Silberman, E.

Publications and source records attributed to Silberman, E..

9 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1999

In-Situ Optical Determination of Thermomechanical Properties of ZnSe and ZnTe Crystals

At temperatures above 1/2 T(sub m), the generation and movement of dislocations may result due to the load created by the weight of the crystal itself The deformation may be expected to increase the line defect density and may result in generation of low angle grain boundaries, especially in the regions of the crystal attached to the ampule. It has often been suspected that elimination of this effect in space can improve crystallinity of crystals grown under microgravity conditions, however, a direct experimental proof of such relation is still missing. In this work we have designed and built a system of in-situ optical detection and measurement of the mechanical deformations of a crystal wafer under its own weight, and studied the deformation effects as a function of temperature. The results of the measurements for ZnSe and ZnTe crystal wafers will be presented.

Burger, A.↗
NASA NTRS1991

Mapping crystal defects with a digital scanning ultramicroscope

A computer controlled scanning ultramicroscope has been built to assist in the characterization of transparent crystals. The device measures the scattering of a focused He-Ne laser beam by crystalline defects. As an XYZ translation table moves the crystal under the ultramicroscope, the scattered light is measured by a photodetector whose output is digitized and recorded. From this data, contour maps or three dimensional perspective plots of the scattering regions of the crystal can be generated to assist in finding patterns of defects which might be correlated with perturbations in the growth process. The verified resolution of the present instrument is about 1 micrometer, which is limited by the minimum step of the stepper-motor driven translation stages, optical diffraction effects and the sensitivity of the detector at the laser light frequency. The instrument was used to build a database of defects patterns in commercial laboratory grown triglycine sulphate (TGS) crystals, and to map defects in a TGS crystal grown from aqueous solution during the flight of Spacelab 3. This crystal shows indications of a reduction both in the generation of defects at the seed-new growth interface and in their propagation into the new crystal.

Springer, J. M.↗
NASA NTRS1989

Purification, growth, and characterization of Zn(x)Cd(1-x)Se crystals

The purification of starting materials which were used in the growth of Zn(x)Cd(1-x)Se (x = 0.2) single crystals using the traveling solution method (TSM) is reported. Up to 13 cm long single crystals and as grown resistivities of 6 x 10(exp 12) ohm/cm could be achieved. Infrared and Raman spectra of Zn(0.2)Cd(0.8)Se are also presented and discussed.

Silberman, E.↗
NASA NTRS1986

Carrier surface generation and recombination effects in photoconduction of HgI2 single crystals

Dc photoconductivity characteristics of HgI2 single crystals have been measured in the range of 1.75-2.75 eV, using CuI as a transparent electrical contact. Hole and electron photocurrents could be separately measured by applying different voltage polarities to the illuminated electrode. It is shown that charge carrier generation near the surface is highly extrinsic, as displayed by differences in the hole and electron photogeneration spectra. Analysis of the photoconductivity versus voltage characteristics indicates that the hole and electron bulk trapping times satisfy greater than 70 and 3 microsec, respectively. The hole and electron surface recombination velocities were 1.0 x 10 to the 4th cm/s and 8 x 10 to the 5th cm/s, respectively.

Burshtein, Z.↗
NASA NTRS1985

Diffusion of triglycine sulfate in aqueous solution

The diffusion coefficient of triglycine sulfate (TGS) in water was measured for several concentrations over a temperature range of 25 to 55 C. The activation energy for diffusion obtained from these measurements was 4180 cal/mol. No concentration dependence was seen. The maximum difference in D for the various ionic species present was determined by Raman spectroscopy to be about 5 percent.

Kroes, R. L.↗
NASA NTRS1975

Optical effect of the contamination of infrared windows by the outgassing of materials in outer space

The products and kinetics of outgassing from S13G paint were studied by using infrared absorption measurements of the material outgassed (using an evaporation cell and vacuum chamber). Two separate long-term experimental depositions from heated samples of the S13G paint were made. Before each experiment, the vacuum chamber and sample holder were carefully cleaned and outgassed to ensure that subsequent deposits on the colled-window were due only to the products evaporated from the sample. Results of experiments are listed and discussed.

Silberman, E.↗
NASA NTRS1975

Optical effect of the contamination of infrared windows by the outgassing of materials in outer space

The composition and evaporation rate of the outgassing of a space vehicle thermal control paint as a function of temperature were studied. A contamination chamber was designed, constructed, and tested. Samples of thermal control paint were tested to determine if heating to moderate temperatures causes them to release outgassing products which can be collected on a cooled cesium iodide window for identification by IR analysis. Results showed that outgassing of surfaces other than the sample was a problem. Spectral bands of the deposits collected were compared.

Silberman, E.↗
NASA NTRS1972

Hydraulic modeling of heat dispersion in large lakes

Case studies of hydraulic models are described for four major generating plants, including information and maps of thermal distribution. Information is of interest to agencies involved in thermal pollution control.

Silberman, E.↗