Accommodating a hexagonal ζ- phase Mn 2 N film on a cubic MgO (001) substrate

The thin films of c -plane dominated hexagonal ζ- phase Mn 2 N were successfully grown on a cubic MgO (001) substrate directly using plasma-assisted molecular beam epitaxy. The surface was comprehensively studied through experimental and theoretical approaches. Reflection high energy electron diffraction revealed two pseudo-cubic domains along [100] MgO and [110] MgO , and one hexagonal domain, which is 30° apart from the [100] MgO direction. Scanning tunneling microscopy was used to image and resolve the high-quality surface, revealing a distorted hexagonal surface structure. Furthermore, atomic resolution of the hexagonal domain with a 2 × 2 reconstructed surface is presented. For c-plane surface, theoretical investigations were carried out using first principles studies to determine the surface formation energy for various reconstructed surfaces. The theoretical study shows that the nitrogen terminated 2 × 2 structure with a manganese adatom on the surface as the most stable reconstruction that reproduces the experimental results. A corresponding simulated scanning tunneling microscopy model is also presented, providing strong support for the experimentally observed in-plane lattice structures. Furthermore, the manganese: nitrogen stoichiometry within the bulk and surface is in good agreement with the expected ratio of 2:1.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2024

Co-deposition of bismuth-nitrogen films on MgO (001) by molecular beam epitaxy

Here, we attempted to grow a thin film of BiN by co-deposition of bismuth and nitrogen on rock-salt structure MgO (001) substrates. Furthermore, we studied the effect of variation of the growth temperature and the nitrogen to bismuth flux ratios on sample growth. For the samples grown and conditions used, we do not find strong evidence for the formation of a bulk Bi-N alloy. Even for very high nitrogen to bismuth flux ratio, we observed only bismuth and no nitrogen using bulk Rutherford back-scattering spectroscopy measurements, and only 1%–2% nitrogen was seen through surface Auger electron spectroscopy measurements. The in-plane lattice measurements show that the resulting Bi (110) samples are strained, which is presumably caused by lattice mismatch between the sample and the substrate when grown without any buffer layer. The use of a high-temperature buffer layer helps to release strain in the sample but only along one axis. Measurements of the atomic layer spacing using x-ray diffraction and also scanning tunneling microscopy confirm the Bi (110) thin film sample structure.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2023

Exploring the interfacial structure and crystallinity for direct growth of Mn 3 Sn(0001) on sapphire (0001) by molecular beam epitaxy

The Kagome antiferromagnet Mn 3 Sn has garnered a lot of attention due to the presence of interesting properties such as anomalous Hall effects and Nernst effects. Until now, few papers have been reported to grow using molecular beam epitaxy with a buffer layer or on other substrates. In this paper, we discuss the synthesis of crystalline Mn 3 Sn layers, prepared on Al 2 O 3 (0001) without a buffer layer using molecular beam epitaxy. The growth is monitored in-situ using reflection high energy electron diffraction and measured ex-situ using X-ray diffraction, Rutherford back-scattering, and cross-sectional scanning transmission electron microscopy. The samples were deposited at 524 ± 5 °C, with an Mn: Sn atomic flux ratio of 3.2:1 for 90 minutes. Orientation relationships between the Mn 3 Sn films and the sapphire substrates are determined from in-plane and out-of-plane measurements. Our analysis indicates that the resulting film is predominantly c−plane oriented. Lastly, the samples prepared in this way were found to be discontiguous, showing a 3-dimensional morphology. According to first-principles calculations, the Mn 3 Sn exhibits a displaced Kagome structure in the very first stages of growth, for 2ML and 4ML growth on Al 2 O 3 (0001). This result is corroborated by calculating the surface formation energies and explains the observed RHEED patterns.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2023

Molecular beam epitaxy and crystal structure of majority a -plane-oriented and substrate-strained Mn 3 Sn thin films grown directly on sapphire (0001)

The Kagome antiferromagnet Mn 3 Sn has garnered much attention due to the presence of exciting properties such as anomalous Hall and Nernst effects. This paper discusses the synthesis of crystalline Mn 3 Sn thin films, prepared on Al 2 O 3 (0001) substrates at 453 ± 5°C using molecular beam epitaxy. The growth is monitored in situ using reflection high energy electron diffraction and measured ex situ using x-ray diffraction, Rutherford back-scattering, and cross-sectional scanning transmission electron microscopy. Our analysis shows the in-plane lattice constants of a 1,M = 4.117 ± 0.027 Å and a 2,M = 4.943 ± 0.033 Å, which is a very unexpected result when compared to the bulk a-plane Mn 3 Sn. This indicates a strain in the film and makes it challenging to provide a straightforward explanation. In an effort to explain our results, we discuss two possible orientation relationships between the Mn 3 Sn films and the sapphire substrates. Samples prepared under these conditions appear to have smooth surfaces locally, but overall the film has a 3D island morphology. First-principles calculations provide atomic models of the Mn 3 Sn (112¯0) lattice on Al 2 O 3 (0001) high symmetry sites, indicating that the L3-R90° is the most stable configuration. A detailed discussion of the experimental data and theoretical results, as well as strain effects, is provided.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