Monocrystalline 1.7-eV MgCdTe solar cells

Monocrystalline 1.7-eV Mg 0.13 Cd 0.87 Te/Mg x Cd 1-x Te (x > 0.13) double-heterostructure (DH) solar cells with varying Mg composition in the barrier layers are grown by molecular beam epitaxy. Furthermore, a Mg 0.13 Cd 0.87 Te/Mg 0.37 Cd 0.63 Te DH solar cell featuring abrupt interfaces between barriers and absorber and the addition of a SiO 2 anti-reflective coating demonstrates open-circuit voltage (V OC ), short-circuit current density (J SC ), fill factor (FF), and device active-area efficiencies up to 1.129 V, 17.3 mA/cm 2 , 77.7% and 15.2%, respectively. The V OC and FF vary oppositely with the Mg x Cd 1-x Te barrier height indicating an optimal design of the MgCdTe DHs as a tradeoff between carrier confinement and carrier transport. Temperature-dependent V OC measurements reveal the majority of carrier recombination in the devices occurs outside the DHs, in the a-Si:H hole-contact layer and at the interface between the a-Si:H layer and the Mg x Cd 1-x Te top barrier at room temperature. Simulation results for the device with the highest efficiency show that the p-type a-Si:H layer and Mg 0.37 Cd 0.63 Te top barrier contribute 1.3 mA/cm 2 and 2.4 mA/cm 2 J SC loss, respectively.

14 SOLAR ENERGY↗

DOE OSTI2021

Recombination rate analysis in long minority carrier lifetime mid-wave infrared InGaAs/InAsSb superlattices

Gallium is incorporated into the strain-balanced In(Ga)As/InAsSb superlattice system to achieve the same mid-wave infrared cutoff tunability as conventional Ga-free InAs/InAsSb type-II superlattices, but with an additional degree of design freedom to enable optimization of absorption and transport properties. Time-resolved photoluminescence measurements of InGaAs/InAsSb superlattice characterization- and doped device structures are reported from 77 to 300 K and compared to InAs/InAsSb. The low-injection photoluminescence decay yields the minority carrier lifetime, which is analyzed with a recombination rate model, enabling the determination of the temperature-dependent Shockley–Read–Hall, radiative, and Auger recombination lifetimes and extraction of defect energy levels and capture cross section defect concentration products. The Shockley–Read–Hall-limited lifetime of undoped InGaAs/InAsSb is marginally reduced from 2.3 to 1.4 μs due to the inclusion of Ga; however, given that Ga improves the vertical hole mobility by a factor of >10×, a diffusion-limited InGaAs/InAsSb superlattice nBn could expect a lower bound of 2.5× improvement in diffusion length with significant impact on photodetector quantum efficiency and radiation hardness. At temperatures below 120 K, the doped device structures are Shockley–Read–Hall limited at 0.5 μs, which shows promise for detector applications.

46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