Publications and source records attributed to Sangid, Michael D..

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2022

Fracture behavior of a melt-infiltration-processed SiC/Si composite at 900°C in argon, air, and steam

The fracture behavior of a melt-infiltration-processed SiC/Si composite, used to mimic the matrices of industrial fiber-reinforced ceramic composites, was examined in different atmospheres and temperatures. Specimens tested in four-point bending at 900 °C in oxygen-gettered argon, dry air, or steam-rich atmospheres exhibited higher average fracture strengths than specimens tested at 25°C. Higher mean fracture strength values were obtained for specimens tested in dry air or in a steam-rich atmosphere at 900°C than for specimens tested in high-purity, oxygen-gettered argon at this temperature. The increased fracture strengths obtained in air and in steam-rich atmospheres coincided with increased specimen oxidation and apparent oxide filling and blunting of flaws in these composites. Further, a transition in the location of catastrophic failure, from sites of preexisting damage created by Vickers indentations for tests in argon to other locations for tests in air or steam-rich atmospheres, was also consistent with such apparent oxide filling/blunting of indentation-induced flaws.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Residual elastic strain evolution due to thermal cycling of a ceramic-metal composite (WC-Cu) via high energy X-ray diffraction and analytical modeling

Residual stress, when superimposed with in-service loading, can significantly reduce the lifetime and performance of a component. Ceramic-metal composites are susceptible to residual stresses due to the thermal expansion mismatch of the ceramic and metallic phases. The WC-Cu composite explored in the present study provides a promising combination of thermal conductivity and strength properties, while exhibiting counterintuitive improvements in strength and ductility after thermal cycling. Further, this work quantifies the evolution of the residual elastic strains as a result of processing and cyclic thermal loading in a co-continuous WC-Cu composite through experimental high energy X-ray diffraction and kinetics-based modeling. Both analyses indicate that processing-induced residual tensile stress in the copper phase is relieved upon subsequent thermal cycling, with kinetics modeling revealing the cyclic-dependent nature of the active power-law creep mechanisms. The results indicate that, through stress relaxation, this material system maintains structural stability during thermal cycling. The illustrated kinetics of relaxation can inform general material processors and designers of ceramic-metal composites to minimize detrimental residual stress and improve performance of these material systems.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Direct observations and characterization of crack closure during microstructurally small fatigue crack growth via in-situ high-energy X-ray characterization

This study provides direct observation of the crack closure mechanism of a naturally occurring, tortuous, 3D microstructurally small fatigue crack (SFC) in additively manufactured Inconel 718. In-situ non-destructive characterization is performed using high-energy X-ray diffraction techniques to capture the evolution of the 3D microstructure and micromechanical response in the vicinity of the crack front. Based on the stress state of twelve grains analyzed at the crack tip, the crack closure events of the SFC front was found to be spatially heterogeneous with respect to loading progression governed by the local stress state of the grains (specifically the stress reversal from compression to tension). From this analysis, three grains that displayed different degrees of crack closure were further investigated, based on the orientation of the crack relative to the grains and the associated modality of crack growth. The stress normal to the crack plane and the associated degree of Mode I crack behavior were correlated with events of the crack opening earlier during the loading cycle. This was further corroborated by diffraction spot spreading analysis that quantified the crystallographic lattice distortion caused by the opening crack. Additionally, the detailed characterization of the opening behavior of the grains located at the crack tip and their associated states of stress elucidates the mechanism governing crack closure and will inform future modeling efforts of this phenomenon.

36 MATERIALS SCIENCE↗
DOE OSTI2021

A crystal plasticity model with an atomistically informed description of grain boundary sliding for improved predictions of deformation fields

Crystal plasticity (CP) is a powerful meso-scale technique for deformation modeling in polycrystalline materials. Crystal plasticity models typically do not include an explicit description of grain boundary (GB) sliding, which could lead to inaccurate predictions of strain distributions, especially in the vicinity of GBs. In the present study, a CP model is developed that includes GB sliding as an additional deformation mechanism and models the interaction between slip and GB sliding. Atomistic simulations are used to formulate the constitutive model for GB sliding and its interaction with incident slip. The deformation fields and structure of the GBs are obtained directly from experimental characterization and are faithfully reproduced as bicrystal systems for molecular dynamics simulations. The GBs are modeled as random-type (non-coincidence, asymmetrical) boundaries as observed from experimental data. The underlying atomistic-scale mechanism for pure sliding of random GBs was found to be analogous to fluid-flow. The interaction between incident slip and a sliding GB caused local increases in stress concentration, which further led to a momentary increase in the local sliding rate. The displacement profiles at the sliding GBs computed from the CP model with sliding accommodation are 38% more accurate than the baseline CP model as quantified by the mean squared error between the simulations and experiment. Here these results help improve the sophistication and accuracy of deformation modeling by including physics-based descriptions for GB sliding and its interaction with slip, eventually leading to more reliable predictions of micromechanical quantities.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Modeling Ti–6Al–4V using crystal plasticity, calibrated with multi-scale experiments, to understand the effect of the orientation and morphology of the α and β phases on time dependent cyclic loading

Classically, crystal plasticity modeling has used a range of constitutive equations, in which the incorporation of additional physics-based relationships typically results in additional model parameters. These additional parameters need to be reliably calibrated, which often necessitates the use of a range of experimental data acquired at multiple length scales. In this work, a crystal plasticity based finite element (CPFE) model for a dual-phase Titanium alloy, Ti–6Al–4V, is developed. The α and β phases of the microstructure are explicitly modeled. The model is calibrated using a systematic optimization routine and experimental data that consist of macroscopic stress-strain curves coupled with lattice strains on different crystallographic planes for the two phases. These experimental data were obtained from in situ high energy X-ray diffraction experiments for multiple material pedigrees, with varying crystallographic orientation distribution and β volume fractions. Depending on the thermomechanical-processing route and the heat treatment used to manufacture the alloy, Ti–6Al–4V can exist in a wide number of microstructural forms, which often results in the α and β phases either having well aligned slip systems (following the Burgers orientation relationship (BOR)) or possessing no alignment of the slip systems across the interphase boundary (not following the BOR). In this study, the fully-calibrated CPFE model is used to gain a comprehensive understanding of the deformation behavior of Ti–6Al–4V, specifically, the effect of microstructures that follow the BOR (or not) on time-dependent cyclic loading (including the effects of dwell hold times).

