DOE OSTI2025

Fabricating Silver Nanowire–IZO Composite Transparent Conducting Electrodes at Roll-to-Roll Speed for Perovskite Solar Cells

This study addresses the challenges of efficient, large-scale production of flexible transparent conducting electrodes (TCEs). We fabricate TCEs on polyethylene terephthalate (PET) substrates using a high-speed roll-to-roll (R2R) compatible method that combines gravure printing and photonic curing. The hybrid TCEs consist of Ag metal bus lines (Ag MBLs) coated with silver nanowires (AgNWs) and indium zinc oxide (IZO) layers. All materials are solutions deposited at speeds exceeding 10 m/min using gravure printing. We conduct a systematic study to optimize coating parameters and tune solvent composition to achieve a uniform AgNW network. The entire stack undergoes photonic curing, a low-energy annealing method that can be completed at high speeds and will not damage the plastic substrates. The resulting hybrid TCEs exhibit a transmittance of 92% averaged from 400 nm to 1100 nm and a sheet resistance of 11 Ω/sq. Mechanical durability is tested by bending the hybrid TCEs to a strain of 1% for 2000 cycles. The results show a minimal increase (<5%) in resistance. The high-throughput potential is established by showing that each hybrid TCE fabrication step can be completed at 30 m/min. We further fabricate methylammonium lead iodide solar cells to demonstrate the practical use of these TCEs, achieving an average power conversion efficiency (PCE) of 13%. The high-performance hybrid TCEs produced using R2R-compatible processes show potential as a viable choice for replacing vacuum-deposited indium tin oxide films on PET.

14 SOLAR ENERGY↗

DOE OSTI2021

Photonic Curing of Nickel Oxide Transport Layer and Perovskite Active Layer for Flexible Perovskite Solar Cells: A Path Towards High-Throughput Manufacturing

High-throughput roll-to-roll (R2R) manufacturing of perovskite solar cells (PSCs) is currently limited by thermal processes that take tens of minutes each, translating to impractically long annealing tools at high web speeds. In addition, PSCs are usually made with metal oxide transport layer materials that require high temperatures for thermal annealing. Here, we demonstrate the fabrication of PSCs using photonic curing, instead of thermal annealing, to convert NiO x directly from sol-gel precursors for hole transport layers and to crystallize methylammonium lead iodide (MAPbI 3 ) active layers on flexible Willow ® Glass substrates. Photonic curing uses short, intense pulses of light to process materials at a high speed, hence it is compatible with R2R manufacturing. We achieved power conversion efficiencies (PCEs) of 11.7% in forward-scan and 10.9% in reverse-scan for PSCs made with photonic cured NiO x and MAPbI 3 films. Furthermore, both NiO x and MAPbI 3 films could be processed with a single photonic curing pulse, with a web speed of 5.7 m/min, and still produce PCEs comparable to thermally annealed control samples. Based on the single-pulse photonic curing condition for each film, we project a web speed of 26 m/min, laying a pathway to high-throughput production of perovskite solar modules.

14 SOLAR ENERGY↗

DOE OSTI2020

Photonic Curing Enabling High-Speed Processing for Perovskite Solar Cells

The thermal annealing step is the bottleneck to high-throughput manufacturing of perovskite solar cells. In this work, we investigate photonic curing to replace thermal annealing for the sol gel NiO hole transport layer. Using solar cell device current density-voltage performance as a metric, we compare the effects of thermal annealing and photonic curing on the conversion of sol gel NiO films deposited on top of indium tin oxide coated Willow® glass substrates. The significant reduction in processing time validates photonic curing as the enabling tool for high-speed manufacturing.

Xu, Weijie↗

DOE OSTI2020

Photonic curing of solution-deposited ZrO 2 dielectric on PEN: a path towards high-throughput processing of oxide electronics

High-throughput manufacturing of oxide electronics will enable new applications ranging from large-area displays to flexible medical devices and low-cost solar panels. However, high quality oxide films from solution-based precursors typically require 20 minutes or more of thermal annealing at high temperature (> 250 °C) for each layer, severely limiting both the throughput and substrate choice. Here, we report high speed photonic curing of ZrO 2 dielectric thin films on flexible plastic substrates. The curing and patterning processes can be achieved simultaneously by using shadow mask patterning or adjusting conditions to convert oxide only on top of underlying metal contacts, i.e. self-aligned patterning. Metal-insulator-metal capacitors using two layers of ZrO 2 films photonically cured in just 100 seconds per layer show non-dispersive capacitance-frequency behavior from 10 2 to 10 6 Hz, high areal capacitance of 200 nF/cm 2 and low dissipation factor of 0.03 at 10 5 Hz, leakage current density of ~ 10 -7 A/cm 2 at an applied field of 2 MV/cm, and a breakdown field of nearly 8 MV/cm. Using an upgraded tool, similar dielectric properties are achieved in as short as 100 milliseconds using a single pulse of light, revealing a pathway to oxide film processing beyond 30 m/min.

14 SOLAR ENERGY↗