STUDIES ON PIPELINE POLYETHYLENES IN HYDROGEN GAS ENVIRONMENTS USING IN-SITU AND EX-SITU CHARACTERIZATION METHODS

Polymeric materials are commonplace in the natural gas infrastructure as distribution pipes, coatings, seals, and gaskets. Under the auspices of the U.S. Department of Energy HyBlend program, one of the means to reduce greenhouse gas emissions is with replacing natural gas, either partially or completely, with hydrogen. This approach makes it imperative that we conduct near-term and long-term materials compatibility research in these relevant environments. Insights into the effects of hydrogen and hydrogen gas blends on polymer integrity can be gained through both ex-situ and in-situ analytical methods. Our work represented here highlights a study of the behavior of pipeline polyethylene (PE) materials, including HDPE (Dow 2490 and GDB50) and MDPE (Ineos and legacy Dupont Aldyl A), when exposed to hydrogen by means of in-situ X-ray scattering and ex-situ Raman spectroscopy techniques. Samples were tested in ex-situ hydrogen and argon gas environments and in-situ hydrogen environments to identify differences due to permeation and solubility of these gases. These methods complemented each other because Raman spectroscopy could capture permanent effects after materials were removed from gaseous environments, and in-situ X-ray scattering analysis collected real-time data to elucidate the impact of the gas environment on polymer microstructure. Data collected revealed that the aforementioned polymers did not show significant changes in crystallinity and microstructure under the exposure conditions tested. Our findings from these studies will help establish real-time effects caused by hydrogen gas transport through pipeline polyethylenes by way of its influence on polymer structure and chemistry, which is directly related to pipeline mechanical strength and longevity of service.

Hydrogen materials compatibility, Natural gas pipe↗
DOE OSTI2024

In-Situ and Ex-Situ Studies on the Morphology Changes of Polymer Pipeline Materials for Use in Hydrogen Gas Environments

The US natural gas infrastructure is a national asset that could be used to deliver hydrogen and hydrogen blends of natural gas as a pathway to reduce carbon emissions. The distribution system comprises nearly 50% plastic pipe composed of medium- and high-density polyethylene materials (MDPE and HDPE). While these materials perform adequately for natural gas, research on their hydrogen compatibility is essential to understand if any immediate and long-term risks are associated with hydrogen addition. The Blended Gas CRADA, a HyBlend project, has established a comprehensive test method for evaluating MDPE and HDPE of various plastic resin compositions of pipeline material in pure hydrogen and 20% hydrogen/80% methane blends. Both in-situ and ex-situ measurements were performed to capture hydrogen-induced changes in the polyethylene material's crystalline, amorphous and their interphase regions. We investigated MDPE and HDPE pipeline materials made from different polymer resin systems to evaluate the effects of hydrogen gas. The materials were characterized by their density, diffusion coefficient, free volume ratio, and degree of crystallinity. Various advanced characterization methods, including in situ NMR, ex situ XRD, ex situ DSC, and ex situ TDA, were used to analyze the effects of changes in crystalline, amorphous, and interphase regions due to gas exposure. Time-dependent post-decompression quasi-static tensile tests were conducted to explore the effects of gas exposure time on the mechanical behavior of the pipe materials. This work will highlight the time sensitivities during and after gas exposure. The correlation between gas-induced polyethylene morphology changes and the associated material performance will be addressed for the intended applications. These studies will show that polyethylene resin composition and material exposure are important factors when considering whether hydrogen gas affects pipeline materials positively or negatively.

Simmons, Kevin L.↗
DOE OSTI2024

Investigating In-Situ Fracture Behaviors of Polymer Pipeline Materials in Hydrogen and Hydrogen-Methane Blended Gas Environments

To reduce carbon emissions, the US natural gas infrastructure is seen as a primary solution for efficiently transporting hydrogen gas. Blending hydrogen gas with natural gas and transporting it across a national infrastructure could save significant infrastructure costs. To properly operate the infrastructure under the new gas system, it is critical to understand material compatibility with hydrogen under various conditions. The Blended Gas CRADA, a Hyblend project, is established to determine the material compatibility of existing natural gas pipes with hydrogen gas. In this study, we investigate the in-plane fracture behaviors of MDPEMarlex and HDPEGDB exposed to hydrogen and hydrogen-methane blended gas. Single-edge notch bending geometry is used. All tests are executed in-situ with the gas environment. The experimental results show a significant effect of the gas environment on HDPEGDB specimens, reducing 5% (H2) to 42% (Blended gas) of specific fracture energy compared to non-aged specimens. For the MDPEMarlex, the effects of the gas environment have increased the specific fracture energy by 10% (H2) to 15% (Blended gas). Fracture surfaces of the tested samples are observed using an electronic microscope. The in-plane fracture surface of HDPEGDB shows a pronounced dimple fracture pattern after exposure to hydrogen and blended gas. The expanded fracture pattern contributes to lower the specific fracture energy. These observations provide critical information for validating polymer pipeline materials when interact with hydrogen and hydrogen-blend gas.

