Thermodynamics of Tritium Trapping by Point Defects at Interfacial Cr-based Phases of the Al Coating
Density functional theory (DFT) simulations have been carried out to evaluate the potential for tritium trapping by metal vacancies in four phases Cr-containing phases (i.e., Cr3Si, Al0.3Cr0.7, Al8Cr5-HT, and Al8Cr5) identified near the interface between the Al coating and 316 stainless steel (316 SS) cladding. In addition, an ab initio thermodynamics approach has been employed to predict the temperature and T2-partial pressure dependence on the thermodynamics of singly tritiated defects. Key results in this work suggest that metal vacancies in the four phases have the potential to favorably trap tritium species, especially Si vacancies in Cr3Si phase. This overall thermodynamic trend can be correlated to the energy cost of having an interstitial tritium in the lattice, which has been calculated to range from 0.17 eV in Al8Cr5-HT to 0.89 eV in Cr3Si. A comparison of the results from this study with previous theoretical works investigating tritium behavior in other Fe-Al phases identified in the aluminide coating, suggests that metal vacancies are generally able to trap tritium in various Fe-Al aluminide phases. Especially, it was found that Si and Al vacancies would be the most efficient to trap for tritium, followed by Cr vacancies, then Fe and Ni vacancies. In the four Cr-based material phases investigated in this work, it is interesting to note that, in the absences of Fe or Ni species, strong interactions between tritium and the metal vacancies are always occurring by the formation of preferential Cr—T bonds (i.e., no Si—T or Al—T bonds were formed).