Design of refractory multi-principal-element alloys for high-temperature applications

Abstract Refractory multi-principal-element alloys (RMPEAs) exhibit high specific strength at elevated temperatures ( T ). However, current RMPEAs lack a balance of room-temperature (RT) ductility, high- T strength, and high- T creep resistance. Using density-functional theory methods, we scanned composition space using four criteria: (1) formation energies for operational stability: $$-150\le {E}_{{\rm {f}}}$$ − 150 ≤ E f ≤ +70 meV per atom; (2) higher strength found via interstitial electron density with Young’s moduli E > 250 GPa; (3) inverse Pugh ratio for ductility: G / B < 0.57; and (4) high melting points: T m > 2500 °C. Using rapid bulk alloy synthesis and characterization, we validated theory and down-selected promising alloy compositions and discovered Mo 72.3 W 12.8 Ta 10.0 Ti 2.5 Zr 2.5 having well-balanced RT and high- T mechanical properties. This alloy has comparable high- T compressive strength to well-known MoNbTaW but is more ductile and more creep resistant. It is also superior to a commercial Mo-based refractory alloy and a nickel-based superalloy (Haynes-282) with improved high- T tensile strength and creep resistance.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Mechanical properties of an Al 10 Nb 20 Ta 15 Ti 30 V 5 Zr 20 A2/B2 refractory superalloy and its constituent phases

Refractory superalloys (RSAs) are a new class of high-temperature structural materials consisting of a nanometer-sized mixture of two coherent A2 (disordered BCC) and B2 (ordered) phases. While these RSAs typically exhibit superior mechanical properties at elevated temperatures, they suffer from limited plasticity at lower temperatures, often attributed to the continuous ordered B2 matrix in these two-phase alloys. To knowledgably control the microstructure and mechanical properties of these alloys, the properties of the constitutive phases in RSAs should be known. Currently this information is absent. Here, in the present work, the microstructure and mechanical properties (at 20–1200 °C) of a candidate Al 0.5 NbTa 0.8 Ti 1.5 V 0.2 Zr RSA and two single-phase alloys, which compositions correspond to the compositions of the A2 and B2 phases in the selected RSA, are reported. Interestingly, and quite unexpectedly, the intrinsic mechanical behavior of the constituent A2 and B2 phases, deciphered for the first time in the present study, revealed that they are softer and substantially more ductile than the parent two-phase RSA. Furthermore, the ordered B2 phase exhibits a deformation twinning mechanism leading to twinning induced plasticity (TWIP) coupled with a low APB energy and activity of 1/2<111> dislocations. These mechanisms are thought to be responsible for the high plasticity of the ordered B2 phase. The results presented here question the current assumption that the ordered B2 phase in these RSAs has limited plasticity and strongly indicate that the nature of the B2/A2 interface boundaries and coherency strengthening play an important role in controlling the mechanical properties of the two-phase RSA.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Effect of Re and Al additions on the microstructure and mechanical properties of Nb-18Ti-12W alloy

Microstructure and mechanical properties at 25–1200 °C of new refractory alloys, Nb-18Ti-12W (NTW), Nb-18Ti-12W-5Re (NTW-R) and Nb-18Ti-12W-5Re-1Al (NTW-RA), all compositions are in atomic percent, are reported. The alloys are developed as an alternative to a denser, more expensive and difficult-to-process refractory alloy WC-3009. After production by arc melting and hot isostatic pressing at 1400 °C, 207 MPa for 3 h, the alloys have a BCC crystal structure with the average grain size of ~150–200 μm and contain low volume fraction of (Ti,N)-rich precipitates near grain boundaries. NTW shows excellent malleability at all studied temperatures. Its yield stress at 25 °C, 1000 °C and 1200 °C is 874 MPa, 353 MPa and 202 MPa, respectively. The NTW-R and NTW-RA alloys are stronger at all the studied temperatures; however, they lack in compression ductility at 25 °C. As a result, extensive deformation twinning and formation of intergranular voids precede the fracture of these two alloys at 25 °C.

36 MATERIALS SCIENCE↗
DOE OSTI2022

High-temperature deformation mechanisms in a BCC+B2 refractory complex concentrated alloy

The current study reports the analysis of the deformation mechanisms at 600 °C in a two-phase, BCC+B2, refractory complex concentrated alloy (RCCA) Al 0.5 NbTa 0.8 Ti 1.5 V 0.2 Zr. At this temperature, the alloy microstructure is unstable and dynamic coarsening of B2 precipitates is evidenced during the mechanical testing. After true plastic strain of 0.030 at strain rate of 10 -4 s -1 , the deformation becomes highly localized in wavy bands reflecting the profusion of cross-slip. Scanning transmission electron microscopy (STEM) observations highlight the presence of paired a/2$\langle$111$\rangle$ dislocations that shear the B2 precipitates in a cooperative process. Additionally, some chemical segregation effect is observed along the narrow dislocation bands likely induced to decrease the antiphase boundary (APB) energy of the system.

ordering↗
DOE OSTI2020

Phase Inversion in a Two-phase, BCC+B2, Refractory High Entropy Alloy

A phenomenon of "phase inversion", presumably the first ever experimental evidence in metallic alloys, is shown in a refractory high entropy alloy (RHEA), Al0.5NbTa0.8Ti1.5V0.2Zr. Phase inversion in crystalline solid systems is driven by the differences in elastic modulus of the two phases. Quenching from a high-temperature single phase field, the RHEA exhibits a co-continuous mixture of a disordered BCC and an ordered B2 phase, that upon isothermal annealing at 600°C develops via spinodal decomposition into a continuous B2 matrix with discrete cuboidal BCC precipitates aligned along the <001> directions. Longer term annealing at 600°C results in the development of necking constrictions along the B2 channels, eventually pinching-off these channels and making the BCC phase continuous with discrete B2 precipitates. This inversion the process can be related to the simultaneous operation of two processes:(i) spheroidization of the initially discrete cuboidal BCC precipitates driven by a reduction in the total interface energy and (ii) an increase in the stiffness of the B2 phase, relative to the BCC phase, due to chemical composition changes during annealing, forcing the B2 regions to become discrete driven by the reduction in the total elastic strain energy.

Soni, Vishal↗