DOE OSTI2023

Fission gas retention of densely packed uranium carbonitride tristructural-isotropic fuel particles in a 3D printed SiC matrix

The Transformational Challenge Reactor (TCR) fuel form was designed to contain large, densely packed uranium carbonitride (UCN) tristructural-isotropic (TRISO) fuel particles within a 3D printed SiC matrix, increasing the uranium density compared to conventional TRISO fuel forms and offering full geometric freedom for core design. Here, this work summarizes initial low-burnup, high-power irradiation testing of TCR fuel materials, including loose UCN TRISO particles and integral fuel compacts with ~55% TRISO particles by volume, to evaluate fission gas retention. Fission gasses were fully retained in all loose particle tests and in integral compacts irradiated at low (<250 °C) surface temperatures. Initial testing at higher (~700–750 °C) fuel surface temperatures showed fission gas release (FGR) and complete fracture of three compacts, but no FGR was observed in later high temperature tests (~300–750 °C) of both fueled compacts and loose TRISO particles. Calculated thermal stresses in the failed compacts were far less than the measured strength of the SiC matrix and the stresses in some failed compacts were less than those in compacts that did not show FGR. Thermal stress-induced matrix cracks also would not cause complete fracture because the tensile stresses transition to compression in the higher temperature regions. Therefore, fuel failure was likely not caused by thermal stresses and may have been related to leakage currents from the electrical heaters and erratic fuel surface temperatures that were only observed in the test for which failure was observed. In any case, the matrix cracks propagated through the coatings of TRISO particles located in the high-density matrix regions on the peripheries of the compacts, resulting in measurable fission gas release. The discussion focuses on the importance of understanding matrix density distributions and the particle-matrix interface properties to prevent matrix cracks from causing TRISO particle failures.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2023

Comparison of unirradiated and irradiated AGR-2 TRISO fuel particle oxidation response

The silicon carbide (SiC) coating in a tristructural isotropic (TRISO) particle acts as a barrier to fission product release during reactor operation and accident scenarios. Oxidation and subsequent failure of the SiC layer during a rare air ingress event is a proposed mechanism for fission product release in a high-temperature gas-cooled reactor (HTGR). Although previous oxidation studies have analyzed unirradiated TRISO particle response, this study compared the oxidation behavior of irradiated and unirradiated TRISO particles from the second Advanced Gas Reactor Fuel Development and Qualification Program irradiation experiment (AGR-2). Particles with exposed SiC were subjected to six varying oxidizing tests in the Furnace for Irradiated TRISO Testing (FITT), examined for failure fraction with the Irradiated Microsphere Gamma Analyzer (IMGA) and characterized with focused ion beam and scanning/transmission electron microscopy techniques to analyze the oxide layer. Uncorrelated unirradiated particle failures throughout the series of exposures suggests that external factors inherent to the experiment increased particle failure sensitivity. However, irradiated particle observations indicated an increased failure response at 400 h 1400 °C in both 2% and 21% O 2 atmospheres above failure associated with external factors. Oxide thickness measurements after 400 h at 1400 °C revealed a greater oxidation rate than predicted by parabolic growth, which was attributed to the increased complexity of the oxide structure at longer exposure times. Altering the atmosphere from 21% to 2% O 2 reduced the average oxide thickness by approximately 12%–14% in both irradiated and unirradiated particles at 400 h 1400 °C. Altogether, the minor variations observed between irradiated and unirradiated particles in this study led to the conclusion that unirradiated TRISO particles can be used to approximate irradiated TRISO oxidation kinetics.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

AGR-2 irradiated TRISO particle IPyC/SiC interface analysis using FIB-SEM tomography

In this work, the morphology in the interface region between the inner pyrolytic carbon layer (IPyC) and silicon carbide (SiC) layers in tristructural-isotropic (TRISO) particle fuel from the AGR-2 irradiation experiment were studied using focused ion beam-scanning electron microscopy tomography. This work quantitatively described the interface and corresponding relevant metrics to understand how the microstructural features at the IPyC/SiC interface may influence actinide and fission product interactions with the SiC layer. Particles were selected with varied 110m Ag retention rates, and their volumes were reconstructed and analyzed for distributions of pores, fission product/actinide features, SiC, and IPyC. It was found that porosity accommodates fission products in the interface and SiC layers. The largest fission product/actinide precipitates were found in the interface region. This was also where the largest number fraction of fission products/actinides was found, consistent with SEM showing fission product/actinide pileup along selected areas of the interface region.

36 MATERIALS SCIENCE↗

DOE OSTI2022

On the efficacy of post-build thermomechanical treatments to improve properties of Zirconium fabricated using ultrasonic additive manufacturing

