NASA NTRS2026

Radiation-Conditioned Ti–hBN Coatings for Space Mechanisms: Bridging Tribology and Irradiation Effects from Laboratory to Low-Earth Orbit

The longevity of tribological components in extraterrestrial environments is challenged by abrasive regolith, extreme temperatures, and ionizing radiation. This study evaluates the performance of vacuum plasma sprayed (VPS) Ti-2vol.% hexagonal boron nitride (hBN) coatings applied to joint mechanisms such as rod and slot, ball and socket, and hinge assemblies, fabricated from Al6061 and Ti6Al4V for planetary structures. Coated and uncoated samples were tested under vacuum with lunar regolith simulant (JSC-1A), followed by environmental exposures including electron radiation and thermal cycling. Results show that coated samples consistently outperformed uncoated counterparts across all configurations. Wear depth in coated components was reduced by over 80%, as confirmed by 3D profilometry and surface imaging. SEM analysis revealed severe abrasion and localized plastic deformation in uncoated surfaces, while coated samples retained structural integrity due to synergy of hard protective phases formed during deposition and retained hBN providing solid lubrication in the sliding surface. Coated and exposed samples exhibited smoother actuation profiles and reduced friction, indicating a beneficial "conditioning" effect from environmental exposure. The coatings-maintained performance even on complex geometries with minimal delamination. These findings demonstrate the potential of VPS Ti-hBN coatings to extend the operational life of lunar mechanisms, bridging laboratory-scale tribology with flight-relevant mechanical applications.

tribology↗
NASA NTRS2025

Erosion Behavior of Ti-hBN Multifunctional Coatings in A Custom-Made Planetary Test Rig at Extreme Lunar Temperatures

Spacecraft landings and takeoffs on the lunar surface, along with extreme temperature variations between day and night (-196 to 150° C), cause high-velocity dust impacts and erosion, resulting in the premature failure of structures. Ti/2 vol% hBN coatings were deposited using atmospheric (APS) and vacuum plasma spray (VPS) using cryo-milled powder feedstock to protect the structural components. The erosion performance of coatings at extreme lunar temperature regimes (-150 to 150° C) was evaluated in a custom-made planetary erosion test rig (PETR) at low (50 mph) and high impact velocities (250 mph). The mass loss of VPS coatings was reduced by 50% compared to the APS coatings and 40% compared to the Ti6Al4V substrate. The cryogenic temperature induces brittleness in the material, rendering it susceptible to extreme conditions of material loss. The particle impact-deformation behavior was captured using a high-speed camera to study the erosion mechanism. This analysis revealed chipping in substrates and brittle APS coatings, while particles rebounding and embedding were observed in VPS coatings. Energy calculations, aided by particle trajectory tracking from the high-speed camera, have conclusively shown that VPS coatings absorb 5–10% more energy than APS coatings during erosion tests. A modified erosion index was developed incorporating the fracture toughness and temperatures. New erosion models for brittle and ductile target materials are proposed for developing erosion-resistant material systems.

Abhijith Kunneparambil Sukumaran↗
NASA NTRS2025

Radiation-Resistant Ti/BN Coatings: Insights From 171 Days Exposure to Space Radiation and Atomic Oxygen in Low Orbit

Atmospheric Plasma Spray (APS) and Vacuum Plasma Spray (VPS) techniques were used to develop Ti/2 vol.% hBN coatings, for extreme space environments and tested aboard the International Space Station as part of the MISSE-17 (Materials International Space Station Experiments) program. The coatings were exposed to atomic oxygen, space radiation, and low-orbit thermal cycling. VPS coatings showed a 56% increase in microhardness, a 26% rise in elastic modulus, minimal porosity and crack density changes compared to APS coatings. The change in mechanical properties is attributed to the formation of TiO, TiO₂ and TiN from nitrogen retention, alongside radiation-induced dislocations, which enhanced surface hardening. The oxidation of titanium led to the formation of TiO and TiO₂, while boron nitride was retained and underwent transmutation in VPS coatings. XPS and EDS analyses confirmed the enhanced space-environment resistance of VPS coatings, making them ideal for long-term spacecraft protection in lunar and Martian conditions.

Abhijith Kunneparambil Sukumaran↗
NASA NTRS2024

Wear and Neutron Shielding Resilience of Titanium-Hexagonal Boron Nitride Coatings Against Extreme Lunar Radiation and Thermal Cycles

