Effect of material composition of diamond field emission array cathodes on quality of transversely shaped beams

Diamond field emitter array field emission cathodes (DFEA FECs) are attractive for the next generation of injectors due to their ability to produce transversely shaped beams without the need for complex masking or laser schemes. However, reliability of this cathode technology remains a challenging issue as principal mechanisms guiding and allowing for output beam shaping remained poorly understood. Here, this paper reports the results of testing two DFEA FECs with the same pattern and emitter tip geometry. Although both cathodes were able to sustain gradients of 44 MV/m and produce maximum output integral charge of 0.5 nC per radio frequency pulse, their emission patterns were different. One cathode did not produce a shaped beam, while the other one did. This difference was explained by the extent of the local variations of the diamond material across the arrays as discovered by spatially resolved Raman spectroscopy. The main practical takeaways were (i) tip sharpness was not a prerequisite for producing a shaped beam and instead (ii) material characteristics resulting in different cathode ballast resistance affected emission spatial uniformity across the array and hence the beam shaping.

36 MATERIALS SCIENCE↗
DOE OSTI2021

An X-Band Ultra-High Gradient Photoinjector

High brightness beams appealing for XFELs and UEM essentially imply a high current and a low emittance. To obtain such beams we propose to raise the accelerating voltage in the gun mitigating repealing Coulomb forces. An ultra-high gradient is achieved utilizing a short-pulse technology. We have designed a room temperature X-band 1,5 cell gun that is able to inject 4 MeV, 100 pC bunches with as low as 0.15 mcm normalized transverse emittance. The gun is operated with as high gradients as 400 MV/m and fed by 200 MW, 10 ns RF pulses generated with Argonne Wakefield Accelerator (AWA) power extractor. We report results of low RF power tests, laser alignment test results, and successful gun conditioning results carried out at nominal RF power.

43 PARTICLE ACCELERATORS↗
DOE OSTI2021

FEbeam: Cavity and electron emission data conversion, processing, and analysis. A freeware toolkit for rf injectors

FEbeam is an all-in-one field emission data processing interface with the capability to analyze the field emission cathode performance in an rf injector by extracting the field enhancement factor, local field, and effective emission area from the Fowler–Nordheim equations. It also has the capability of processing beam imaging micrographs using its sister software, FEpic. Furthermore, the current version of FEbeam was designed for the Argonne Cathode Test-stand of the Argonne Wakefield Accelerator facility switch yard. With slight modifications, FEbeam could work for many rf field emission injectors. This software is open-source and can be found at GitHub.

43 PARTICLE ACCELERATORS↗
DOE OSTI2020

Demonstration of nitrogen-incorporated ultrananocrystalline diamond photocathodes in a RF gun environment

Quantum efficiency (QE), intrinsic emittance, and robustness are the three most important figures of merit for photocathodes, the first two determine the ultimate achievable brightness of an electron beam, and the third one directly correlates with the complications of a beamline design. Nitrogen-incorporated ultrananocrystalline diamond [(N)UNCD] materials are promising candidates for photocathode applications due to their remarkable electron emission performance as well as the moderate vacuum requirement. Two (N)UNCD photocathodes have been characterized in a realistic RF gun environment with the nicely balanced performance of all three figures of merit. In this work, the QE of the first (N)UNCD cathode (stored in air for two years before the test) was found to be 3.8 x 10 –4 using a 262 nm UV laser and a cathode surface field of 30MV/m. It was found that the QE of the second (N)UNCD sample (grown days before the test) was nearly the same and, therefore, demonstrates the exceptional environmental tolerance of the material. The intrinsic emittance of (N)UNCD was measured to be 1.00 μm/mm.

36 MATERIALS SCIENCE↗