The nontrivial effects of annealing on superconducting properties of Nb single crystals

The effect of annealing on the superconducting properties of niobium single crystals was studied using optical, magnetic, and scanning tunneling microscopy (STM) methods. Pieces of the same crystal boule were studied before and after the annealing at 800 ${^\circ}\textrm{C}$, 1400 ${^\circ}\textrm{C}$, and near the melting point of niobium (2477 ${^\circ}\textrm{C}$). The initial samples had a high hydrogen content and low-temperature imaging revealed large hydrides (hundreds of micrometers) appearing below 190 K. The formation of these large precipitates is already completely suppressed by annealing at 800 ${^\circ}\textrm{C}$. However, the overall superconducting properties of the annealed samples did not improve and, in fact, worsened. In particular, the superconducting transition temperature decreased, the upper critical field increased, and the pinning strength increased. In the STM study, the sample was annealed initially at 400 ${^\circ}\textrm{C}$, measured, annealed at 1700 ${^\circ}\textrm{C}$, and measured again. The STM revealed a ‘dirty’ superconducting gap with a significant spatial variation in tunneling conductance after annealing at 400 ${^\circ}\textrm{C}$. The clean gap was recovered after annealing at 1700 ${^\circ}\textrm{C}$. This is likely due to oxygen redistribution near the surface, which is always covered by oxide layers in as-grown crystals. Our results indicate that vacuum annealing at least up to 1400 ${^\circ}\textrm{C}$, while removing a large percentage of hydrogen, introduces additional nanosized defects, likely hydride precipitates, that act as efficient pair-breaking and pinning centers. The dimensionless scattering rate is estimated to have increased from $\Gamma = 0.2$ to about $\Gamma = 0.4$ after annealing at 1400 ${^\circ}\textrm{C}$. These results on single crystals differ drastically from those obtained in polycrystalline bulk niobium (i.e. cut from superconducting radio-frequency cavities), where annealing is known to have a significant positive effect that is attributed to the improvement of the crystalline structure masking the more subtle influence of the hydrides.

43 PARTICLE ACCELERATORS↗

DOE OSTI2024

Multiple magnetic interactions and large inverse magnetocaloric effect in TbSi and TbSi 0.6 Ge 0.4

We present a comprehensive investigation of the electronic structure, magnetization, specific heat, and crystallography of TbSi (FeB structure type) and TbSi 0.6 ⁢Ge 0.4 (CrB structure type) compounds. Both TbSi and TbSi 0.6 ⁢Ge 0.4 exhibit two antiferromagnetic (AFM) transitions at T N⁢1 ≈ 58 and 57 K, and T N⁢2 ≈ 36 and 44 K, respectively, along with an onset of weak metamagneticlike transition around 6 T between T N⁢1 and T N⁢2 . High-resolution specific heat (C P ) measurements show the second- and first-order nature of the magnetic transition at T N⁢1 and T N⁢2 , respectively, for both samples. However, in the case of TbSi, the low-temperature (LT) AFM to high-temperature (HT) AFM transition takes place via an additional AFM phase at the intermediate temperature (IT), where both LT to IT AFM and IT to HT AFM phase transitions exhibit a first-order nature. Both TbSi and TbSi 0.6 ⁢Ge 0.4 manifest significant magnetic entropy changes (Δ⁢S M ) of 9.6 and 11.6 J/kg-K, respectively, for Δ⁢μ 0 ⁢H=7 T, at T N⁢2 . The HT AFM phase of TbSi 0.6 ⁢Ge 0.4 is found to be more susceptible to the external magnetic field, causing a significant broadening in the peaks of Δ⁢S M curves at higher magnetic fields. Temperature- and field-dependent specific-heat data have been utilized to construct the complex HT phase diagram of these compounds. As a result, temperature-dependent x-ray diffraction measurements demonstrate substantial magnetostriction and anisotropic thermal expansion of the unit cell in both samples.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2024

Developing techniques for crystal growth synthesis and characterization of rare earth-silicon-germanium magnetoresponsive alloys

In this study, a crystal growth technique was developed for the family of intermetallic, magnetoresponsive RE 5 (Si 1-x Ge x ) 4 alloys in order to access the intrinsic and anisotropic properties. Initial bulk properties measured on polycrystalline samples alluded to the properties being obscured or averaged and high-quality, well-characterized, single crystals would clarify this. Successful crystal growth led to development of oriented sample preparation techniques specific for the crystal structures (monoclinic and orthorhombic) and mechanical properties (hard and brittle) of these alloys, and customized for the various measurement techniques undertaken. Here we describe our journey, sometimes circuitous, from crystal growth to sample preparation and cite the scientific discoveries that came about as a result.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Exceptional magnetic and magnetoelastic behavior of rare-earth non-centrosymmetric Sm 7 Pd 3

