Bend-Test Results of the MISSE 7 Flexural Stress Effects Experiment After 1.5 Years of Space Exposure

Low Earth orbital environmental exposure can cause degradation of exterior spacecraft materials. Radiation and thermal exposure often result in bond-breaking and embrittlement of polymers, reducing mechanical strength and structural integrity. The Flexural Stress Effects Experiment (FSEE) was flown with the objective of determining the role of space exposure on the degradation of polymers under flexural stress. The FSEE samples were flown in a wake orientation on the exterior of International Space Station for 1.5 years. Twenty-three polyimide and fluorinated polymers with various coatings were flown: 11 bent over a 0.375-inch diameter holder and 12 over a 0.25-inch diameter holder. A non-standard bend-test procedure was used to determine the surface strain at which embrittled polymers crack. None of the control samples cracked, even under surface strains up to 19.7%, although one coating cracked. Of the 10 flight samples tested, seven indicated increased embrittlement through bend-test cracking at surface strains from 0.65% to 8.11%. Therefore, most of the tested polymers were embrittled due to space exposure, when compared to their control samples. The samples flown over the 0.375-inch holder were more embrittled than those on the 0.25-inch holder. Determination of the extent of space induced embrittlement of polymers is important for designing durable spacecraft.

Snow, Kate E.↗

NASA NTRS2017

Erosion Results of the MISSE 8 Polymers Experiment After 2 Years of Space Exposure on the International Space Station

Polymers and other oxidizable materials on the exterior of spacecraft in the low Earth orbit (LEO) space environment can be eroded due to reaction with atomic oxygen (AO). Therefore, in order to design durable spacecraft, it is important to know the LEO AO erosion yield (E(sub y), volume loss per incident oxygen atom) of materials susceptible to AO reaction. A spaceflight experiment, called the Polymers Experiment, which contained 42 samples, was developed to determine the effect of solar exposure on the AO E(sub y) of fluoropolymers flown in ram, wake, or zenith orientations. The Polymers Experiment was exposed to the LEO space environment on the exterior of the International Space Station (ISS) as part of the Materials International Space Station Experiment 8 (MISSE 8) mission. The MISSE 8 mission included samples flown in a zenith/nadir orientation for 2.14 years in the MISSE 8 Passive Experiment Container (PEC), and samples flown in a ram/wake orientation for 2.0 years in the Optical Reflector Materials Experiment-III (ORMatEIII) tray. The experiment included Kapton H (Registered Trademark) witness samples for AO fluence determination in each orientation. This paper provides an overview of the MISSE 8 mission, a description of the flight experiment with details on the polymers flown, the characterization techniques used, the AO fluence for each exposure orientation, and the LEO E(sub y) results. The E(sub y) of Teflon fluorinated ethylene propylene (FEP) samples flown in ram, wake, and zenith orientations have been compared, and the E(sub y) was found to be highly dependent on orientation and therefore environmental exposure. The FEP E(sub y) was found to directly correlate with the solar exposure/AO fluence ratio showing the effect of solar radiation and/or heating due to solar exposure on FEP erosion. In addition, back-surface carbon painted FEP (C-FEP) flown in the zenith orientation had a significantly higher E(sub y) than clear FEP or Al-FEP further indicating that heating has a significant impact on the erosion of FEP. This experiment provides valuable LEO flight data on the erosion of Teflon FEP, a commonly used spacecraft thermal insulation.

Teflon↗

NASA NTRS2016

Erosion Results of the MISSE 7 Polymers Experiment and Zenith Polymers Experiment After 1.5 Years of Space Exposure

