Preparation and Characterization of YBa 2 Cu 4 O 8 Superconductor
Solid-state reaction of appropriate amounts of Y 2 O 3 , BaCOs, and CuO for 2 h at 800°C in flowing oxygen with a total pressure of 2.7 x 10 2 Pa (2 mm Hg), followed by cooling and annealing at 750°C for 10 h in oxygen at ambient pressure, has produced orthorhombic YBa 2 Cu 4 O 8 (124) as the main phase with YBa 2 Cu 3 O x (123) as an impurity phase. After the as-calcined powder was annealed in oxygen at 800°C for 24 h under ambient pressure, the phase purity improved considerably. Calcined 124 powder was pressed into pellets and rapidly annealed at temperatures from 870°C to 935°C. At these temperatures, the 124 decomposed into 123. The superconducting transition temperature, T c , of the annealed samples depended upon the annealing temperature and atmosphere. The decomposed samples have been characterized by low field RF SQUID magnetometer and high resolution transmission electron microscopy.