Sharon, John | Search NASA

DOE OSTI2023

Computationally-Guided ODS Refractory HEAs via Additive Manufacturing

This document is the final report for ARPA-E ULTIMATE project DE-AR0001422. To achieve higher efficiency turbine operation, the RTX Technology Research Center (RTRC) explored the use of additive manufacturing (AM) to produce test specimens of novel high entropy alloys (HEA) enhanced with oxide dispersion strengthening (ODS). HEAs, with multiple principal elements, offer a vast alloy design space rich with unique properties especially enhanced solid solution strengthening. ODS alloys historically are some of the best performing materials for high temperature applications. Leveraging AM enables near net shape part production and incorporation of ODS into the alloy. Density, melting temperature, and elevated temperature strength properties of several novel HEA compositions were found to meet or exceed program targets; however, obtaining sufficient room temperature ductility in these alloys proved challenging. In order to obtain an alloy with sufficient ductility, the team explored more conventional refractory alloy compositions, focusing on a niobium based alloy. This inherently ductile alloy also satisfied program metrics for cost, density, and fracture toughness. Results showed the oxide dispersions increased high temperature strength, and improved creep resistance compared to the conventional alloy, though the program creep metric was not met. Further tuning of the alloy chemistry, and optimization of the oxide dispersion, is likely required to improve creep resistance.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Computational Tools for Additive Manufacture of Tailored Microstructure and Properties

Additive manufacturing has the potential to revolutionize industrial hardware and unlock efficiency gains through the fabrication of geometries and architectures not possible by conventional processing. Currently most additive builds use a single set of process parameters (e.g. laser power and scan speed) which results in a part with a homogenous microstructure that provides a singular performance level. To move beyond this state, Raytheon Technologies Research Center worked to create a set of computational tools to track material evolution through each step of the additive process. Computational fluid dynamics and phase field models for microstructure evolution as a function of processing parameters, and crystal plasticity models fully coupling microstructure and mechanical properties for performance predictions were leveraged to establish a connection between additive parameters and the final microstructure. This framework was utilized to tailor spatially-varying mechanical properties in a part by appropriately controlling the microstructure evolution during the additive process. Specifically, a turbine blade was 3D printed from nickel superalloy IN718 using laser powder bed fusion with coarse grains in the airfoil section which experiences the highest temperatures and is creep limited while finer grains were printed in the root of the blade which experience higher stresses but at lower temperatures and is therefore fatigue limited. The benefit of being able to intentionally insert coarse grains in the high temperature region of the blade was showcased with a microstructure sensitive creep model that indicates longer creep life for coarser grains.

20 FOSSIL-FUELED POWER PLANTS↗