9 records

DOE OSTI2024

Low-Cost, High-Performance Carbon Fiber for Compressed Natural Gas Storage Tanks (Final Technical Report – Down Select Report)

The aim of this project is to reduce the cost of Type IV, carbon fiber (CF) composite overwrap compressed gas storage tanks by reducing the cost of CF and CF composites. The project team worked to reduce the cost of CF by exploring and testing opportunities for a low-cost alternative precursor material for CF production to supplant market-dominant and costly polyacrylonitrile (PAN). Concurrently, the team aimed to reduce the cost of the tanks at the composite level by improving the interfacial adhesion between the fibers and the matrix resin through the incorporation of low-cost nanoparticles recycled from waste materials, which would reduce the volume of costly CF required to achieve the same tank performance. At the end of the first year, the project team selected mesophase pitch as the primary precursor candidate from a field of materials based on the superior mechanical performance and cost-saving potential. During the second year, the team produced CFs derived from mesophase pitch achieving an average tensile strength of 365.6 ksi and average tensile modulus of 40.74 Msi. Facility availability for spinning and converting these fibers at greater scale has hindered scale-up demonstration, but the team has identified opportunities to conduct this work in the near term. Cost modeling shows that these mesophase pitch-derived CFs can be up to 40% less expensive than PAN-derived CFs due to the lower cost of the feedstock material, higher throughput, greater conversion yield, and lower cost spinning method and compared to PAN. Additionally, the team has demonstrated at lab-scale that nanoparticle coating CFs can significantly increase the interfacial shear strength and load transfer efficiency of CFs in a matrix. Single filament pull-out testing showed a 27% average increase in max interfacial shear strength due to this coating. A continuous method of applying these coatings to a tow of CF has been developed for scale-up. 26 m tows of coated CFs were produced using this system and formed into composite ring samples for ASTM ring burst testing. Issues with the testing protocol have limited assessment of these results. A prototype Type IV tank was designed to meet ANSI HGV2 standards, and the design criteria set out by DOE, using the CF properties developed by the team paired with a proprietary resin matrix, a polyamide liner, and aluminum end bosses. The tank weighs 153.1 kg and with a total capacity of 5.8 kg H2 (5.6 kg usable), which yields a gravimetric capacity of 1.17 kWh/kg. Cost modeling predicts that the tank will have a projected cost of $15.73/kWh. Tank performance modeling does not include considerations for fiber-matrix load transfer efficiency improvements offered by nanoparticle coating method.

08 HYDROGEN↗

DOE OSTI2024

1,4-cineole: a bio-derived solvent for highly stable graphene nanoplatelet suspensions and well-dispersed UHMWPE nanocomposite fibers

The exceptional properties of carbon nanoparticles, such as graphene, promise to expand the performance and functionality of many materials. The reinforcement of polymers is of keen interest due to their low density and flexible manufacturing methods. However, dispersing graphene in them has proven to be an enduring challenge due to the particles’ propensity to form performance degrading agglomerations. Furthermore, effective solvents for nanoparticle dispersion are commonly harmful, non-renewable, petrochemicals. In this work, a bio-derived solvent, 1,4-cineole, is demonstrated as a renewable alternative to these solvents that can be used to form highly stable graphene nanoplatelet (GnP) suspensions and used to gel spin well-dispersed UHMWPE/GnP nanocomposite fibers. The GnP concentration in the fibers was varied across three orders of magnitude, 0.01 wt% to 1 wt%, to examine its effect on fiber microstructure and properties. At low concentrations the particles act as point defects without affecting the fiber microstructure, and poor particle/matrix interfacial adhesion results in significantly reduced mechanical properties. At 1 wt% GnPs, a network effect takes hold thereby reinforcing the fibers, but the particles also impede the growth and orientation of crucial load-carrying crystalline structures in the fiber. Furthermore, unveiling the microstructural effects of GnPs on highly oriented and crystalline polymers in this study provides crucial insights for future work developing high-performance polymer nanocomposite fibers.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Tuning Microstructure of Mesophase Pitch Carbon Fiber by Altering the Carbonization Ramp Rate

The microstructure of mesophase pitch carbon fibers (CFs) are tuned by varying ramp rates from 1 to 50 °C min –1 up to 1000 °C to study the effect of ramp rate on CFs’ microstructure, thermal and mechanical properties with the goal of offsetting the cost by decreasing cycle time. The ramp rates represent carbonization times ranging from 16.4 to 1.17 h, not including cool down. Differential scanning calorimetry, thermogravimetric analysis, and derivative thermogravimetry are used to investigate the impact ramp rate has on the thermal properties of mesophase pitch. It is found that lower ramp rates are endothermic in nature with a lower temperature onset and maximum weight loss. Higher ramp rates possess an exothermic nature with higher temperatures resulting in maximal weight loss over a smaller range of temperatures. Mechanical testing shows varying CF strengths and moduli dependent on ramp rate and an optimized process is developed to produce the strongest CF. Furthermore, microstructural characterization revealed that faster ramp rates lead to smaller interplanar spacings and larger crystallites but possessed greater disorder.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Evaluating consumer 3D printing nozzles as a low cost alternative for mesophase pitch-derived carbon fiber production

Synthetic fibers, such as Kevlar fibers, SiC fibers, and carbon fibers, are essential components for constructing high performance structures. Whether for engineering, sports, energy storage (batteries and supercapacitors), or aerospace applications, fiber microstructure plays a critical role in fiber properties and functionalities. However, studying fiber nozzle configurations and spinning parameters to achieve the desired microstructure remains challenging, costly, and time consuming. Here, mesophase pitch-derived fibers were used as an example to demonstrate that low cost, commercially available 3D printer nozzles can “print” fibers. Four different nozzles were used to “print” fibers and the effects of their features on fiber properties were observed and compared to other lab spun and commercial pitch- derived CF. A longer orifice length resulted in higher modulus fiber whereas a larger draw-down ratio yielded a stronger fiber. Furthermore, the findings provide a new opportunity for 3D printer hardware application and open up opportunities for developing low-cost fibers.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Exploration of fibers produced from petroleum based-mesophase pitch and pet blends for carbon fiber production