Polymers and other oxidizable materials on the exterior of spacecraft in the low Earth orbit (LEO) space environment can be eroded due to reaction with atomic oxygen (AO). Therefore, in order to design durable spacecraft it is important to know the LEO AO erosion yield (E(sub y), volume loss per incident oxygen atom) of materials susceptible to AO reaction. Two spaceflight experiments, the Polymers Experiment and the Zenith Polymers Experiment, were developed to determine the AO E(sub y) of various polymers flown in ram, wake or zenith orientations in LEO. These experiments were flown as part of the Materials International Space Station Experiment 7 (MISSE 7) mission for 1.5 years on the exterior of the International Space Station (ISS). The experiments included Kapton H(TradeMark) witness samples for AO fluence determination in ram and zenith orientations. The Polymers Experiment also included samples to determine whether AO erosion of high and low ash containing polymers is dependent on fluence. This paper provides an overview of the MISSE 7 mission, a description of the flight experiments with details on the polymers flown, the characterization techniques used, the AO fluence for each exposure orientation, and the LEO E(sub y) results. The E(sub y) values ranged from 7.99x10(exp -28)cu cm/atom for TiO2/Al2O3 coated Teflon(TradeMark) fluorinated ethylene propylene (FEP) flown in the ram orientation to 1.22x10(exp -23cu cm/atom for polyvinyl alcohol (PVOH) flown in the zenith orientation. The E(sub y) of similar samples flown in different orientations has been compared to help determine solar exposure and associated heating effects on AO erosion. The E(sub y) data from these ISS spaceflight experiments provides valuable information for LEO spacecraft design purposes.

Teflon↗

NASA NTRS2016

Erosion Data from the MISSE 8 Polymers Experiment After 2 Years of Space Exposure on the International Space Station

The Polymers Experiment was exposed to the low Earth orbit (LEO) space environment for 2.14 and 2.0 years as part of the Materials International Space Station Experiment 8 (MISSE 8) and the Optical Reflector Materials Experiment-III (ORMatE-III), respectively. The experiment contained 42 samples, which were flown in either ram, wake, or zenith orientations. The primary objective was to determine the effect of solar exposure on the atomic oxygen erosion yield (Ey) of fluoropolymers. This paper provides an overview of the experiment with details on the polymers flown, the characterization techniques used, the atomic oxygen fluence for each exposure orientation, and the LEO Ey results. The Ey values for the fluoropolymers range from 1.45 x 10(exp -25) cm(exp 3)/atom for white Tedlar Registered Trademark (polyvinyl fluoride with white titanium dioxide pigment) flown in the ram orientation to 6.32 x 10(exp -24) cm(exp 3)/atom for aluminized-Teflon Registered Trademark fluorinated ethylene propylene (Al-FEP) flown in the zenith orientation. Erosion yield data for FEP flown in ram, wake and zenith orientations are compared, and the Ey was found to be highly dependent on orientation, hence environmental exposure. Teflon FEP had an order of magnitude higher Ey when flown in the zenith direction (6.32 x10(exp -24) cm(exp3)/atom) as compared to the ram direction (2.37 x 10(exp -25) cm(exp 3)/atom). The Ey of FEP was found to increase with a direct correlation to the solar exposure/AO fluence ratio showing the effect of solar radiation and/or heating due to solar exposure on FEP erosion. In addition, back-surface carbon painted FEP (C-FEP) flown in the zenith orientation had a significantly higher Ey than clear FEP or Al-FEP further indicating that heating has a significant impact on the erosion of FEP, particularly in the zenith orientation.

Solar radiation↗

NASA NTRS2014

Design, Analysis, and On-Sun Evaluation of Reflective Strips Under Controlled Buckling

Solar concentrators are envisioned for use in a variety of space-based applications, including applications involving in situ resource utilization. Identifying solar concentrators that minimize mass and cost are of great interest, especially since launch cost is driven in part by the mass of the payload. Concentrators must also be able to survive the wide temperature excursions on the lunar surface. Identifying smart structures which compensate for changes in concentrator geometry brought about by temperature extremes are of interest. Some applications may benefit from the ability to change the concentrators focal pattern at will. This paper addresses a method of designing a single reflective strip to produce a desired focal pattern through the use of controlled buckling. Small variations in the cross section over the length of the reflective strip influence the distribution of light in the focal region. A finite element method of analysis is utilized here which calculates the curve produced for a given strip cross section and axial load. Varying axial force and strip cross section over the length of the reflective strip provide a means of optimizing ray convergence in the focal region. Careful selection of a tapered cross section yields a reflective strip that approximates a parabola. An array of reflective strips under controlled buckling produces a light weight concentrator and adjustments in the compression of individual strips provide a means of compensating for temperature excursions or changing the focal pattern at will.

