NASA NTRS1994

Comparison of the magnetic properties and Mossbauer analysis of glass from the Cretaceous-Tertiary boundary, Beloc, Haiti, with tektites

The magnetic properties of black Beloc glass have been measured. The Curie constant, the magnetization, and the magnetic susceptibility of the Beloc glass fall within the known ranges observed for tektites. However, the temperature-independent component of the magnetic susceptibility is slightly higher than that found for tektites. Moreover, it is not possible to match the experimental magnetic data for the Beloc glass with the calculated values using the previously reported Fe(3+)/Fe(2+) ratio of 0.7. The oxidation state of Fe was therefore redetermined by Mossbauer measurements, and the Fe(3+)/Fe(2+) ratio was found to be 0.024 plus or minus 0.015. Using the redetermined value of the ratio, the magnetic parameters were again calculated using formulas that are applicable to tektites, and good agreement was found between the calculated and experimental values. The experimental magnetic measurements and the redetermined Fe(3+)/Fe(2+) ratio of the Beloc glass specimens are essentially the same as those found for tektite glass.

Thorpe, A. N.↗
NASA NTRS1993

Magnetic properties and Moessbauer analyses of glass from the K-T boundary, Beloc, Haiti

The experimental magnetic susceptibility, the temperature-independent component of the magnetic susceptibility, the magnetization, and the Curie constant have been measured for a number of specimens of glass from the K-T boundary found at Beloc, Haiti, and the results are compared with those of similar measurements of tektites. Because the Fe(3+)/Fe(2+) ratio is needed to calculate the magnetic parameters, Moessbauer spectroscopic measurements were also made. The data were consistent with the classification of the Beloc glasses as tektites.

Senftle, F. E.↗
NASA NTRS1974

Antiferromagnetic inclusions in lunar glass

The magnetic susceptibility of eleven glass spherules from the Apollo 15, 16, and 17 fines and two specimens of a relatively large glass spherical shell were studied as a function of temperature from room temperature to liquid helium temperatures. All but one specimen showed the presence of antiferromagnetic inclusions. Closely spaced temperature measurements of the magnetic susceptibility below 77 K on five of the specimens showed antiferromagnetic temperature transitions (Neel transitions). With the exception of ilmenite in one specimen, these transitions did not correspond to any transitions in known antiferromagnetic compounds.

Thorpe, A. N.↗
NASA NTRS1972

Temperature-dependent magnetic properties of individual glass spherules, Apollo 11, 12, and 14 lunar samples.

Magnetic susceptibility of 11 glass spherules from the Apollo 14 lunar fines have been measured from room temperature to 4 K. Data taken at room temperature, 77 K, and 4.2 K, show that the soft saturation magnetization was temperature independent. In the temperature range 300 to 77 K the temperature-dependent component of the magnetic susceptibility obeys the Curie law. Susceptibility measurements on these same specimens and in addition 14 similar spherules from the Apollo 11 and 12 mission show a Curie-Weiss relation at temperatures less than 77 K with a Weiss temperature of 3-7 degrees in contrast to 2-3 degrees found for tektites and synthetic glasses of tektite composition. A proposed model and a theoretical expression closely predict the variation of the susceptibility of the glass spherules with temperature.

Thorpe, A. N.↗