Ti6Al4V and Al6061 are aerospace alloys used in lunar structural components and rovers owing to their high specific strength. However, they deteriorate rapidly when subjected to demanding conditions of the lunar environment, such as extreme thermal cycles, solar particle radiation, and abrasive regolith. Cryo-milled powders were employed to deposit hBN-reinforced protective titanium coatings through plasma spray (atmospheric APS and vacuum-VPS) with 2 and 10 vol% of hBN on Ti6Al4V and Al6061 substrates. These coatings were evaluated for durability under extreme lunar-like conditions, including thermal cycling, electron radiation, and synergistic (electron radiation-thermal cycle) exposure. The coatings exhibited radiation-induced hardening, resulting in a substantial increase in their microhardness ~20–40% compared to virgin condition. Bright-field transmission electron microscopy (TEM) analysis reveals the presence of high dislocation densities, black dot defects, and dislocation clusters, providing evidence of the severe impact of synergistic environmental stresses. Ball-on-disk tribological tests were conducted in the presence of JSC-1 A lunar regolith simulant to evaluate the wear performance of coatings. Compared to conventional Ti6Al4V substrate, 50%, 90%, and 70% reductions in wear volume were observed in the Ti/2 vol% hBN coatings in thermal-only, radiation-only, and synergistic environments. Neutron shielding tests indicate that the synergistic coatings offer higher neutron shielding performance by up to 28% compared to virgin coatings, attributed to improved neutron capture by 10B isotopes. Upon a comprehensive assessment and ranking of multiple coatings under varying conditions, the VPS Ti/2 vol% hBN coating emerges as the top choice for protection against extreme radiation and thermal cycles for future lunar explorations.

Boron nitride↗
NASA NTRS2023

Tribological and Radiation Shielding Response of Novel Titanium-Boron Nitride Coatings for Lunar Structural Components

Aluminum (Al) and titanium (Ti) lightweight alloys play a crucial role in space systems due to their exceptional strength-to-weight ratio. However, their premature failure in the presence of lunar regolith and their lack of neutron shielding ability are significant challenges. To address these issues, we have developed air and vacuum plasma-sprayed hBN (hexagonal Boron Nitride) -reinforced titanium coatings with 2 and 10 vol% of hBN. Tribological studies conducted with JSC-1 A lunar regolith simulant revealed a 90 % reduction in wear volume for the Ti/2 vol% hBN coatings compared to conventional materials due to the synergistic action of harder secondary phases and solid lubrication effect of hBN. Additionally, a 27 % enhancement in radiation shielding is obtained based on the mass absorption coefficient (radiation absorbed per sample density and thickness) for VPS Ti/2 vol% hBN coatings.

Wear↗
NASA NTRSDate not supplied

Feasibility Study to Dissolve Additively Manufactured Inconel 718 Support Structures

Additive manufacture (AM) component design face constrains due to support structure removal. Interior passages or delicate geometries require supports yet cannot be removed without compromising the design or complicating post-processing. A process was developed to dissolve metal AM supports where a sensitizing agent is applied post-build. During stress relief the sensitizing agent diffuses into the surface and alters the chemical composition of the top 100 to 200 μm. During an electrochemical dissolution process the sensitized region is susceptible to corrosion/dissolution and the etching reaction self-terminates once the sensitized region is dissolved. Support thickness varies from 80 to 200 μm, resulting in total dissolution or sufficiently weakened to facilitate removal. The objective of this project was to demonstrate a support structure dissolution process for IN718 components built using AM and to characterize the impact on mechanical properties, microstructure, and surface finish.

Omar R Mireles↗
NASA NTRSDate not supplied

Metallic Environmentally Resistant Coating Rapid Innovation Initiative (MERCRII)

Lightweight alloys such as aluminum (Al) and titanium (Ti) are often specified for space systems to minimize mass while maintaining structural integrity. These alloys, however, exhibit poor tribological response (high friction and wear) in extreme space environments and are exacerbated by the presence of lunar regolith. This leads to a shortened service life that poses a challenge for long term operations on the lunar surface. This project seeks to address this technology gap by developing advanced wear- and radiation-resistant coatings for lightweight parts to extend the lifetime and sustainability of both lunar and Martian assets and the missions they support.

dust mitigation↗
NASA NTRSDate not supplied

Metallic Environmentally Resistant Coating Rapid Innovation Initiative (MERCRII)

Mission concepts such as JPL’s Endurance-A utilize rovers such as Astrolab’s FLEX concept to explore the lunar surface. For these types of systems, lightweight alloys such as aluminum (Al) and titanium (Ti) are often specified to minimize mass while maintaining structural integrity. Such alloys, however, exhibit poor tribological response in the form of high friction and wear, especially in extreme space environments and with the additional presence of lunar regolith. This shortens the lifetimes of these systems which have a requirement to traverse 1,00km/year. This project is addressing the technology need of this and future rover missions by developing advanced wear- and radiation-resistant coatings for lightweight parts to extend the lifetime and sustainability of both lunar and Martian assets.

MISSE↗
NASA NTRSDate not supplied

In Space Manufacturing

Explore the source record for details and available documents.

In Space Manufacturing↗
NASA NTRSDate not supplied

Metallic Environmentally Resistant Coatings Rapid Innovation Initiative (MERCRII) Mechanism Development and Testing

This project seeks to address the high friction and low wea resistance of lightweight aluminum (Al) and titanium (Ti) alloys to extend the lifetime and sustainability of both lunar and Martian assets missions by developing advanced wear-and radiation-resistant. MERCRII started with 6 candidate coating materials and 3 candidate application methods that were down-selected through pathfinder and 2 phases of testing to one coating configuration: Ti64 with 2%hBN Vacuum Plasma Spray.

dust mitigation↗