Study of fatigue durability of advanced composite materials under conditions of accelerated loading

The effect of temperature on the tension-tension fatigue life of the T300/5208 graphite/epoxy angle-ply laminate system was investigated in an effort to develop an acceptable and reliable method of accelerated loading. Typical S log sub 10 N curves were determined experimentally at 25 C, 75 C, and 115 C. The time-temperature superposition principle was employed to find the shift factors of uniaxial fatigue strength, and a general linear equation of S log sub 10 N for shifting purpose was established. The combined techniques of cyclic creep measurements and optical microscopy upon fatigue failure allow some assessment of the possible physical basis of S log 10 N curve shifting. Before fatigue, the laminates at all test temperatures and stress levels undergo a unique damage mechanism during fatigue loading. It is concluded that an accelerated loading method is feasible.

Shih, H. M.↗

NASA NTRS1977

Inclusions, grain boundaries and hydrogen attack

Optical metallography, scanning electron microscopy, and X-ray spectrometry were used to study the roles of grain boundaries and inclusions in the nucleation process and fissure growth during the rapid stage of hydrogen attack on 1020 steel in the annealed condition at temperatures up to 600 C and a hydrogen pressure of 10.3 MN/sq m. It is found that intergranular fracture occurred when specimens were fractured at 77 K after hydrogen exposure and that macroscopically observable fissures formed due to the coalescence of bubbles which nucleated at inclusions in grain boundaries. The inclusions are tentatively identified as MnS.

Shih, H. M.↗