solar collectors↗

NASA NTRS2013

MISSE 6 Stressed Polymers Experiment Atomic Oxygen Erosion Data

Polymers and other oxidizable materials used on the exterior of spacecraft in the low Earth orbit (LEO) space environment can be eroded away by reaction with atomic oxygen (AO). For spacecraft design, it is important to know the LEO AO erosion yield, Ey (volume loss per incident oxygen atom), of materials susceptible to AO erosion. The Stressed Polymers Experiment was developed and flown as part of the Materials International Space Station Experiment 6 (MISSE 6) to compare the AO erosion yields of stressed and non-stressed polymers to determine if erosion is dependent upon stress while in LEO. The experiment contained 36 thin film polymer samples that were exposed to ram AO for 1.45 years. This paper provides an overview of the Stressed Polymers Experiment with details on the polymers flown, the characterization techniques used, the AO fluence, and the erosion yield results. The MISSE 6 data are compared to data for similar samples flown on previous MISSE missions to determine fluence or solar radiation effects on erosion yield.

deGroh, Kim K.↗

NASA NTRS2012

Preliminary Design of a Galactic Cosmic Ray Shielding Materials Testbed for the International Space Station

The preliminary design of a testbed to evaluate the effectiveness of galactic cosmic ray (GCR) shielding materials, the MISSE Radiation Shielding Testbed (MRSMAT) is presented. The intent is to mount the testbed on the Materials International Space Station Experiment-X (MISSE-X) which is to be mounted on the International Space Station (ISS) in 2016. A key feature is the ability to simultaneously test nine samples, including standards, which are 5.25 cm thick. This thickness will enable most samples to have an areal density greater than 5 g/sq cm. It features a novel and compact GCR telescope which will be able to distinguish which cosmic rays have penetrated which shielding material, and will be able to evaluate the dose transmitted through the shield. The testbed could play a pivotal role in the development and qualification of new cosmic ray shielding technologies.

Gaier, James R.↗

NASA NTRS2012

An Examination of Radiation Induced Tensile Failure of Stressed and Unstressed Polymer Films Flown on MISSE-6

Thin film polymers are used in many spacecraft applications for thermal control (multilayer insulation and sunshields), as lightweight structural members (solar array blankets, inflatable/deployable structures) and have been proposed for propulsion (solar sails). Polymers in these applications are often under a tensile load and are directly exposed to the space environment, therefore it is important to understand the effect of stress in combination with the environment on the durability of these polymer films. The purpose of the Polymer Film Tensile Experiment, flown as part of Materials International Space Station Experiment 6 (MISSE 6), was to expose a variety of polymer films to the low Earth orbital environment under both relaxed and tension conditions. This paper describes the results of post flight tensile testing of these samples.

Miller, Sharon K.↗

NASA NTRS2011

Design for On-Sun Evaluation of Evaporator Receivers

A heat pipe designed for operation as a solar power receiver should be optimized to accept the solar energy flux and transfer this heat into a reactor. Optical properties of the surface, thermal conductance of the receiver wall, contact resistance of the heat pipe wick, and other heat pipe wick properties ultimately define the maximum amount of power that can be extracted from the concentrated sunlight impinging on the evaporator surface. Modeling of solar power receivers utilizing optical and physical properties provides guidance to their design. On-sun testing is another important means of gathering information on performance. A test rig is being designed and built to conduct on-sun testing. The test rig is incorporating a composite strip mirror concentrator developed as part of a Small Business Innovative Research effort and delivered to NASA Glenn Research Center. In the strip concentrator numerous, lightweight composite parabolic strips of simple curvature were combined to form an array 1.5 m x 1.5 m in size. The line focus of each strip is superimposed in a central area simulating a point of focus. A test stand is currently being developed to hold the parabolic strip concentrator, track the sun, and turn the beam downward towards the ground. The hardware is intended to be sufficiently versatile to accommodate on-sun testing of several receiver concepts, including those incorporating heat pipe evaporators. Characterization devices are also being developed to evaluate the effectiveness of the solar concentrator, including a receiver designed to conduct calorimetry. This paper describes the design and the characterization devices of the on-sun test rig, and the prospect of coupling the concentrated sunlight to a heat pipe solar power receiver developed as part of another Small Business Innovative Research effort.

