Composite PEMs from Electrospun Crosslinkable Poly(Phenylene Sulfonic Acid)s (Final Technical Report)
The main objective of this project is to fabricate and demonstrate superior fuel cell performance of an electrospun composite all-hydrocarbon, non-PFSA membrane. The project builds on two earlier, DOE-funded studies demonstrating high proton conductivity, even at very low humidity of crosslinkable poly(phenylenesulfonic acid), cPPSA, solution cast films, and high durability of electrospun perfluorosulfonic acid (PFSA) composite membranes. Most project milestones were fully met but the best membrane conductivity and fuel cell performance were obtained with membranes that did not contain electrospun sulfonated polyphenylene, as initially planned. Instead, an excellent performance was achieved with membranes fabricated by pore-filling, either with electrospun poly(phenyl sulfone) scaffolds or with commercial, expanded polytetrafluoroethylene scaffolds. Fuel cell testing demonstrated performance better than that of Nafion 211 or Nafion XL, particularly at lower cell humidification levels with significantly lower hydrogen crossover. No accelerated stress testing was performed, due to the initial numerous difficulties with controlling the copolymerization reaction, which took excessive amount of time to overcome. Potential scale-up of the proposed composite membrane technology can aid in boosting the fuel cell power output and simplification of the cell hydration system.