Josephson junction parametric amplifiers are playing a crucial role in the readout chain in superconducting quantum information experiments. However, their integration with current 3D cavity implementations poses the problem of transitioning between waveguide, coax cables, and planar circuits. Moreover, Josephson amplifiers require auxiliary microwave components, like directional couplers and/or hybrids, that are sources of spurious losses and impedance mismatches that limit measurement efficiency and amplifier tunability. We have developed a wireless architecture for these parametric amplifiers that eliminates superfluous microwave components and interconnects. This greatly simplifies their assembly and integration into experiments. We present an experimental realization of such a device operating in the 9–11 GHz band with about 100 MHz of amplitude gain-bandwidth product, on par with devices mounted in conventional sample holders. The simpler impedance environment presented to the amplifier also results in increased amplifier tunability.
46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND ↗
Interdiffusion and intrinsic diffusion in the NiAl /delta/ phase of the Al-Ni system
Interdiffusion coefficients at 950 to 1150 C and the ratio of intrinsic diffusion coefficients at 1100 C were measured as functions of composition in the NiAl (delta) phase of the Al-Ni system, using a vapor-solid technique. Diffusivity values were also obtained for the Ni3Al (epsilon) and Ni (Al) solid solution (zeta) phases from 950 to 1150 C. The interdiffusion coefficient in NiAl (delta) varies several orders of magnitude over the delta phase field with a deep minimum in the diffusivity-composition curve at 48 to 49 at% Al. The ratio of intrinsic diffusion coefficients DNi/DAl, in the delta phase also varies with composition from a value of 3 to 3.5 below 50 at% Al to 0.1 or less above 50 at% Al.
Shankar, S.↗
Thermodynamics and kinetics of reactions in protective coating systems
A study of the aluminization of Ni from packs containing various percentages of unalloyed Al confirmed that the surface aluminum content of specimens aluminized tends to decrease with time and consequently a simple parabolic law for the weight-gain vs. time relationship is not obeyed. The diffusivity-composition relationship in NiAl was examined, and a set of curves is presented. A numerical method for the calculation of coating dissolution rates was developed and applied to NiAl-Ni3Al type of coatings.