Petroleum-derived mesophase pitch and polyethylene terephthalate (PET) were blended and melt-extruded to create precursor fibers. The raw blends, heat treated bulk materials, and fibers were all examined to determine compatibility between petroleum-derived mesophase pitch and PET. Thermal investigation of the raw blends showed the presence of both the pitch and PET in separate phases suggesting no interactions had occurred during mixing. Here, the heat-treated bulk material also showed multiple phases under polarized light while Fourier-transform infrared spectroscopy indicated that the two materials did not fully separate during extrusion. Elemental scans of the precursor fibers showed areas of high oxygen concentrations averaging 11.7% as compared to a 2% oxygen concentration across the majority of the cross-section. Tensile tests of the precursor fibers showed a decrease in average modulus as compared to pure pitch fibers; however, the depressed modulus of the blended fibers was found to be independent of the PET weight percentage. Fibers created from 5 wt.% PET had a strength value within 10% of pure pitch and a 200% increase in modulus and were therefore found to be the most promising for carbon fiber production. Pure pitch and the 5 wt.% PET fibers were stabilized and carbonized to 1000 °C. Both types of fibers were tensile tested to determine their strength and stiffness. Pure pitch carbon fibers maintained a higher strength while the carbon fibers produced from 5 wt.% PET possessed a stiffer modulus which can be attributed to their radial microstructure.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Influence of Oxygen Uptake on Pitch Carbon Fiber

Carbon fiber precursor materials, such as polyacrylonitrile, pitch, and cellulose/rayon, require thermal stabilization to maintain structural integrity during conversion into carbon fiber. Thermal stabilization mitigates undesirable decomposition and liquification of the fibers during the carbonization process. Generally, the thermal stabilization of mesophase pitch consists of the attachment of oxygen-containing functional groups onto the polymeric structure. In this study, the oxidation of mesophase pitch precursor fibers at various weight percentage increases (1, 3.5, 5, 7.5 wt%) and temperatures (260, 280, 290 °C) using in situ differential scanning calorimetry and thermogravimetric analysis is investigated. The results are analyzed to determine the effect of temperature and weight percentage increase on the stabilization process of the fibers, and the fibers are subsequently carbonized and tested for tensile mechanical performance. Finally, the findings provide insight into the relationship between stabilization conditions, fiber microstructure, and mechanical properties of the resulting carbon fibers.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Compatibility of mesophase pitch and linear low-density polyethylene for low-cost carbon fiber

Mesophase pitch and linear low-density polyethylene (LLDPE) were blended by shear mixing and extruded producing precursor fibers which were then converted to carbon fibers (CFs). LLDPE additives agglomerate within the isotropic spheres rather than uniformly dispersing throughout the entire matrix. The blends possess different thermal properties and precursor tensile properties evident by two-phase tensile stress nature not present in precursor fibers produced from pure pitch. The resultant CFs were oxidized at 280 °C for 4 h and carbonized at 1000 °C for 15 min. This process created pitch CFs with a tensile strength of 1.23 GPa and a Young’s modulus of 99 GPa. All CFs produced from blends of pitch and LLDPE possessed a tensile strength of 0.63 GPa and less. These CFs showed a microstructure slightly different from the pure pitch CFs with fractured CF cross sections revealing voids present in all blended CFs due to burnt off LLDPE stemming from carbonization. Further study into compatibilizers and new conversion processes is required to successfully blend LLDPE with mesophase pitch for the purpose of producing a new low-cost CF.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Unveiling the microstructural evolution of carbon fibers derived from polyamide-6

Polyacrylonitrile-based carbon fibers have dominated the industry for decades, but the high cost of polyacrylonitrile has prevented the widespread adoption of carbon fiber in high-volume structural applications. As such, a significant amount of research has been dedicated to finding an alternative, low-cost carbon fiber precursor. In this work, carbon fibers were produced from polyamide-6 using metal salt impregnation and a thermo-oxidative stabilization step. To gain further insight into the carbonization process and microstructural transformation, the morphologies, crystallinities, elemental compositions, and thermal stabilities of the fibers were characterized at various stages of processing. The stabilization step resulted in a significant increase in carbon yield, indicating a dramatic increase in thermal stability. This is due to the crosslinking of polyamide-6 chains, which was confirmed by functional group analysis. The crystallinity of the fibers was also significantly altered during processing, as the produced carbon fibers consisted of pseudo-amorphous carbon with two distinct regions of metal salt impregnation. Finally, the findings and microstructural evolution mechanisms provide guidelines for further research into carbon fiber produced from polyamide-6.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Carbon fibers derived from commodity polymers: A review

Carbon fiber composites are prohibitively expensive for a wide array of applications that would greatly benefit from their superior specific strength and specific stiffness. Replacing the market-dominant carbon fiber precursor material, polyacrylonitrile, with a low-cost alternative would significantly reduce the cost of carbon fiber production. Commodity polymers may provide such an alternative thanks to their abundance and ease of production into fibers. Furthermore, this review presents state-of-the-art carbon fiber production from polyacrylonitrile, an overview of melt-spinnable alternative precursors broadly, and an in-depth review of the latest advances in the synthesis of carbon fibers from low-cost, commodity thermoplastics such as polyethylene, polyamide, polystyrene, polyester, and poly(vinyl chloride).

36 MATERIALS SCIENCE↗