Ko, Seunghyun↗
DOE OSTI2024

Polymer-fiber-reinforced polymers with enhanced interfacial bonding between polypropylene fiber and polyethylene matrix

Self-reinforced composites (SRCs) consist of reinforcing fibers and a base matrix made of the same thermoplastic polymer, offering lightweight, recyclability, and sustainability benefits. However, limited research exists on composites where the reinforcing thermoplastic polymer fibers differ from the base thermoplastic matrix. Here, this study focuses on investigating the mechanical behavior of such composites and exploring different surface modification methods to enhance the fiber/matrix interfacial bonding using polypropylene fibers and a polyethylene matrix as an example. It is shown that surface treatment with a commercial adhesion promoter containing n-butyl acetate significantly improves the interfacial shear strength between polypropylene fibers and the polyethylene matrix, increasing it by 145% compared to other methods investigated. Additionally, increasing the length of the embedded polymer fiber in the matrix leads to a notable increase in specific interfacial energy. Consequently, the thermoplastic polymer-fiber-reinforced polymers (PFRPs) using surface-treated woven polypropylene fabrics and a polyethylene matrix exhibit a 20% higher tensile strength and a 65% higher toughness compared to non-treated PFRPs. This study also shows that specific mechanical properties (normalized by the composite density) of the investigated woven PFRPs are similar to those of non-treated SRCs under uni-axial tension. Particularly, their ductility outperforms carbon-/glass-/aramid-fiber-reinforced polymers by at least 6 times at a same fiber volume fraction. The investigation of such composites and the exploration of surface modification methods present important progress in the field of thermoplastic PFRPs, which serve as a solution for addressing concerns related to recyclability and sustainability.

Fiber pull-out↗
DOE OSTI2024

Equivalent Properties of Interfacial Void Defects at the CFRTP-adhesive Interface and Their Detrimental Effects on the Bonding Performance of Metal-CFRTP Dissimilar Joints

This paper revealed the detrimental effects of micro-scale air interfacial voids on the debonding at the interface of carbon-fiber-reinforced polyphthalamide (CFRPPA) and thermoset adhesive, representing a weak adherend-adhesive interface, within a dissimilar joint made of an aluminum alloy and a CFRPPA. The reduced lap shear strength of the joint, due to different void area fractions at the CFRPPA-adhesive interface, can be computationally described by using equivalent interfacial properties in the modeling to avoid the explicit modeling of the micro-scale interfacial voids. Such equivalent interfacial properties (e.g., interfacial normal strength, etc.) was found to have a non-linear relationship with respect to interfacial void area fraction as well as lap shear strength. This work has practical applications by utilizing equivalent interfacial properties for the analytical and/or computational design(s) of adhesively bonded joints.

Qiao, Yao↗
DOE OSTI2024

Exploring Failure of Adhesively-Bonded Joints with Different Void Sizes at the Same Void Volume Fraction through A Micro-scale Numerical Modeling

This paper studied the effects of void sizes on the failure behavior of adhesively-bonded materials under global shear via micro-scale computational modeling. The numerical results indicate that large void sizes with increased distances between them at the same void volume fraction can alleviate the reduced joint strength of a weaker adherend-adhesive interface caused by interfacial voids. However, this is not the case for an adherend-adhesive interface with the interfacial tensile strength being sufficiently higher than the adhesive strength, showing the negligible effect on the joint strength due to various void sizes and the amount of interfacial voids. This preliminary investigation provides insightful information for scaling up the void size in the macro-scale computational modeling of joints, and enhances the understanding of the micro-mechanical adhesion in adherend-adhesive interfaces with different levels of bonding.

