DOE OSTI2023

A Hybrid Physics-Based, Data-Driven Approach to Model Damage Accumulation in Corrosion of Polymeric Adhesives

The degradation of polymeric adhesives in dissimilar joints is a menace to electric and structural components of the automotive industry. In polymeric adhesives, failure often occurs due to damage accumulated from discrete environmental sources—thermal degradation, oxidation, hydrolysis, radiation, and moisture—that are combined with progressive damage mechanisms, such as aging and fatigue. Because most damage mechanisms that lead to degradation act in parallel, the estimation of the lifetime of a polymeric material becomes a significant reliability issue, no study currently exists that can simultaneously consider even two of these phenomena. Most current efforts are directed toward a single-phenomenon, single-model approach in which a model is developed to cover one specific damage mechanism. While this approach is advantageous in exploring single mechanisms, it is strongly inconclusive for degradation that occurs by multiple damage mechanisms. Our team plans to take a fresh perspective by designing a hybrid constitutive/data-driven approach that allows models of different damage mechanisms to be integrated into one model and then used to explore the degradation-induced failure of polymeric adhesives. The theoretical-computational part of this work is divided into four research components as described in the Approach section below.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Effect of Dual Environment Aging on Flexible Polyurethane Based Adhesive

Abstract Environmental degradation of adhesives naturally increases with the intensity of the ambient weathering agents involved. During service life, these materials are never subjected to a constant environmental loading. Real-time applications expose the material to multiple weather conditions, ranging from dry to humid or fully wet conditions. While some understanding exists about aging environments in isolation, we intend to investigate the effect of multiple environments on the constitutive behavior of the materials in question. The extent of damage can be accessed by analyzing the changes in constitutive behavior and toughness of aged material. Therefore, this aging experiment was designed around two-way aging regimes involving combinations of thermo-oxidation, hydrolytic and hygrothermal aging environments. We selected a polyurethane based flexible adhesive which is commonly used in the automotive industry as a glass sealant. The aged specimens were subjected to uniaxial tensile tests, and variation in material toughness and constitutive behavior was analyzed to ascertain the mechanics involved in the case of each environmental exposure. We outlined how different environments affect the material in isolation and how they interact with other weathering conditions. This study will help better understand and model the damage mechanics involved in exposure to multiple environmental conditions.

Shaafaey, Mamoon↗
DOE OSTI2023

Constitutive Modeling of the Cross-Linked Polymers During the Trio-Aging Mechanism: Effects of Water, Oxygen, UV

Abstract The synergized effects of diverse environmental conditions such as humidity, temperature, UV, and oxygen, are considered through a generic model by combining the concepts of network alteration, hygrothermal, and Photo-thermo oxidation Models [1–4]. Hygrothermal and Photo-oxidation are considered dual aging mechanisms which are due to the synergized effects of moisture-oxygen, and UV-oxygen, respectively at elevated temperatures. Here Trio-aging is considered as the synergized effects of Hygrothermal, and Photo-oxidation which the main environmental elements involved in polymer degradation are oxygen, water, and UV radiation where each of which has a different micro-structural impact on the polymer matrix. While oxygen imposes chain scission and cross-link formation, water, and UV radiation mainly cause chain scission. Similar to our recent models, the dual network hypothesis of Topolosky is utilized and as a result, the strain energy of the polymer matrix is written in terms of two states namely unaged and infinity. The infinity state network, itself, is decomposed into three networks, namely brittle, flexible, and dead networks. While the brittle network models the cross-link formation as sub-structural phenomena, the flexible and dead networks are utilized to represent the cross-link reduction and chain scission. The contribution of these networks in the infinity state is based on the amount of relevant environmental elements. The model is developed for a domain with plenty of oxygen and holds true for a gradual aging process that happens in super-thin samples.

