Publications and source records attributed to Signer, H..

9 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1976

Endurance and failure characteristic of main-shaft jet engine bearing at 3 million DN

Groups of thirty 120-mm bore angular-contact ball bearings were endurance tested at a speed of 12,000 and 25,000 rpm (1.44 million and 3.0 million DN, where DN is the product of the bearing bore in mm and the shaft speed in rpm) and a thrust load of 66,721 N. The bearings were manufactured from a single heat of VIM-VAR AISI M-50 steel. At 1.44 million and 3.0 million DN, 84,483 and 74,800 bearing test hours were accumulated, respectively. Test results were compared with similar bearings made from CVM AISI M-50 steel run under the same conditions. Bearing lives at speeds of 3 million DN with the VIM-VAR AISI M-50 steel were nearly equivalent to those obtained at lower speeds. A combined processing and material life factor of 44 was found for VIM-VAR AISI M-50 steel. Continuous running after a spall has occurred at 3.0 million DN can result in a destructive fracture of the bearing inner race.

Bamberger, E. N.↗
NASA NTRS1976

Endurance and failure characteristics of main-shaft jet engine bearings at 3x10 to the 6th power DN

Groups of thirty 120-mm bore angular contact ball bearings were endurance tested at a speed of 12,000 and 25,000 rpm and a thrust load of 66 721 N. The bearings were manufactured from a single heat of VIM-VAR AISI M-50 steel. At 1.44X1 million and 3.0x1 million DN, 84 483 and 74 800 bearing test hours were accumulated, respectively. Test results were compared with similar bearings made from CVM AISI M-50 steel run under the same conditions. Bearing lives at speeds of 3x1 million DN with the VIM-VAR AISI M-50 steel were nearly equivalent to those obtained at lower speeds. A combined processing and material life factor of 44 was found for VIM-VAR AISI M-50 steel. Continuous running after a spall has occurred at 3.0x1 million DN can result in a destructive fracture of the bearing inner race.

Bamberger, E. N.↗
NASA NTRS1975

Operating limitations of high-speed jet-lubricated ball bearings

A parametric study was performed with 120-mm bore angular-contact ball bearings having a nominal contact angle of 20 deg. The bearings either had an inner- or an outer-race land riding cage. Lubrication was by recirculating oil jets. The oil jets either had a single or dual orifice. Thrust load, speed, and lubricant flow rate were varied. Test results were compared with those previously reported and obtained from bearings of the same design which were under-race lubricated but run under the same conditions. Jet lubricated ball bearings were limited to speeds less than 2,500,000 DN. Bearings having inner-race land riding cages produced lower temperatures than bearings with outer-race land riding cages. For a given lubricant flow rate dual orifice jets produced lower bearing temperatures than single orifice jets. However, under-race lubrication produced under all conditions of operation lower bearing temperatures with no apparent bearing speed limitation.

Zaretsky, E. V.↗
NASA NTRS1975

Long life, high speed, thrust-load ball bearings

Long-term bearing operation at three million DN can be achieved with high degree of reliability using full combination of sophisticated but currently available state-of-the-art bearing materials and designs, lubricants, and lubricating techniques.

Signer, H.↗
NASA NTRS1975

Effect of speed and load on ultra-high-speed ball bearings

A study was undertaken to determine the effects of speed and load on the operation of 120-mm bore angular-contact ball bearings at speeds to 25,000 rpm and thrust loads to 22,240 newtons (5000 lb). Bearing temperature and power consumption increased with increases in load and/or speed. The effect of load on temperature and power consumption was small relative to the speed effect. Actual measurements of bearing operating contact angle were in excellent agreement with theoretical predictions. Skidding occurred in the bearing in various amounts, generally increasing with speed at given load. The highest amount of skidding, 6 percent, occurred at the highest speed, 25,000 rpm. No visible damage to the bearing surfaces occurred due to the skidding.

Bamberger, E. N.↗
NASA NTRS1975

Operating limitations of high speed jet lubricated ball bearings

A parametric study was performed with 120-mm bore angular-contact ball bearings having a nominal contact angle of 20 degrees. The bearings had either an inner- or an outer-race land riding cage, and lubrication was by recirculating oil jets which had either a single or dual orifice. Thrust load, speed, and lubricant flow rate were varied. Test results were compared with those previously reported and obtained from bearings of the same design which were under-race lubricated but run under the same conditions. Jet lubricated ball bearings were limited to speeds less than 2,500,000 DN, and bearings having inner-race land riding cages produced lower temperatures than bearings with outer-race land riding cages. For a given lubricant flow rate dual orifice jets produced lower bearing temperatures than single orifice jets, but under-race lubrication produced lower bearing temperatures under all conditions of operation with no apparent bearing speed limitation.

Zaretsky, E. V.↗
NASA NTRS1974

Operating characteristics of 120-millimeter-bore ball bearings at 3 million DN

A parametric study was performed with split inner-race 120-mm-bore angular-contact ball bearings at a speed of 25,000 rpm (3 million DN) at initial contact angles of 20 deg and 24 deg. Provisions were made for outer- and inner-race cooling and for injection of lubricant into the bearing through a number of radial holes in the split inner-race of the bearing. Oil flow and coolant rate to the bearing was controlled and varied for a total up to approximately 3.2 gal/min. Bearing temperature was found to decrease as the total lubricant flow to the bearing increased. However, at intermediate flow rates temperature began to increase with increasing flow. Power consumption increased with increasing flow rate. Bearing operating temperature, differences in temperatures between the inner and outer races, and bearing power consumption can be tuned to any desirable operating requirement. Cage speed increased by not more than 2 percent with increasing oil flow to the inner race.

Zaretsky, E. V.↗
NASA NTRS1973

Parametric study of the lubrication of thrust loaded 120-mm bore ball bearings to 3 million DN

A parametric study was performed with 120-mm bore angular-contact ball bearings under varying thrust loads, bearing and lubricant temperatures, and cooling and lubricant flow rates. Contact angles were nominally 20 and 24 deg with bearing speeds to 3 million DN. Endurance tests were run at 3 million DN and a temperature of 492 K (425 F) with 10 bearings having a nominal 24 deg contact angle at a thrust load of 22241 N (5000 lb). Bearing operating temperature, differences in temperatures between the inner and outer races, and bearing power consumption can be tuned to any desirable operating requirement by varying 4 parameters. These parameters are outer-race cooling, inner-race cooling, lubricant flow to the inner race, and oil inlet temperature. Preliminary endurance tests at 3 million DN and 492 K (425 F) indicate that long term bearing operation can be achieved with a high degree of reliability.

Signer, H.↗