Here, hot-isostatic pressing has been applied to Zirconium plate fabricated using the ultrasonic additive manufacturing (UAM) technique to enhance interfacial bond quality. Specimens heated to 800 C for 1 h at 100 MPa pressure showed grain growth across many prior foil-to-foil interfaces, thereby increasing foil adhesion. In addition to the material softening induced by a loss of Hall-Petch strengthening, premature failure of specimens loaded parallel to the build direction was observed. Premature specimen failure was attributed to the local delamination at prior foil-to-foil boundaries where grain growth was pinned by Ti impurities introduced during the UAM process via the interaction between a Ti-alloy buffer foil and the welded Zr-foils underneath. In addition, the presence of Ti along select foil interfaces resulted in the nucleation and growth of secondary (Zr,Ti)(Fe,Cr) laves phases during higher-temperature thermomechanical processing. Using a combination of micro-scale X-ray computed tomography, fractography, and in-situ digital image correlation, the effect of defects along prior foil-to-foil boundaries was revealed as delamination-assisted plasticity accelerated specimen failure in preferred tensile orientations. These findings underscore the importance of impurity control when optimizing weld quality of higher-strength material systems using ultrasonic welding.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Initial Microstructure Examination of High Burnup Fuel with Varying Operational Burnups

his report presents an initial examination of the microstructure of high burnup UO 2 under pre- and postloss of coolant accident (LOCA) conditions. This work builds upon work previously conducted on high burnup UO 2 fuel at Oak Ridge National Laboratory. Studying microstructure evolutions that occur in UO 2 during irradiation, particularly in high burnup fuel, will provide a deeper understanding of fuel fragmentation under simulated LOCA conditions. High burnup UO 2 microstructural data is also needed to improve constitutive models intended to predict high burnup fuel fragmentation. The objective of this work is to begin the process of examining high burnup fuel microstructural features before and after LOCA testing to better understand mechanisms driving experimental observations. Several high burnup fuel samples were available from historic fuel shipments to ORNL. These samples were leveraged along with state-of-the-art microscopy capabilities. This report summarizes the current ongoing work using these fuel samples to interpret and analyze high burnup fuel microstructures.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

Oxidation Testing and Examination of AGR-2 Particles

Post-irradiation examination (PIE) oxidation testing is being performed at Oak Ridge National Laboratory (ORNL) on fuel particles from the second Advanced Gas Reactor (AGR) irradiation experiment (AGR-2). Tristructural isotropic (TRISO)-coated particles containing mixed uranium carbide and uranium oxide (UCO) fuel kernels were taken from AGR-2 Compact 5-4-2 and heated in the Furnace for Irradiated TRISO Testing (FITT) under varying oxidizing conditions. Details on Compact 5-4-2 PIE can be found in a previous report (Hunn et al. 2018).

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

Demonstration of Dimensional and Microstructural Postirradiation Examination Capabilities on MiniFuel Disk Specimens

This work demonstrates two new MiniFuel postirradiation examination (PIE) capabilities, laser profilometry and serial sectioning, for future use on alpha-U specimens for the upcoming Mini-99 irradiation campaign. Representative U–Mo disk specimens—3 mm in diameter and approximately 0.75 mm in thickness—were subjected to dimensional measurements using standard calipers, as well as a new Keyence CL-3000 series laser profilometry system designed to measure the surface of both sides of the disk simultaneously. The laser profilometry system captured thickness gradients across the specimens as large as 0.2 mm. Additionally, because of the limitations inherent to the use of calipers, caliper measurements consistently overestimated the initial volume of MiniFuel disk specimens compared to the laser profilometry method by up to 5%. However, the results show that optimal data collection and analysis procedures are crucial to avoiding significant artifacts during data collection that can lead to large errors (approximately 10%). Serial sectioning using a combination of ion milling and electron imaging was also demonstrated for the analysis of micron-sized control volumes. Nanometer- to micron-scale porosity was resolved on a representative U–Mo specimen before irradiation, even when the surface of the specimen appeared free of porosity. Future efforts to relate microstructural features (porosity, fission product distributions, and so on) to macroscale effects (dimensional changes, thermal conductivity degradation) require accurate characterization methods such as those demonstrated in this work. These advanced PIE capabilities will be applied to optimized alpha-U specimens for the upcoming Mini-99 neutron irradiation campaign.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

Fabrication of UN-Mo CERMET Nuclear Fuel Using Advanced Manufacturing Techniques

Ceramic-metallic nuclear fuels are a candidate fuel for nuclear thermal propulsion systems due to their high heat transport properties, which are necessary in very high-temperature environments. The conventional fabrication of uranium nitride–molybdenum fuel has been thoroughly studied in the past, but modern manufacturing techniques have presented a unique opportunity for further development within this field. This work demonstrates the use of advanced manufacturing techniques to produce nuclear fuel pellets composed of uranium nitride microspheres encased in a molybdenum matrix. Binder jetting is used to print molybdenum disks that are filled with uranium nitride microspheres and afterward sintered using spark plasma sintering. Two fuel pellets were fabricated to demonstrate the methodology and to provide a baseline analysis of the effects of temperature and pressure processing conditions. Characterization of the sintered fuel pellets includes detailed microstructural analysis and thermal conductivity measurements.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

Characterization of PyC/SiC interfaces with FIB-SEM tomography

Tristructural-isotropic (TRISO) fuel is being considered for multiple reactor designs due to its exceptional performance. This work studies pyrocarbon (PyC) and silicon carbide (SiC) substrates that are near-representative of the inner pyrocarbon (IPyC) and SiC in TRISO fuel. Focused ion beam (FIB)-scanning electron microscopy (SEM) tomography was used to understand the influence of different processing routes on the PyC/SiC interface structure. Additionally, this work outlines a methodology for characterizing the IPyC/SiC interface when considering fission product accommodation and retention in TRISO fuel design. The high-fidelity images collected with FIB-SEM tomography can be used to achieve a more in-depth interpretation of microstructural parameters and pore-shape analysis that can inform simulations and processing.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