Low-cost, high-efficiency silicon by heat exchanger method and fixed abrasive slicing technique

The paper describes the heat exchanger method (HEM) for growing silicon crystals. The problem of ingot cracking was solved by using a graded structure silica crucible, and vacuum processing eliminated expensive high-purity argon. Solar cells fabricated from HEM silicon demonstrated conversion efficiencies up to 15% (AM1) at low cost, using square cross-section, single crystal silicon. A modified multiblade slurry machine was adapted for multiwire fixed abrasive slicing of silicon which uses a diamond attached to wires; this method provides a conversion ratio of 1.08 sq m of wafer per kg of silicon ingot, and produces wafers free of edge chipping with a surface damage of 3-5 microns.

Khattak, C. P.↗
NASA NTRS1978

Silicon Sheet Growth Development for the Large Area Sheet Task of the Low Cost Solar Array Project. Heat Exchanger Method - Ingot Casting Fixed Abrasive Method - Multi-Wire Slicing

Solar cells fabricated from HEM cast silicon yielded up to 15% conversion efficiencies. This was achieved in spite of using unpurified graphite parts in the HEM furnace and without optimization of material or cell processing parameters. Molybdenum retainers prevented SiC formation and reduced carbon content by 50%. The oxygen content of vacuum cast HEM silicon is lower than typical Czochralski grown silicon. Impregnation of 45 micrometers diamonds into 7.5 micrometers copper sheath showed distortion of the copper layer. However, 12.5 micrometers and 15 micrometers copper sheath can be impregnated with 45 micrometers diamonds to a high concentration. Electroless nickel plating of wires impregnated only in the cutting edge showed nickel concentration around the diamonds. This has the possibility of reducing kerf. The high speed slicer fabricated can achieve higher speed and longer stroke with vibration isolation.

Schmid, F.↗
NASA NTRS1977

Heat exchanger-ingot casting/slicing process, phase 1: Silicon sheet growth development for the large area silicon sheet task of the low cost silicon solar array project

A controlled growth, heat-flow and cool-down process is described that yielded silicon with a high degree of single crystallinity. Even when the seed melted out, very large grains formed. Solar cell samples made from cast material yielded conversion efficiency of over 9%. Representative characterizations of grown silicon demonstrated a dislocation density of less than 100/sq cm and a minority carrier diffusion length of 31 micron. The source of silicon carbide in silicon ingots was identified to be from graphite retainers in contact with silica crucibles. Higher growth rates were achieved with the use of a graphite plug at the bottom of the silica crucible.

Schmid, F.↗