Jaworske, Donald A.↗

NASA NTRS2011

Evaluating Heat Pipe Performance in 1/6 g Acceleration: Problems and Prospects

Heat pipes composed of titanium and water are being considered for use in the heat rejection system of a fission power system option for lunar exploration. Placed vertically on the lunar surface, the heat pipes would operate as thermosyphons in the 1/6 g environment. The design of thermosyphons for such an application is determined, in part, by the flooding limit. Flooding is composed of two components, the thickness of the fluid film on the walls of the thermosyphon and the interaction of the fluid flow with the concurrent vapor counter flow. Both the fluid thickness contribution and interfacial shear contribution are inversely proportional to gravity. Hence, evaluating the performance of a thermosyphon in a 1 g environment on Earth may inadvertently lead to overestimating the performance of the same thermosyphon as experienced in the 1/6 g environment on the moon. Several concepts of varying complexity have been proposed for evaluating thermosyphon performance in reduced gravity, ranging from tilting the thermosyphons on Earth based on a cosine function, to flying heat pipes on a low-g aircraft. This paper summarizes the problems and prospects for evaluating thermosyphon performance in 1/6 g.

Jaworske, Donald A.↗

NASA NTRS2009

Thermal Interface Evaluation of Heat Transfer from a Pumped Loop to Titanium-Water Thermosyphons

Titanium-water thermosyphons are being considered for use in the heat rejection system for lunar outpost fission surface power. Key to their use is heat transfer between a closed loop heat source and the heat pipe evaporators. This work describes laboratory testing of several interfaces that were evaluated for their thermal performance characteristics, in the temperature range of 350 to 400 K, utilizing a water closed loop heat source and multiple thermosyphon evaporator geometries. A gas gap calorimeter was used to measure heat flow at steady state. Thermocouples in the closed loop heat source and on the evaporator were used to measure thermal conductance. The interfaces were in two generic categories, those immersed in the water closed loop heat source and those clamped to the water closed loop heat source with differing thermal conductive agents. In general, immersed evaporators showed better overall performance than their clamped counterparts. Selected clamped evaporator geometries offered promise.

Jaworske, Donald A.↗

NASA NTRS2008

NASA Glenn Research Center's Materials International Space Station Experiments (MISSE 1-7)

NASA Glenn Research Center (Glenn) has 39 individual materials flight experiments (>540 samples) flown as part of the Materials International Space Station Experiment (MISSE) to address long duration environmental durability of spacecraft materials in low Earth orbit (LEO). MISSE is a series of materials flight experiments consisting of trays, called Passive Experiment Carriers (PECs) that are exposed to the space environment on the exterior of the International Space Station (ISS). MISSE 1-5 have been successfully flown and retrieved and were exposed to the space environment from one to four years. MISSE 6A & 6B were deployed during the STS-123 shuttle mission in March 2008, and MISSE 7A & 7B are being prepared for launch in 2009. The Glenn MISSE experiments address atomic oxygen (AO) effects such as erosion and undercutting of polymers, AO scattering, stress effects on AO erosion, and in-situ AO fluence monitoring. Experiments also address solar radiation effects such as radiation induced polymer shrinkage, stress effects on radiation degradation of polymers, and radiation degradation of indium tin oxide (ITO) coatings and spacesuit fabrics. Additional experiments address combined AO and solar radiation effects on thermal control films, paints and cermet coatings. Experiments with Orion Crew Exploration Vehicle (CEV) seals and UltraFlex solar array materials are also being flown. Several experiments were designed to provide ground-facility to in-space calibration data thus enabling more accurate in-space performance predictions based on ground-laboratory testing. This paper provides an overview of Glenn s MISSE 1-7 flight experiments along with a summary of results from Glenn s MISSE 1 & 2 experiments.

