Schindelholz, Eric

Publications and source records attributed to Schindelholz, Eric.

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2022

Stress corrosion cracking mechanism of cold spray coating on a galvanically similar substrate

Here, the chloride-induced stress corrosion cracking (CISCC) mechanism of cold spray (CS) coating on a galvanically similar substrate is investigated. Arc welded 304L stainless steel (SS) specimens are loaded into four-point bend fixtures, cold sprayed with 304L SS, then immersed in boiling MgCl 2 . Interconnected porosity forms through crevice corrosion along CS splat boundaries, allowing corrosive species to penetrate through the CS layer. Nevertheless, the substrate is resistant to CISCC likely because of compressive stress introduced by peening during CS particle impacts. These findings underscore the importance of residual stress in the environmental degradation of CS coatings or repairs of engineering structures.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Crystallographic effects on transgranular chloride-induced stress corrosion crack propagation of arc welded austenitic stainless steel

Abstract The effect of crystallography on transgranular chloride-induced stress corrosion cracking (TGCISCC) of arc welded 304L austenitic stainless steel is studied on >300 grains along crack paths. Schmid and Taylor factor mismatches across grain boundaries (GBs) reveal that cracks propagate either from a hard to soft grain, which can be explained merely by mechanical arguments, or soft to hard grain. In the latter case, finite element analysis reveals that TGCISCC will arrest at GBs without sufficient mechanical stress, favorable crystallographic orientations, or crack tip corrosion. GB type does not play a significant role in determining TGCISCC cracking behavior nor susceptibility. TGCISCC crack behaviors at GBs are discussed in the context of the competition between mechanical, crystallographic, and corrosion factors.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Marine Atmospheric Corrosion of Additively Manufactured Stainless Steels

Additively manufactured (AM) stainless steels exhibit numerous microstructural differences compared to their wrought counterparts, such as Cr enriched dislocation cell structures. The influence these unique features have on a SSs corrosion resistance are still under investigation with most current works limited to laboratory experiments. The work herein shows the first documented study of AM 304L and 316L exposed to a severe marine environment on the eastern coast of Florida with comparisons made to wrought counterparts. Coupons were exposed for 21 months and resulted in significant pitting corrosion to initiate after 1 month of exposure for all conditions. At all times, the AM coupons exhibited lower average and maximum pit depths than their wrought counterparts. After 21 months, pits on average were 4 μm deep for AM 316L specimen and 8 μm deep for wrought specimen. Pits on the wrought samples tended to be nearly hemispherical and polished with some pits showing crystallographic attack while pits on AM coupons exhibited preferential attack at melt pool boundaries and the cellular microstructure.

36 MATERIALS SCIENCE↗