Engineering topics
Publications and source records attributed to Shang, Zhongxia.
Nanometer thick grain boundaries enable room temperature deformability in conventional brittle intermetallics.
Additive manufacturing has become an appealing technique to fabricate three-dimensional metallic materials and components for nuclear reactors. However, response of additively manufactured alloys to high-dose heavy ion irradiations at elevated temperatures is still not well understood. Here, an additively manufactured 316LN austenitic stainless steel with high-density solidification cells was irradiated using 3.5 MeV Fe ion to a peak dose of 220 dpa at 450 °C. Microscopy studies show a lower Frank loop density and smaller size in the additively manufactured sample compared with its cold worked counterpart, and the cellular structures may largely suppress the formation of perfect loops and dislocation networks and reduce the magnitude of solute segregations comparing with high angle grain boundaries. In conclusion, the present work advances the understanding on the high-temperature irradiation response of additively manufactured steels for nuclear reactor applications.
Gradient structures containing nanograins in the surface layer have been introduced into Inconel 718 (IN718) nickel-based alloy using the surface mechanical grinding treatment technique. The thermal stability of the gradient IN718 alloy was investigated. Annealing studies reveal that nanograins with a grain size smaller than 40 nm exhibited significantly better thermal stability than those with larger grain size. Transmission electron microscopy analyses reveal that the enhanced thermal stability was attributed to the formation of grain boundaries with low energy configurations. This study provides new insight on strategies to improve the thermal stability of nanocrystalline metals.
We show understanding the void evolution in irradiation environment is of great interest and significance, as irradiation-induced voids typically lead to pronounced volumetric swelling and degradation of mechanical properties. In situ studies on the irradiation response of nanovoids at elevated temperature remain limited. In this work, we performed systematic in situ 1 MeV Kr ++ irradiations on Cu with nanovoids in a transmission electron microscope up to 350 °C. The in situ studies revealed intriguing void spheroidization, shrinkage and migration. Furthermore, the morphology evolution and migration of nanovoids showed a strong dependence on irradiation temperature and initial void size. Post-irradiation analyses identified defect clusters in the form of stacking fault tetrahedrons, and the remaining large faceted nanovoids. The underlying mechanisms of irradiation-induced void spheroidization and shrinkage were discussed based on phase-field modeling.
Nanoprecipitates or grain refinement can effectively enhance the mechanical strength of Al alloys, but the room-temperature strengths of precipitation hardened and nanocrystalline Al alloys often fall below 1 GPa. Furthermore, they are largely plagued by precipitous mechanical softening at elevated temperature below 300°C, mostly due to degraded microstructural stability. Here, we report a mechanism of coupled solute effect in nanotwinned Al-Fe-Ti alloys that enables stability of nanograins up to 400°C and an unprecedented high-temperature flow stress of ~ 1.7 GPa at 300°C. The supersaturated Fe solutes in Al act as effective grain refiner, forming superstrong solid solution alloys. More importantly, empirical evidence combined with first principle calculations indicate that the Ti solutes delay the agglomeration of Fe solutes, thereby remarkably extending the temperature window for the stability of nanograins in nanotwinned Al alloys. Finally, this study highlights the opportunity to design ultrastrong and stable nanostructured alloys for potential high temperature applications via a coupled solute effect.
Metallic materials with a gradient microstructure usually exhibit excellent mechanical properties. How- ever, the radiation response of gradient structural materials is less well understood. In this work, room- temperature He ion irradiation up to ~4.5 dpa with ~10 at% He injection was performed on a gradient T91 steel processed by surface severe plastic deformation. In comparison to the coarse-grained ferritic T91, the gradient T91 with the nanocrystalline layers shows improved radiation tolerance in terms of less bubble swelling and radiation hardening. Additionally, bubble distribution along grain boundaries depends on misorientation angle suggesting a strong capacity of non-equilibrium grain boundaries in storing He atoms. The present study provides insight into the design of radiation tolerant gradient steels for nuclear industry applications.