NASA NTRS1981

An evaluation of the sandwich beam compression test method for composites

The sandwich beam in a four-point bending compressive test method for advanced composites is evaluated. Young's modulus and Poisson's ratio were obtained for graphite/polyimide beam specimens tested at 117 K, room temperature, and 589 K. Tensile elastic properties obtained from the specimens were assumed to be equal to the compressive elastic properties and were used in the analysis. Strain gages were used to record strain data. A three-dimensional finite-element model was used to examine the effects of the honeycomb core on measured composite mechanical properties. Results of the analysis led to the following conclusions: (1) a near uniaxial compressive stress state existed in the top cover and essentially all the compressive load was carried by the top cover; (2) laminate orientation, test temperature, and type of honeycomb core material were shown to affect the type of beam failure; and (3) the test method can be used to obtain compressive elastic constants over the temperature range 117 to 589 K.

Shuart, M. J.↗

NASA NTRS1979

Sandwich beam compressive test method

Tests presented show that the sandwich beam in four-point bending could be used to obtain reliable compressive elastic constants for graphite/polyimide laminates although some difficulties were encountered measuring composite compressive strengths. Data were obtained for ultimate stress, ultimate strain, Young's modulus, and Poisson's ratio values in 117K, room temperature, and 589K test environments for the HTS1/PMR-15 material system. A total of 36 compressive tests on various laminates were performed. Also, 24 tensile tests on the same laminate orientations were performed to obtain input to the analytical portion of this program. A portion of the beam test section was analyzed using a linear elastic finite element computer program to predict the stress state in the graphite/polyimide composite. The influence of the honeycomb core of this stress state was analytically determined.

Shuart, M. J.↗

NASA NTRS1978

An evaluation of the sandwich beam in four-point bending as a compressive test method for composites

The experimental phase of the study included compressive tests on HTS/PMR-15 graphite/polyimide, 2024-T3 aluminum alloy, and 5052 aluminum honeycomb at room temperature, and tensile tests on graphite/polyimide at room temperature, -157 C, and 316 C. Elastic properties and strength data are presented for three laminates. The room temperature elastic properties were generally found to differ in tension and compression with Young's modulus values differing by as much as twenty-six percent. The effect of temperature on modulus and strength was shown to be laminate dependent. A three-dimensional finite element analysis predicted an essentially uniform, uniaxial compressive stress state in the top flange test section of the sandwich beam. In conclusion, the sandwich beam can be used to obtain accurate, reliable Young's modulus and Poisson's ratio data for advanced composites; however, the ultimate compressive stress for some laminates may be influenced by the specimen geometry.

Shuart, M. J.↗

NASA NTRS1978

On Poisson's ratio for metal matrix composite laminates

The definition of Poisson's ratio for nonlinear behavior of metal matrix composite laminates is discussed and experimental results for tensile and compressive loading of five different boron-aluminum laminates are presented. It is shown that there may be considerable difference in the value of Poisson's ratio as defined by a total strain or an incremental strain definition. It is argued that the incremental definition is more appropriate for nonlinear material behavior. Results from a (0) laminate indicate that the incremental definition provides a precursor to failure which is not evident if the total strain definition is used.

Herakovich, C. T.↗

NASA NTRS1977

Tensile and compressive test results for metal matrix composites

Experimental results of the mechanical behavior of two metal matrix composite systems at room temperature are presented. Ultimate stress, ultimate strain, Poisson's ratio, and initial Young's Modulus are documented for BORSIC/Aluminum in uniaxial tension and Boron/Aluminum in uniaxial tension and compression. Poisson's ratio is used for nonlinear stress-strain behavior. A comparison of compression results for B/Al as obtained from sandwich beam compression specimens and IITRI coupon compression specimens is presented.

Shuart, M. J.↗