36 MATERIALS SCIENCE↗
DOE OSTI2020

A complete grain-level assessment of the stress-strain evolution and associated deformation response in polycrystalline alloys

Polycrystalline alloys are used pervasively across structural applications contingent upon extensive experimental testing. A statistically representative number of tests are required to expose the variability in the material's performance, as a result of non-uniform microstructures and associated micromechanical fields. In a more direct means of capturing this pertinent information, multi-modal experimental techniques are presented to measure and track the complete micromechanical state, evolving during loading, of each and every grain within the regions of interest. Specifically, a combination of high-energy X-ray diffraction microscopy and digital image correlation coupled with electron backscatter diffraction are conducted on a specimen for each of the alloys, Haynes 282 and Ti7Al. The results of the multi-modal analysis definitively demonstrate that the degree of heterogeneity increases with deformation level and is used to assess the number of grains necessary for a representative volume element description of the stress state for each of these materials. Moreover, higher resolution imaging is used for identification of the slip system activity and subsequently used to study slip transmission events. An accurate knowledge of the resolved shear stress in adjacent grains (grain interactions) is demonstrated to be a key descriptor of the slip transmission events.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Void coalescence and ductile failure in IN718 investigated via high-energy synchrotron X-ray tomography and diffraction

Ductile failure through the growth and coalescence of voids is of particular relevance for many engineering materials. Yet, the lack of experimental measurements of the mechanical state of the material at an appropriate length scale has limited further understanding of the regime of ductile failure. In this study, local grain-scale experimental measurements are used to determine their relevance for describing and predicting ductile failure. Additive manufactured materials, due to the presence of inherent porosity, as well as the ability to tailor internal porosity, provides a promising avenue to study ductile failure. Selective laser melting is used to manufacture a specially designed specimen with two large, internal voids, in addition to the natural porosity, which is characteristic to the production process. The initial porosity and its evolution upon tensile loading are characterized via micro tomography. Several locations of void coalescence are captured in the sample, revealing activity of multiple modes of failure. Finite element simulations, with a simplified J2 plasticity model, instantiated with the initial void structure, is deployed, in which geometric localizations of stress concentration corresponded with experimentally observed sites of coalescence but was inadequate in capturing the appropriate failure mechanism. Furthermore, from the experimental results of the far-field high-energy diffraction microscopy, the heterogeneous micromechanical state is identified and tracked around voids due to the local grain interactions. These experiments determine narrow bands of low stress triaxiality, at the onset of failure, which highlight the path of coalescence through intervoid shearing. Diffraction spot spreading analysis aided characterization of intragranular plasticity and strain heterogeneity, which can be coupled with high triaxiality to form the conditions inducive for coalescence through intervoid necking. In this study, the experimentally determined grain-scale description of the micromechanical state provides a physical basis that can accurately capture both the sites and the mechanism of void coalescence at the onset of ductile failure.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Strain rate sensitivity, microstructure variations, and stress-assisted β → α" phase transformation investigation on the mechanical behavior of dual-phase titanium alloys

In this study, the microstructures of three widely used dual-phase titanium alloys: Ti-6Al-4V, Ti-6Al-2Sn-4Zr-2Mo, and Ti-6Al-2Sn-4Zr-6Mo are characterized using backscatter electron imaging and the deformation behaviors in their individual α and β phases are investigated using in situ high-energy X-ray diffraction during uniaxial tension experiments. This is accompanied by calculation of the strain rate sensitivity (SRS) in these alloys, as a function of applied loading. The results of the calculated SRS and the mechanical response (in terms of lattice strains and hardening behaviors) are rationalized based on the local microstructure, composition, and texture of the alloy. A stress-induced β (BCC) to α" (orthorhombic) phase transformation is observed during the in-situ diffraction experiment, which permitted analysis of the lattice strain evolution during the phase transformation. Results from this study provide insights into the relationship between microstructure, composition, applied loading, and the deformation behavior, including effects on loading with time holds. Specifically, the results show that the microstructure, and not necessarily the chemical composition (Mo content), along with the applied loading have a dominant role in the observed SRS variation in titanium alloys. Further, the evolution of the α" (orthorhombic) phase is observed for the first time during deformation of an industrially relevant titanium alloy, Ti-6246.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Small fatigue crack growth behavior of Ti-6Al-4V produced via selective laser melting: In situ characterization of a 3D crack tip interactions with defects

Small fatigue crack growth (SFCG) behavior is examined for additively manufactured Ti-6Al-4V specimens with optimal and trial build conditions (representing an increased degree of defects) through a combination of in situ tomography and in situ energy dispersive X-ray diffraction. The results showed slower crack growth rates for the SFCG samples compared to the long cracks (which was not expected). Finally, in the case of the trial conditions, the increased levels of porosity deterred crack growth by blunting the crack, as evident by the in situ tomography characterization.

36 MATERIALS SCIENCE↗