Enhanced Oxygen Reduction Performance on {101} CoMn 2 O 4 Spinel Facets

Here, we present a facile colloidal synthesis method for producing {101}-facet-tailored CoMn 2 O 4 spinel nano-octahedra with uniform size (9 nm). These nano-octahedra exhibit superior electrocatalytic activity for the oxygen reduction reaction (ORR) in alkaline media compared to their spherical counterparts and previously reported spinel electrocatalysts. At 0.85 V, they achieve a high mass activity (MA) of 60.0 A/g, surpassing the spherical counterparts (38.6 A/g). Furthermore, the CoMn 2 O 4 nano-octahedra demonstrate excellent stability, maintaining an MA of 47.2 A/g after 10,000 durability cycles. This work highlights a promising approach for synthesizing advanced spinel nano-oxides with controlled crystal facets, offering potential as non-precious metal ORR electrocatalysts. The exposed active catalyst surfaces and well-defined structures contribute to their enhanced ORR performance.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Improving Oxygen Reduction Performance of Surface-Layer-Controlled Pt–Ni Nano-Octahedra via Gaseous Etching

This study demonstrates an atomic composition manipulation on Pt–Ni nano-octahedra to enhance their electrocatalytic performance. By selectively extracting Ni atoms from the {111} facets of the Pt–Ni nano-octahedra using gaseous carbon monoxide at an elevated temperature, a Pt-rich shell is formed, resulting in an ~2 atomic layer Pt-skin. The surface-engineered octahedral nanocatalyst exhibits a significant enhancement in both mass activity (~1.8-fold) and specific activity (~2.2-fold) toward the oxygen reduction reaction compared with its unmodified counterpart. After 20,000 potential cycles of durability tests, the surface-etched Pt–Ni nano-octahedral sample shows a mass activity of 1.50 A/mg Pt , exceeding the initial mass activity of the unetched counterpart (1.40 A/mg Pt ) and outperforming the benchmark Pt/C (0.18 A/mg Pt ) by a factor of 8. DFT calculations predict this improvement with the Pt surface layers and support these experimental observations. Therefore, this surface-engineering protocol provides a promising strategy for developing novel electrocatalysts with improved catalytic features.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Synthesis of Core@Shell Cu-Ni@Pt-Cu Nano-Octahedra and Their Improved MOR Activity

Fabrication of 3d metal-based core@shell nanocatalysts with engineered Pt-surfaces provides an effective approach for improving the catalytic performance. The challenges in such preparation include shape control of the 3d metallic cores and thickness control of the Pt-based shells. Herein, we report a colloidal seed-mediated method to prepare octahedral CuNi@Pt-Cu core@shell nanocrystals using CuNi octahedral cores as the template. By precisely controlling the synthesis conditions including the deposition rate and diffusion rate of the shell-formation through tuning the capping ligand, reaction temperature, and heating rate, uniform Pt-based shells can be achieved with a thickness of < 1 nm. Furthermore, the resultant carbon-supported CuNi@Pt-Cu core@shell nano-octahedra showed superior activity in electrochemical methanol oxidation reaction (MOR) compared with the commercial Pt/C catalysts and carbon-supported CuNi@Pt-Cu nano-polyhedron counterparts, demonstrating that both the lattice strain and shape effects arising from the as-prepared CuNi@Pt-Cu octahedral nanocatalysts play a crucial role in MOR performance.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Alloying–realloying enabled high durability for Pt–Pd-3d-transition metal nanoparticle fuel cell catalysts

Abstract Alloying noble metals with non-noble metals enables high activity while reducing the cost of electrocatalysts in fuel cells. However, under fuel cell operating conditions, state-of-the-art oxygen reduction reaction alloy catalysts either feature high atomic percentages of noble metals (>70%) with limited durability or show poor durability when lower percentages of noble metals (<50%) are used. Here, we demonstrate a highly-durable alloy catalyst derived by alloying PtPd (<50%) with 3d-transition metals (Cu, Ni or Co) in ternary compositions. The origin of the high durability is probed by in-situ/operando high-energy synchrotron X-ray diffraction coupled with pair distribution function analysis of atomic phase structures and strains, revealing an important role of realloying in the compressively-strained single-phase alloy state despite the occurrence of dealloying. The implication of the finding, a striking departure from previous perceptions of phase-segregated noble metal skin or complete dealloying of non-noble metals, is the fulfilling of the promise of alloy catalysts for mass commercialization of fuel cells.