Bahrololoumi, Amir↗
DOE OSTI2023

Independence of Environmental and Mechanical Damages on Silicone Adhesive Stored in a Thermo-Oxidative Environment

Abstract Elastomeric polymer materials hold a special place in today’s industrial sectors with respect to structural application needs. Low quality materials are detrimental to industries like aerospace, and automotive engineering. Assessment of the durability of elastomers for structural applications has been of much interest among the literary circles for decades and new materials keep outperforming the existing ones. Polymeric adhesives are one of the most abundantly used materials in these industries. All polymeric materials get damaged when in contact with aggressive environments in presence of high temperature and oxygen. Commonly referred to as thermo-oxidation, this environment exposes the material to heat and oxidation reactions in presence of oxygen. Resultantly, during service life, the damage to the polymer matrix is primarily caused by two factors: mechanical damage and environmental aging. Environmental aging is an irreversible phenomenon caused by changes in the molecular structure while mechanical damage maintains the shape of the polymer matrix, and the deterioration is mostly due to polymer chain mobility. Environmental aging can be caused by a single environmental agent or by a synergized impact of several environmental elements. Increasing temperature is found to be proportional to decreasing tensile strength and toughness of material. The rate and extent of degradation can be accessed by scrutinizing the changes in constitutive behavior of material through mechanical and chemical properties. Accelerated thermal aging is among the most common modes of process related degradation, leading generally to chain scission, and crosslinking phenomena and reduced resistance to fracture stress, and strain. In this experimental study, our goal is to separate the environmental degradation from mechanical damage. A silicone-based adhesive was aged in thermo-oxidative at (0%RH) aging environment. The damage and decay mechanisms have been used to draw a distinction between environmental degradation and mechanical damage. Material characterization included uniaxial tensile test (failure and cyclic) and scanning electron microscopy (SEM) tests on as-received and aged samples. Aging was conducted at three different temperatures (60°C, 80°C and 95°C) and six different exposure durations (1, 3, 10, 30, 90 and 200 days). This work confirms that environmental damage is superposed on top of the mechanical damage, and thus, they are separable. The total mechanical and environmental damage is a synergized effect of all exposure conditions and parameters involved i.e., aging time, temperature, and oxygen. The chemistry and mechanics of the polymer degradation were found to be in good agreement with each other.

Alazhary, Sharif↗
DOE OSTI2022

Experimental Characterization of Hygrothermal Aging: Competition Between Thermo-Oxidation and Hydrolysis Phenomena

Abstract In this work, we have presented a comparison between effects of accelerated thermo-oxidative, hydrolytic and hygrothermal aging on the mechanical and chemical properties of a polyurethane based (PUB) adhesive. The adhesive is a flexible adhesive which is extensively used in automobile industry as a glass sealant. During service life it gets exposed to the hygrothermal environment and the integrity of matrix interface is most vulnerable. This study focuses on weighing and comparing effects of different aging environments on material behavior; and it shows that hygrothermal aging environment results as a competition between two sub-aging phenomena i.e., thermo-oxidation and hydrolytic aging. Samples were exposed to 0%RH, 80%RH and submerged condition in distilled water. Uni-axial tensile tests, and cross-link density analysis by swelling test were carried out on as-received and aged samples. The aging process was conducted at three different temperatures (60°C, 80°C and 95°C) and for four different exposure durations of 1, 10, 30, and 90 days. This work confirms that the effect of hygrothermal aging is a result of competition between thermo-oxidation and hydrolytic aging environments. The total mechanical and environmental damage incurred by specimens is a collaborative effect of all exposure environments involved i.e., aging time, temperature, oxygen, water and humidity. The results are in agreement with the chemical test outcomes as well.

Shaafaey, Mamoon↗
DOE OSTI2022

A Micro-Mechanical Constitutive Model to Predict Hygrothermal Aging of Cross-Linked Polymers

Abstract A multi-physics material model is presented to describe the effects of temperature, oxygen, and humidity on the constitutive response of cross-linked polymers. The effect of hygrothermal damage on the mechanical integrity of the polymer matrix can be considered as the result of damage accumulation of two independent aging mechanism namely, i) thermo-oxidative, and ii) hydrolytic aging. In order to capture the mutual effects of thermo-oxidative and hydrolytic aging, an assumption has been made that each of the aging phenomenon can be superposed to each other. In fact, each of them works independently and as a result, they can compete with each other. Utilizing the theory of network decomposition, all phenomena and their correlation were modeled and thus, the strain energy function of the polymer matrix is written with respect to four independent mechanisms, i) the shrinking original matrix that has neither been attacked by water nor oxygen, ii) conversion of the first network to two new network due to the reduction and formation of cross-links, and iii) energy loss from network degradation due to attack of the water molecules to polymer active agents. Moreover, the proposed model is micro-mechanically based and is mainly relevant on thin samples due to our underlying assumption of homogeneous diffusion of oxygen and water throughout the matrix. The model has been validated against extensive data-sets obtained from experiments we specifically designed for concept validation.

Bahrololoumi, Amir↗