Qiao, Yao↗
DOE OSTI2024

Acrylonitrile-butadiene-lignin thermoplastic rubber adhesive for enhanced metal-to-metal joining

With the growing requirement for lightweight structural materials in automotive, aerospace, and infrastructure applications, multi-material joints made with adhesive have attracted intense research interest. Commercial thermoset adhesives are one-time cures, and difficult to disassemble the bonded components for repair and recycling. Our prior work with a thermoplastic acrylonitrile-butadiene-lignin rubber (ABL) addresses this sustainability/recycling challenge, but the adhesive exhibits deficient joining strength compared to standard thermosets. Here, we modify the ABL matrix by loading particulate fillers to enhance its modulus and toughness. Further, the goal is to manufacture a cure-free thermoplastic adhesive system with a simple dispensing protocol and characteristic ductility combined with a high yield stress for improved shear strength of a bonded joint. Fumed silica (FS) and epoxidized glass spheres (EGS) were used as fillers in the ABL to promote the dispersion of lignin particles that tailored the functionalities and free energy components of the adhesive surface. With optimal loading of FS (5 wt%) and EGS (30 wt%) in the ABL adhesive matrix, the lap-shear strength of the bonded aluminum joint was elevated by 128%, compared to the neat ABL, reaching 21 MPa, which is 90% of the performance of a commercial epoxy-based adhesive.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Phase field modeling of hydrogen release in nitrile-butadiene rubber composites after high-pressure hydrogen exposure

Experimental data showed that a simple diffusion model doesn’t suffice to explain the hydrogen (H 2 ) release kinetics in nitrile butadiene rubber (NBR) composites (one with no filler or plasticizer, one with plasticizer only, one with fillers and plasticizer, and one with fillers only) after exposed to hydrogen gas at a pressure of 27.6 MPa. In this work, we developed a phase field model that considers the effect of H 2 gas bubble evolution on H 2 release kinetics. With the model, we simulated the effect of thermodynamic and kinetics properties on the nucleation, growth, and shrinkage of gas bubbles and H 2 release kinetics during and after decompression. Here, the results demonstrated that 1) the model built upon certain thermodynamic and kinetics properties of a given material can well describe its H 2 release kinetics measured in experiments, and 2) the model can predict the gas bubble evolution, which is associated with the material property degradation and failures, with accurate thermodynamic and kinetics properties or H 2 release data from experiments.

08 HYDROGEN↗
DOE OSTI2023

Plasma treatment on both adhesive tape and adherends for significantly enhanced CFRTP-related adhesive joints

Unlike existing literature that primarily concentrates on either the plasma treatment of adherends alone or solely on adhesive surfaces, this work leverages plasma modification of both adhesive in tape form and adherend surfaces to largely enhance the interfacial bonding between a thermoset-based adhesive tape and carbon-fiber-reinforced thermoplastic polymer (CFRTP) for structural bonding applications. Here, by conducting single lap shear tests on adhesively-bonded AA6061-CFRPPA (carbon-fiber-reinforced polyphthalamide) dissimilar joints, it is shown that the plasma treatment of adherends alone can increase the lap shear strength (LSS) of the joints by approximately 200% compared to non-treated counterparts. An additional plasma treatment of adhesive tape surfaces leads to even higher LSS improvement, reaching up to 315%, due to the formation of a denser crosslinked network of covalent bonds and a reduced area fraction of interfacial voids at the CFRPPA/adhesive interface. The highest plasma-enhanced LSS of the metal-CFRTP dissimilar joints rivals that of metal-metal joints, which is typically stronger than the joints associated with fiber-reinforced polymers. This study is important for achieving strong CFRTP-related structural components bonded using adhesive tape, providing better compatibility with plasma treatment and other joining methods like riveting compared to adhesive paste or liquid.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Network stability of FKM rubber compounds under hydrogen pressure

Fluorocarbon-based rubber (FKM) compounds are typically utilized in the aeronautical industry due to its exceptional chemical and thermal resistance and recently has drawn significant interest from the hydrogen community for various hydrogen applications, but there exists little data evaluating its hydrogen compatibility. In this paper, a formulated FKM compound was exposed to ultrahigh hydrogen pressure (90 MPa) and analyzed by attenuated total reflectance Fourier-transform infrared (ATR-FTIR) spectroscopy and crosslinking densities by solvent swelling measurement. ATR-FTIR spectroscopic data demonstrated that high-pressure hydrogen not only caused cleavages in polymer backbone and cross linkages, but also induced additional degradation of FKM compounds by breaking intermolecular hydrogen bonding between carboxylic acids, which were produced during rubber molding and post curing processes. This hydrogen pressure-driven degradation was significantly higher towards the core of the material than at the surface due to its weaker bonding between polymers and fillers.

