Solid-state reaction mediated microstructural evolution in a spark plasma sintered in situ Ti–B 4 C composite
For this study, a novel porosity-free in situ Ti–B 4 C composite was fabricated via spark plasma sintering (SPS). Detailed analysis of the phase evolution, coupling results from XRM, XRD and SEM-EBSD-EDS, indicate that primarily TiB 2 precipitates formed due to the in-situ reactions between the boron-carbide and titanium powders. The precipitation of TiB 2 resulted in the formation of a graphitic C-rich thin layer circumscribing the partially reacted B 4 C particles. Further progression of the in-situ reaction leads to the out-diffusion of the excess carbon from the B 4 C particles, across the graphite and TiB 2 phases, forming TiC upon reacting with the titanium matrix. Therefore, the final microstructure primarily consisted of TiB 2 , TiC, and partially reacted B 4 C phases, with small amounts of TiB, α-Ti, and graphite. Furthermore, the microstructure in these SPS processed in situ composites appeared to be the product of a solid-state Ti–B 4 C diffusion couple, substantially different from their fusion-based additively manufactured counterparts. Nano-indentation tests revealed a remarkably high average hardness of ~25 GPa for this SPS-processed Ti–B 4 C composite and comparable (with literature) phase-specific hardness and modulus values for the constituent TiB 2 , TiC, and B 4 C phases.
Influence of fine-scale B2 precipitation on dynamic compression and wear properties in hypo-eutectic Al0.5CoCrFeNi high-entropy alloy
The near equiatomic high-entropy alloys based on Al, Co, Cr, Fe, Ni have provided a novel microstructural template for alloy design. The face-centered cubic (FCC) matrix strengthened by body-centered cubic (BCC) based ordered B2 precipitates can be used to develop a new generation of precipitation strengthened alloys. The present study focuses on an Al0.5CoCrFeNi hypo-eutectic alloy consisting of an as-solidified FCC+B2 microstructure. Guided by solution thermodynamic modeling, this alloy has been isothermally aged for solid-state precipitation of a high fraction of fine-scale intragranular B2 particles. The dynamic compressive strength, hardness, and sliding wear response of the alloy as a function of B2 phase fraction is examined. The flow stress at 0.02% true strain increased from ~ 670 MPa to ~1350 (102%) MPa, the ultimate compressive strength increased from ~1160 MPa to 1500 MPa (20%), and the wear resistance increased more than 5 times with progressively increasing phase fraction of B2 precipitates.