deGroh, Kim K.↗

NASA NTRS2007

Lunar Simulation in the Lunar Dust Adhesion Bell Jar

The Lunar Dust Adhesion Bell Jar has been assembled at the NASA Glenn Research Center to provide a high fidelity lunar simulation facility to test the interactions of lunar dust and lunar dust simulant with candidate aerospace materials and coatings. It has a sophisticated design which enables it to treat dust in a way that will remove adsorbed gases and create a chemically reactive surface. It can simulate the vacuum, thermal, and radiation environments of the Moon, including proximate areas of illuminated heat and extremely cold shadow. It is expected to be a valuable tool in the development of dust repellant and cleaning technologies for lunar surface systems.

Gaier, James R.↗

NASA NTRS2002

Facility and Methods Developed for Simulated Space Vacuum Ultraviolet Exposure Testing of Polymer Films

Vacuum ultraviolet (VUV) radiation of wavelengths between 115 and 200 nm produced by the Sun in the space environment can degrade polymer films, producing changes in their optical, mechanical, and chemical properties. These effects are particularly important for thin polymer films being considered for ultralightweight space structures, because, for most polymers, VUV radiation is absorbed in a thin surface layer. The NASA Glenn Research Center has developed facilities and methods for long-term ground testing of polymer films to evaluate space environmental VUV radiation effects. VUV exposure can also be used as part of combined or sequential simulated space environmental exposures to determine combined damaging effects with other aspects of the space environment, which include solar ultraviolet radiation, solar flare x-rays, electron and proton radiation, atomic oxygen (for low-Earth-orbit missions), and temperature effects. Because the wavelength sensitivity of VUV damage is not well known for most materials, Glenn's VUV facility uses a broad-spectrum deuterium lamp with a magnesium fluoride window that provides output between 115 and 200 nm. Deuterium lamps of this type were characterized by the National Institute of Standards and Technology and through measurements at Glenn. Spectral irradiance measurements show that from approximately 115 to 160 nm, deuterium lamp irradiance can be many times that of air mass zero solar irradiance, and as wavelength increases above approximately 160 nm, deuterium lamp irradiance decreases in comparison to the Sun. The facility is a cryopumped vacuum chamber that achieves a system pressure of approximately 5310(exp -6) torr. It contains four individual VUV-exposure compartments in vacuum, separated by water-cooled copper walls to minimize VUV radiation and any sample contamination cross interactions between compartments. Each VUV-exposure compartment contains a VUV deuterium lamp, a motor-controlled sample stage coupled with a moveable cesium iodide VUV phototube, and two thermocouples for temperature measurement. The vacuum chamber and exterior equipment is shown. Each VUV lamp is located at the top of the chamber with its projection-tube pushed through an O-ring compression fitting. The lamp assemblies are located on ports that can be isolated from the rest of the vacuum chamber, permitting maintenance or replacement of the lamps without breaking vacuum in the main chamber where the samples are located. A view of two of the four interior VUV-exposure compartments, including the moveable sample stages and detector holders is also shown. Glenn is using this facility to support testing of Next Generation Space Telescope sunshield materials that is being led by the NASA Goddard Space Flight Center and to develop an understanding of the wavelength, intensity, and temperature dependence of VUV-induced polymer degradation.

Dever, Joyce A.↗

NASA NTRS2002

Simulated Space Vacuum Ultraviolet (VUV) Exposure Testing for Polymer Films

Vacuum ultraviolet (VUV) radiation of wavelengths between 115 and 200 nm produced by the sun in the space environment can cause degradation to polymer films producing changes in optical, mechanical, and chemical properties. These effects are particularly important for thin polymer films being considered for ultra-lightweight space structures, because, for most polymers, VUV radiation is absorbed in a thin surface layer. NASA Glenn Research Center has developed facilities and methods for long-term ground testing of polymer films to evaluate space environmental VUV radiation effects. VUV exposure can also be used as part of sequential simulated space environmental exposures to determine combined damaging effects. This paper will describe the effects of VUV on polymer films and the necessity for ground testing. Testing practices used at Glenn Research Center for VUV exposure testing will be described including characterization of the VUV radiation source used, calibration procedures traceable to the National Institute of Standards and Technology (NIST), and testing techniques for VUV exposure of polymer surfaces.