Magnetic compounds possessing an intrinsic combination of near-zero magnetization with high magnetic anisotropy are highly desirable for spinronic applications and memory recording. A comprehensive study of Sm 7 Pd 3 binary compound uncovered a unique combination of strong magnetoelastic behavior, very low net magnetization, and exceptionally high magnetic coercivity. The temperature-dependent X-ray synchrotron powder diffraction study indicates the abrupt changes in the compound's lattice parameters at the magnetic ordering temperature of T C =169 K, although the crystal structure remains non-centrosymmetric hexagonal Th 7 Fe 3 -type down to 6 K. Density functional theory calculations confirm high intrinsic magnetocrystalline anisotropy of Sm 7 Pd 3 , which explains the extremely large coercivity of the polycrystalline sample, up to H cr = 130 kOe at 2 K. In conclusion, this discovery brings to life a novel class of highly anisotropic materials that are distinctly different from known spintronic materials, making them interesting future systems for magnetic memory research.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Anisotropic magneto-resistivity and magnetocaloric effect in DyAl 2

Here, in this study, we experimentally and theoretically investigate the correlation between the anisotropic magnetic resistivity and magnetocaloric effect in DyAl 2 single crystals. DyAl 2 crystallizes in the C15 Laves phase structure with cubic symmetry. While some earlier studies revealed that the isothermal entropy change in dialuminides follows a similar trend as the electrical resistivity change as a function of temperature and magnetic field, the correlation between anisotropic behavior of these two physical parameters is yet to be explored to the best of our knowledge. To address this gap, we measured electrical resistivity of DyAl 2 single crystals along two different directions in zero and applied magnetic fields and compared the experimental results with our theoretical model. For the theoretical analysis, we employed a model Hamiltonian in the mean-field approximation, considering the exchange interaction, Zeeman effect, and crystalline electric field associated with the cubic symmetry. Our findings reveal a significant dependence of DyAl 2 resistivity on the direction of the applied magnetic field, in agreement with our theoretical results. These outcomes emphasize the interplay between magnetocaloric effect and magneto-resistivity, underscoring the potential of the magnetocaloric effect as a valuable tool for gaining deeper insights into basic physical properties including electron transport behavior.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Evidence for temperature chaos in spin glasses

We study the field cooled magnetization of a CuMn spin glass (SG) under temperature perturbations. The T-cycling curves are compared with the reference curve without temperature cycling. There is a crossover from the cumulative aging region to noncumulative aging region as the temperature change is increased. The cumulative aging range scales with the chaos length, ℓ c , becoming comparable to the correlation length, ξ, at the crossover boundary. The extracted chaos exponent, ζ=1.1, is in agreement with theoretical predictions. Furthermore, our results strongly suggest temperature chaos exists in real SG systems.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2020

Clathrate BaNi 2 P 4 : An Interplay of Heat and Charge Transport Due to Strong Host–Guest Interactions

Heat and charge transport properties of the metallic unconventional clathrate BaNi 2 P 4 , hosting Ba cations in oversized Ni 8 P 16 cages, are investigated. A novel method of single-crystal growth was developed, yielding 2–3 mm sized crystals of BaNi 2 P 4 . We also developed a setup to accurately measure thermal conductivity and electrical resistivity of the synthesized single crystals in a wide temperature range avoiding crystal remounting. BaNi 2 P 4 has a metallic temperature dependence of its electrical resistivity (decreasing with decreasing temperature) and manifests an unconventional T 2 power law for 50 K < T < 300 K; below 50 K, the power-law exponent increases gradually such that below 10 K the power law is T 5 , a predicted but extremely rarely experimentally observed dependence for peculiar electron–phonon interactions. Furthermore, electronic band structure calculations, consistent with measurements of de Haas–van Alphen oscillations, show large band dispersions with significant contributions of Ba orbitals to states near the Fermi level, which is atypical for clathrates. The thermal properties of BaNi 2 P 4 were probed using a combination of variable-temperature single-crystal X-ray diffraction experiments, heat capacity measurements, first-principles phonon dispersion calculations, and inelastic neutron scattering measurements. BaNi 2 P 4 exhibits significant hybridization of the Ba-guest and Ni–P-framework vibrational modes, which may be enhanced via the detected split of the Ba position, which results in strong Ba-framework interactions.

36 MATERIALS SCIENCE↗