Structural Changes during the Conversion Reaction of Tungsten Oxide Electrodes with Tailored, Mesoscale Porosity
In-plane tungsten oxide nanostructures, including hexagonally patterned cylinders and holes in a matrix, were fabricated via sequential infiltration synthesis (SIS) on self-assembled block copolymer templates. Using the tailored morphology and porosity of these model electrodes with in situ grazing incidence small angle X-ray scattering, the intrinsic structural change of nanoscale active materials during the conversion reaction of WO 3 + 6Li ↔ W + 3 Li 2 O was investigated at controlled electrochemical conditions. Reversible electrode volume expansion and contraction was observed during lithiation and delithiation cycles, respectively. The potential where electrode’s thickness expansion started was ~1.6 V, which is close to thermodynamically expected one for conversion reaction of WO 3 with lithium (1.65 V). The temporal evolution of the electrode volume at constant electrode potentials revealed high overpotential for bulk lithiation and slow conversion reaction kinetics, despite the tailored porosity of the SIS electrodes. Oxide cylinders showed smaller overall electrode thickness change, likely due to unconstrained lateral volume change, as compared to a matrix with holes. On the other hand, better connectivity and guided volume change of the latter electrode morphology provided improved cycling stability. Additionally, heterogeneity in an electrode, from internal pores and density gradients, was found to aggravate the fragmentation of the electrode during conversion reaction. Insights into oxide conversion reaction kinetics and the relationship between electrode mesostructure and cycling behavior obtained from this study can help guide the more rational design of conversion electrode for high performing batteries.