Polymers, hydrogen, stability, degradation, Charac↗
DOE OSTI2023

A Micro-scale Numerical Investigation of Internal and Interfacial Void Defects in Adhesive on Failure Behavior of Adhesively-Bonded Materials with Rough Surfaces

This paper studied the effects of air void defects on the failure behavior of adhesively-bonded materials under global shear via micro-scale computational modeling. The numerical results indicated that interfacial void defects can largely facilitate interfacial debonding of a weaker adherend/adhesive interface under shear. However, this is not the case for a stronger adherend/adhesive interface, showing the reduction on the nominal shear strength of an adhesive joint is mainly due to internal void defects. The reduced bonding performance due to voids can be improved by leveraging an appropriate surface roughness. This preliminary investigation is a first step to better understand the micro-mechanics of interfacial failure in the adhesion of a roughened/patterned adherend via surface modification(s) and an adhesive, and also shows the importance of minimizing interfacial void defects in particular at a weaker adherend/adhesive interface via different techniques.

Qiao, Yao↗
DOE OSTI2023

A study of adhesive bonding in metal–metal, metal–CFRP, and CFRP–CFRP material combinations under shear deformation: Fracture morphologies and damage mechanisms

Safe design of adhesive joining in multi-materials in engineered structures requires the accumulation of numerous experimental data on the failure behavior of various adhesively-bonded material combinations under different loading conditions. The deep understanding of mechanical performance, fracturing morphologies, and main damage mechanisms is also quintessential for accelerating the development of proper physics-based and multi-scale models for assisting the design. Towards this goal, this work presents a comprehensive characterization of the failure behavior of adhesively-bonded metal–metal, metal–CFRP, and CFRP–CFRP material combinations under global shear deformation via single lap shear testing. Thanks to a synergistic combination of measurement methods by using Digital Imaging Correlation (DIC) and 3D optical profilometry, adhesive features on the adherend after failure were quantified and the main progressive damage mechanisms were identified. The characterization performed in this work provides quantitative data that contributes to a better understanding of shear failure in adhesive bonding across different bi-material combinations. Finally, the obtained results have practical implications, including the potential to enhance adhesive bonding design, identify failure causes in adhesive joints, and develop or validate computational models capable of capturing the observed behavior in various adhesively-bonded materials under global shear deformation.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Interfacial bond characterization of epoxy adhesives to aluminum alloy and carbon fiber-reinforced polyamide by vibrational spectroscopy

Vibrational spectroscopic technique has been utilized to investigate interfacial bonding chemistry of two epoxy adhesive products, XP0012 and XP5005F, on plasma-treated AA6061 and carbon fiber-reinforced polyamide 66 (CFRP-PA66) surfaces. The change in vibrational peak ratios was measured by attenuated total reflectance-Fourier transform infrared (ATR-FTIR) spectroscopy to deduce bonding mechanisms. Both adhesives showed strong crosslinking polymerization of hydroxyl- and amine-initiated epoxy ring opening on AA6061 surface, but on CFRP surface XP0012 formed a simple amide linkage by the reaction of surface hydroxyl groups and nitrile groups of curing agent, and XP5005F formed a crosslinked network by hydroxyl-initiated epoxy ring opening polymerization. The different interfacial bonding formation of two adhesives on CFRP-PA66 surface is attributed to additive effect. Addition of additives to epoxy adhesives (XP5005F) changed the interfacial bonding mechanism on CFRP-PA66 surface, rather forming hydroxyl-initiated epoxy opening crosslinking polymerization than a simple amide bond formation (XP0012). The interfacial bonding chemistry was also proved by addition of bisphenol A (BA) to a simplified model diglycidyl ether of bisphenol A/dicyandiamide (DGEBA/DICY) epoxy system. When BA was added to the model DGEBA/DICY system, epoxy ring gradually decreased on CFRP-PA66 surface, while without BA, DGEBA/DICY showed only decrease in a nitrile peak intensity in ATR-FTIR. In conclusion, the foregoing different types of interfacial chemical bonds at the adhesive/CFRP-PA66 interfaces can affect the lap shear behavior of the joint.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Investigation of desorption of hydrogen gas from polymer matrix using thermal desorption analysis and finite element modeling

Polymer materials are used widely as sealing materials and liners in hydrogen storage and transportation infrastructure. During operating conditions, polymers are exposed to high pressure hydrogen gas periodically. When in contact, the hydrogen gas diffuses through the polymer material with ease due to its smaller sized molecules compared to the polymer molecules. In the event of rapid decompression of outside hydrogen gas, the hydrogen molecules within the polymer diffuse out. This process is known as the desorption of polymer and can cause blisters or cracking causing permanent damage to the polymer. Here, we used a combined experimental and modeling approach to investigate the desorption of the hydrogen gas in the polymer. Thermal desorption analysis (TDA) experiments were performed on the polymer sample exposed to the high-pressure hydrogen gas to measure the diffusion coefficient and equilibrium hydrogen concentration. Experiments also provided the quantity of hydrogen within the polymer during the desorption process which followed Fick’s law. However, for higher pressurization values, some anomaly was observed in the quantity of hydrogen remaining in the polymer sample. A continuum mechanics based coupled diffusion–deformation-damage model was deployed to simulate the gas desorption process in the material using the finite element method to understand its effect on the material. It was found that the anomaly in TDA results were due to the blister formation on the polymer surface which resulted in longer hydrogen retention. Simulations also showed that blister formation can be affected by multiple parameters such as the addition of filler particles, and pre-existing cavity size.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Resolving protein-mineral interfacial interactions during in vitro mineralization by atom probe tomography