Dever, Joyce A.↗

NASA NTRS2001

Specimens Prepared for Materials International Space Station Experiment

The Materials International Space Station Experiment (MISSE) is a materials flight experiment sponsored by the Materials and Manufacturing Directorate of the Air Force Research Laboratory at Wright-Patterson Air Force Base and the NASA Space Environmental Effects Program at the NASA Marshall Space Flight Center. MISSE is a cooperative effort among the Air Force, several NASA field centers, and industry. The experiment package will be placed on the exterior of the International Space Station in the summer of 2001. Approximately half of the specimens will be exposed to the space environment for 1 year, and the other half will be exposed for 3 years. The Electro-Physics Branch at the NASA Glenn Research Center has prepared and delivered over 150 specimens to be included in MISSE. Specimens include: 1) Double-coated polyimide Kapton to compare mass loss from in-space atomic oxygen undercutting erosion to ground-laboratory atomic oxygen undercutting erosion for predicting in-space durability; 2) Silicones to study changes in surface hardness and optical properties after combined atomic oxygen--ultraviolet radiation exposure for predicting in-space durability; 3) Forty-one different polymers to accurately measure their atomic oxygen erosion yields; 4) Scattering chambers to study atomic oxygen scattering characteristics that are relevant to the degradation found in spacecraft with exterior openings; 5) Thin polymer film disks and tensile specimens to study the effects of radiation on their optical properties and mechanical properties; 6) Lightweight intercalated graphite epoxy composites to study electromagnetic interference shielding performance; and 7) Polymer-based materials utilizing new atomic oxygen protection concepts to study their durability.

Banks, Bruce A.↗

NASA NTRS2000

Steady State Vacuum Ultraviolet Exposure Facility With Automated Calibration Capability

NASA Glenn Research Center at Lewis Field designed and developed a steady state vacuum ultraviolet automated (SSVUVa) facility with in situ VUV intensity calibration capability. The automated feature enables a constant accelerated VUV radiation exposure over long periods of testing without breaking vacuum. This test facility is designed to simultaneously accommodate four isolated radiation exposure tests within the SSVUVa vacuum chamber. Computer-control of the facility for long, term continuous operation also provides control and recording of thermocouple temperatures, periodic recording of VUV lamp intensity, and monitoring of vacuum facility status. This paper discusses the design and capabilities of the SSVUVa facility.

Stueber, Thomas J.↗

NASA NTRS2000

Facility Designed and Built to Investigate the Combined Effects of Contaminant and Atomic Oxygen on a Light-Transmitting Surface

A need exists to investigate changes in the transparency of a light-transmitting surface during simultaneous exposure to a contaminant and an atomic oxygen (AO) flux. This mechanism may be responsible for the degradation of the light-transmitting surfaces of both photovoltaic cells and photodiodes currently in use on many low-Earth-orbit spacecraft. To address this need, researchers from the Electro-Physics Branch of the NASA Glenn Research Center at Lewis Field built such a test system within their AO beam facility. This facility produces an effective AO flux of 1.4 10(exp 16) atoms/sq cm/sec and contains a three-axis positioning system that provides the motion capability necessary for test operations. During testing, a target surface is held directly within the AO beam and close to two contaminant effusion cells. The effusion cells are shielded from the AO beam, and the outgassing contaminant is constrained to move across the target surface when heat is applied to either of the reservoirs. A light source is periodically moved over the target surface, and the transmitted light intensity is checked with a photodiode located below the target. This light source is also periodically checked with a separate photodiode, which is protected from contamination and AO exposure, to allow adjustments necessary to maintain a consistent light intensity.