Schneiderman, Benjamin

Publications and source records attributed to Schneiderman, Benjamin.

4 records

DOE OSTI2023

In situ synchrotron X-ray diffraction analysis of ultrasonically assisted microstructure refinement during laser melting process

This work investigates the effect of ultrasonic treatment (UST) on the microstructure of AA4043 alloy during laser melting process. Here, the study utilizes in situ synchrotron X-ray diffraction (SXRD) and postmortem electron backscatter diffraction (EBSD) techniques to examine the ultrasonic grain refinement mechanism. The SXRD diffraction patterns exhibit higher continuity of major diffraction rings in the UST-test pattern, indicating a more refined grain structure. The presence of new diffraction spots in the post-test diffraction pattern with UST suggests the breakdown of epitaxial growth of columnar dendrites during solidification. Thermal profiles determined by analyzing the lattice parameter evolution show a faster cooling rate with UST. The inverse pole figures and aspect ratio distribution from EBSD reveal that the UST samples exhibit a refined, more equiaxed grain structure along the weld centerline. UST sample also develops more fine-sized low angle grain boundaries (LAGBs). These features offer better hot-cracking resistance in aluminum alloys.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Synchrotron X-ray diffraction analysis of constituent phases in transition joint between nickel alloy 738LC and a MnFeCoNiCu alloy

Synchrotron x-ray diffraction (XRD) analysis was performed on transition joints between a single-phase MnFeCoNiCu alloy and Ni-base Alloy 738LC to efficiently identify the constituent phases across the interface, with different levels of material intermixing generated by laser-welding with variable power. Here, the intermixing extent was quantified by postmortem energy dispersive x-ray spectroscopy mapping. Diffraction-based analyses on complex composition spaces with limited prior data present significant challenges because elemental substitution in both disordered and ordered phases is more extensive than in conventional alloy spaces, which may effectuate relatively large shifts in the observed lattice parameters that convolute the analysis. Therefore, thermodynamic simulations and crystallographic literature data were employed to construct a system-specific diffraction library of twelve prospective phases for the composition space investigated. Subsequently, for predicted disordered cubic phases, statistical hard-sphere models were established to estimate the lattice parameters and predict diffraction peak positions for inclusion in the library. The library was then employed to analyze diffraction profiles measured from the variably intermixed transition joints, with focus on accounting for both high and low-intensity peaks. 99.0 % of diffraction peaks with relative intensity greater than 0.001 were assigned to phases from the system-specific library, exemplifying rigorous peak accounting and indicating that no unexpected phases were present. Up to six of the twelve library phases were experimentally found in the transition joints. The lattice parameters predicted by the statistical hard-sphere model based upon thermodynamic simulations agree reasonably well with the measured values for the disordered FCC matrix phase.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Influence of oxygen on performance of multi-principal element alloy as braze filler for Ni-base alloys

In manufacturing of multi-principal element alloys (MPEAs), the casting process is often a primary point of oxygen introduction to the material system, which was demonstrated by the laboratory scale button arc-melting process. Oxygen introduction raises concerns for the mechanical performance of these alloys if employed as structural materials alone or in engineering applications, such as serving as filler materials to enable joining of similar or dissimilar alloy pairs that are conventionally considered difficult to join. In this work, oxide inclusions in an as-cast off-equiatomic MnFeCoNiCu MPEA and Ni-base alloy braze joints made with this MPEA were evaluated by synchrotron x-ray diffraction mapping and electron microscopy. MnO was found to be prevalent throughout the cast MPEA and was chemically reduced during brazing by trace Al from the base material, Ni-base Alloy 600. Incomplete reaction of the MnO with Al, and some alternative reaction with Cr, left a mixture of MnO, Al 2 O 3 , and Cr 2 O 3 in the as-brazed joint, with the oxides concentrated near the braze centerline due to directional solidification. Further, in the braze joints, the non-oxide constituent phases detected were an FCC matrix and particles of Cr 23 C 6 , Cr 7 C 3 , and TiN which are all native to Alloy 600. The evolution of oxides within the brazed joints at elevated service temperatures of 600-800°C was also evaluated. While MnO and Al 2 O 3 were stable during high-temperature service, Cr 2 O 3 particles grew to several hundred microns, with dissolved oxygen in the MPEA providing a significant source for oxide growth. Comparing tensile performance of the as-brazed condition with post-service conditions showed that the evolution of oxide particles contributed to an increase in strength and decrease in ductility of the brazed joints. Evaluating particle morphologies among fracture surfaces of individual specimens demonstrated that large Cr 2 O 3 particles and continuous cluster networks of Al 2 O 3 were the features most detrimental to total elongation. Hence, unmitigated evolution of oxygen-containing species during brazing and service conditions is detrimental to the ductility of the brazed joints, which highlights the importance of oxygen control in initial manufacturing of MPEAs for engineering applications.

36 MATERIALS SCIENCE↗

DOE OSTI2021

In situ synchrotron diffraction and modeling of non-equilibrium solidification of a MnFeCoNiCu alloy

The solidification mechanism and segregation behavior of laser-melted Mn 35 Fe 5 Co 20 Ni 20 Cu 20 was firstly investigated via in situ synchrotron x-ray diffraction at millisecond temporal resolution. The transient composition evolution of the random solid solution during sequential solidification of dendritic and interdendritic regions complicates the analysis of synchrotron diffraction data via any single conventional tool, such as Rietveld refinement. Therefore, a novel approach combining a hard-sphere approximation model, thermodynamic simulation, thermal expansion measurement and microstructural characterization was developed to assist in a fundamental understanding of the evolution of local composition, lattice parameter, and dendrite volume fraction corresponding to the diffraction data. This methodology yields self-consistent results across different methods. Via this approach, four distinct stages were identified, including: (I) FCC dendrite solidification, (II) solidification of FCC interdendritic region, (III) solid-state interdiffusion and (IV) final cooling with marginal diffusion. It was found out that in Stage I, Cu and Mn were rejected into liquid as Mn 35 Fe 5 Co 20 Ni 20 Cu 20 solidified dendritically. During Stage II, the lattice parameter disparity between dendrite and interdendritic region escalated as Cu and Mn continued segregating into the interdendritic region. After complete solidification, during Stage III, the lattice parameter disparity gradually decreases, demonstrating a degree of composition homogenization. The volume fraction of dendrites slightly grew from 58.3 to 65.5%, based on the evolving composition profile across a dendrite/interdendritic interface in diffusion calculations. Postmortem metallography further confirmed that dendrites have a volume fraction of 64.7 ± 5.3% in the final microstructure.

36 MATERIALS SCIENCE↗