in the fiber and matrix. Both models produced similar results and demonstrated that they could capture the complex local load transfer due to the shear lag effect.

discrete long fiber composites↗