Engineering topics
Shubhashish, Shubhashish
Publications and source records attributed to Shubhashish, Shubhashish.
Stoichiometric metal nitration based novel green synthesis of mesoporous metal oxides and their enhanced heterogeneity
Here, in this work, a general and novel method for the green synthesis of mesoporous metal oxides via stoichiometric metal nitration has been demonstrated. Pluronic surfactants and their effect on synthesis procedures in terms of surface area have been experimentally studied in detail. Contrary to the traditional synthesis procedure, water has been utilized as the solvent and in several cases, such as tin oxide, manganese oxide, aluminum oxide, antimony oxide, zinc oxide, cobalt oxide, copper oxide, yttrium oxide, lanthanum oxide, and silver either the highest or comparable surface areas have been successfully synthesized. Through XRD, and TEM, all materials were observed to be crystalline except silver and magnesium oxide. SEM shows that with an increase in surfactant molar mass agglomeration decreases. Ammonia chemisorption on acidic materials gives quantitative amounts of ammonia chemical bonding with catalysts, whereas carbon dioxide chemisorption gives a quantitative value of CO 2 chemical binding with basic sites. As high as 1901.8 μmol/g and 994.6 μmol/g ammonia chemisorption values for oxides of vanadium and tin were achieved. Amphoteric materials give both acidic and basic enhanced adsorption. Finally, all synthesized materials are studied under organic catalytic transformations. Benzyl bromide is theoretically more active compared with benzylamine and benzyl alcohol which was also experimentally shown through the conversion.
Highly Mesoporous MoO 3 Catalysts for Electrophilic Aromatic Substitution
Not provided.
Microwave Hydrothermal Synthesis of Mesoporous First-Row Transition Metal Ferrites
Not provided.
Magnetically Doped Molybdenum Disulfide Layers for Enhanced Carbon Dioxide Capture
Not provided.
Synthesis of Highly Porous Metal Oxide Nanoparticles for Adsorption Applications
Not provided.
Selenium-doped copper oxide nanoarrays: Robust electrocatalyst for the oxygen evolution reaction with ultralow overpotential
The oxygen evolution reaction (OER) is the key anodic reaction in electrochemical water splitting. OER is a four-electron process with sluggish reaction kinetics. RuO 2 and IrO 2 are the benchmark catalysts for OER. Thus, finding a low-cost, earth-abundant, and stable electrocatalyst for OER is a big challenge. Here in this work, we report OER over Se-CuO/CF nanoarrays with an ultralow overpotential of 440 mV (at 50 mA/cm 2 current density). Se-CuO/CF nanoarray has a TOF of 0.05 s -1 at 300 mV. The catalyst showed consistent OER performance upto1000 cycles run over a period of 10 h. The OER performance of Se-CuO/CF nanoarrays was compared with RuO 2 /CF catalyst and the overpotential for RuO 2 /CF nanoarray was only 10 mV lower than Se-CuO/CF 50 mA/cm 2 current density. Se-CuO/CF nanoarray showed 50 mV lower overpotential than the state of the art RuO 2 /CF catalyst at a current density of 100 mA/cm 2 . The Tafel slope of Se-CuO/CF is 21 mV/decade lower compared to RuO 2 /CF suggesting faster reaction kinetics of Se-CuO/CF. The electrochemical surface area and the conductivity were increased upon doping Se into CuO/CF nanoarrays which can be attributed to enhanced OER performance of the Se-CuO/CF nanoarrays.
Syntheses of gold supported on metal oxides and their application in organic transformations
Herein, we report a general and straightforward synthesis method for gold supported on mesoporous and microporous metal oxides. Supported materials, in general, show higher crystallinity compare to unsupported systems as verified through powder X-ray diffraction (XRD). Also, through XRD, most of the metal is observed to be in its oxide form, whereas the gold support was found to be in its metallic state, which has been further confirmed from TEM. In terms of surface area, the catalyst was not found to follow any trend. Morphology wise, there are no changes observed after doping except in few cases. Combined results from XRD, X-ray fluorescence spectroscopy, Auger, and X-ray photoelectron spectroscopy suggest that gold is mainly in the bulk and very little (0.04% in case of gold doped calcium oxide) or non (in case of gold doped mixed manganese-cerium oxide) on the surface. The presence of Au (0) 4f peaks in XPS further confirms the metallic state of the gold. Oxides of indium, magnesium and calcium have been studied for the organic transformation reactions. An enhancement in activity and product selectivity was observed in the case of the gold supported catalysts. Indium serves as a great catalyst for C–C coupling and electrophilic aromatic substitution reactions and gives >99% conversion. Interestingly, 88% selectivity for C–C coupling and >99% selectivity for aromatic substitution have been achieved at 100 °C and room temperature respectively. Magnesium and calcium give Knoevenagel condensation products. At room temperature with very low catalyst loading, >99% conversion and selectivity were observed for the Knoevenagel reaction with as high as 35.30 TOF. Finally, a mechanism for the C–C coupling reaction has been proposed based on these results.
Selective Oxidative Coupling of Amines Using Mesoporous MoO x Catalysts
In this paper, we report a synthesis method for highly porous molybdenum oxide via molybdenum-oxo cluster formation under acidic conditions providing extraordinary stability. Synthesized materials indicate higher valences of molybdenum as compared to the commercial standards as verified through X-ray photoelectron spectroscopy, electron paramagnetic resonance spectroscopy, and ultraviolet–visible spectroscopy. The formation of a 91% orthorhombic molybdenum oxide bulk structure was verified through powder X-ray diffraction analysis. The effect of the hydrogen peroxide solvent system was optimized to obtain pore diameters as big as 17.4 nm and pore volumes as high as 0.168 cm 3 /g. These materials serve as great catalysts providing excellent yields of imine via amine coupling, having first-order kinetics with a turnover number as good as 27.93 with a slight decrease to 22.04 even after the fourth cycles. Surface hydroxyl species on the catalyst aid in the solid acid catalysis to jump-start the reaction.
Nanoporous Co/Mn-Mixed Metal Oxides Templated via Polysulfones for Amine Oxidation
Herein, we report syntheses of microporous and mesoporous mixed metal oxides templated via an anionic surfactant. The effects of acid treatment, solvent type, and the amount of metal incorporation were investigated. Two different cobalt–manganese oxide spinels that were synthesized with surface areas as high as 137 m 2 /g were obtained. These nanomaterials indicate 3.8 nm monomodal pore sizes with crystallite sizes of 2.4–3.6 nm. 59 Co MASNMR studies have shown that quadrupole coupling values from 1500 to 5000 kHz with asymmetry values ranging from 0.1 to 1 have been used to identify cobalt oxidation states. Amine oxidation was used as a model reaction, which allowed for imide yields of above 90% from benzylamine homocoupling. Finally, the use of these nanoporous oxides allows for a high-yielding homocoupling of benzylamine.