Organic macromolecules exert remarkable control over the nucleation and growth of inorganic crystallites during (bio)mineralization, as exemplified during enamel formation where the protein amelogenin regulates the formation of hydroxyapatite (HAP). However, it is poorly understood how fundamental processes at the organic-inorganic interface, such as protein adsorption and/or incorporation into minerals, regulates nucleation and crystal growth due to technical challenges in observing and characterizing mineral-bound organics at high-resolution. Here, atom probe tomography techniques were developed and applied to characterize amelogenin-mineralized HAP particles in vitro, revealing distinct organic-inorganic interfacial structures and processes at the nanoscale. Specifically, visualization of amelogenin across the mineralized particulate demonstrates protein can become entrapped during HAP crystal aggregation and fusion. Identification of protein signatures and structural interpretations were further supported by standards analyses, i.e., defined HAP surfaces with and without amelogenin adsorbed. These findings represent a significant advance in the characterization of interfacial structures and, more so, interpretation of fundamental organic-inorganic processes and mechanisms influencing crystal growth. Ultimately, this approach can be broadly applied to inform how potentially unique and diverse organic-inorganic interactions at different stages regulates the growth and evolution of various biominerals.

36 MATERIALS SCIENCE↗
DOE OSTI2023

A renewable lignin-based thermoplastic adhesive for steel joining

Adhesive bonding of metals has become increasingly relevant in recent years due to the demand for reducing weight and improving performance in structural applications such as automobiles and aerospace. We developed renewable thermoplastic adhesives from technical organosolv lignin isolated from hardwood biomass and acrylonitrile butadiene co-polymer rubber (NBR) for joining steel substrates. NBR33, NBR41 and NBR51 with acrylonitrile molar ratios of 33, 41 and 51%, respectively, were blended with lignin to form two-phase thermoplastic adhesives, and their adhesion, viscoelastic and surface properties were measured. Lignin content in the compositions were varied, ranging from 40% to 80% (w/w), to alter toughness, stiffness, and surface energy characteristics of the material. Better interaction or reactivity between the lignin and NBR phases was observed with greater nitrile content in NBR, leading to greater modulus and stiffness of the adhesive. Simultaneously, increasing the proportion of lignin reduced toughness and improved stiffness, with the highest adhesive strength of 13.1 MPa measured in a 60% lignin loading ratio with NBR51. Surface energy measurements revealed that total surface energy (sum of polar and dispersive surface energy) raised with lignin loading, suggesting that both surface energy and matrix strength play a critical role in the adhesive properties of the synthesized materials. A finite element-based cohesive zone model (CZM) was developed and implemented to study the failure strength of the adhesively bonded joint. Here, this study demonstrates the viability of lignin as a valuable building block for adhesives, not only due to its inherent chemical structure and rigidity, but also for its surface energy characteristics.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Plasma surface modification coupled with thermal and step-over distance effects on significant fracture improvement of adhesively-bonded metal-$\mathrm{CFRTP}$ dissimilar materials

Here, this work proposes an approach to improve the interfacial bonding between carbon-fiber-reinforced thermoplastic polymers (CFRTP) and thermoset adhesive by using the surface modification with the combination of air plasma, thermal, and step-over effects. Thanks to the proper heating which causes the exposure of carbon fibers on the CFRTP surface, both polymer matrix and these exposed carbon fibers can have improved bonding with adhesive due to air plasma treatment. By conducting the Double Cantilever Beam (DCB) tests performed on adhesively-bonded AA5052/CFRP-PA66 dissimilar joints, it was shown in this work that the average Mode I specific fracture energy can be improved up to about 180% compared to non-treated counterparts. The foregoing improvement can be further increased by considering the step-over distance of the surface treatment, which triggers the tortuous damage path in the failure process of adhesively-bonded structures. By manipulating this treatment parameter, often overlooked in the literature, and other parameters (i.e., treatment speed, nozzle tip-to-surface distance, etc.) investigated in this study, the average Mode I specific fracture energy of adhesively-bonded AA5052/CFRP-PA66 dissimilar joints can be improved reaching up to about 410% compared to non-treatment counterparts.