5 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2023

Prioritization of Existing Reactor Materials

The Advanced Materials and Manufacturing Technologies (AMMT) Program is aiming at the faster incorporation of new materials and manufacturing technologies into complex nuclear-related systems. An integrated approach, combining advanced characterization, high-throughput and accelerated testing, modeling and simulation, including machine learning and artificial intelligence, will be employed. Although 316H (Fe–[16–18]Cr–[10–14]Ni–[2–3]Mo–[0.04–0.1]C) has been identified as a key alloy to be integrated into the AMMT accelerated alloy qualification approach because of its relevance for many current and future nuclear energy reactors, many other alloys could be considered for the advanced fabrication of innovative, high-performance nuclear components. Argonne National Laboratory (ANL), Idaho National Laboratory (INL), Oak Ridge National Laboratory (ORNL), and Pacific Northwest National Laboratory (PNNL) are collaborating on identifying the most promising alloy candidates relevant for the AMMT Program. A selection criteria matrix was established to evaluate the alloys considering their relative importance and technological readiness levels for nuclear energy applications, with a focus on laser powder bed fusion (LPBF). Because of the broad range of potential candidate alloys, ORNL and INL focused on nickel-based alloys, and ANL and PNNL mainly evaluated iron-based alloys. PNNL previously published material scorecards reports on several key alloys, and this report provides a broader overview of iron- and nickel-based candidate alloys, expending beyond alloys well-known to the nuclear community.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2022

Role of electronic energy loss on defect production and interface stability: Comparison between ceramic materials and high-entropy alloys

High-entropy alloys (HEAs) and some complex alloys exhibit desirable properties and significant structural stability in harsh environments, including possible applications in advanced reactors. Energetic ion irradiation is often used as a surrogate for neutron irradiation; however, the impact of ion electronic energy deposition and dissipation is often neglected. Moreover, differences in recoil energy spectrum and density of cascade events on damage evolution must also be considered. In many chemically complex alloys, the mean free path of electrons is reduced significantly, thus their decreased thermal conductivity and slow dissipation of localized radiation energy can have noticeable effects on displacement cascade evolution that is greatly different from metals with high thermal conductivity. In this work, nanocrystalline HEAs of Ni 20 Fe 20 Co 20 Cr 20 Cu 20 and nonequiatomic (NiFeCoCr) 97 Cu 3 , both having much lower room-temperature thermal conductivity than pure Ni or Fe, are chosen as model HEAs to reveal the role that electronic energy loss during ion irradiation has in complex alloys. The response of nanocrystalline HEAs is investigated under irradiation at room temperature using MeV Ni and Au ions that have different ratios of electronic energy to damage energy, which is the energy dissipated in displacing atoms. Different from previously reported amorphization of nanocrystalline SiC, experimental results on these HEAs show that, similar to the process in nanocrystalline oxide materials, both inelastic thermal spikes via electron–phonon coupling and elastic thermal spikes via collisions among atomic nuclei contribute to the overall grain growth. The growth follows a power law dependence with the total deposited ion energy, and the derived value of the power-exponent suggests that the irradiation-induced instability at and near grain boundaries leads to local rapid atomic rearrangements and consequently grain growth. The high power-exponent value can be attributed to the sluggish diffusion and delayed defect evolution arising from the chemical complexity intrinsic to HEAs. Here, this work calls attention to quantified fundamental understanding of radiation damage processes beyond that of simplified displacement events, especially in simulating neutron environments.

36 MATERIALS SCIENCE↗
DOE OSTI2021

A microscopic and crystallographic study of proton irradiated alloy 718

Solution annealing and age hardening are important processes for achieving good engineering and chemical properties of alloy 718. The composition of alloy 718 also plays an important role as it can affect both mechanical (γ”- and γ’-phase formation) and irradiation behaviors. Therefore, in this study five different sets of alloy 718 samples with two different chemical compositions were fabricated using different processing conditions and irradiated up to 4 dpa. Based on the effects of irradiation on the microstructural data of γ”- and γ’-phases, irradiation-induced dislocation statistics, and crystallographic data, it can be inferred that the samples processed at high solution annealing temperature (1093°C) behave better under irradiation compared to the samples processed at low solution annealing temperatures (945 and 1065°C).

36 MATERIALS SCIENCE↗
DOE OSTI2021

Temperature and time effects of post-weld heat treatments on tensile properties and microstructure of Zircaloy-4

Opportunities exist to expand the application of Zircaloy-4 (Zry-4) into lower-temperature (<100°C) applications. Welded areas within these structures are potential failure points and post-weld heat treatments (PWHTs) are not yet standardized for application in this temperature range. Zry-4 tungsten inert gas (TIG) welds were given PWHTs from 450-900°C with hold times from 0.5-48 hours to investigate changes to tensile properties and microstructure. Treatment of 800°C for 1 hour was found to produce the most ductile material, measured by total elongation of the tensile bar (16.5%). Furthermore, both PWHT time and temperature were observed to increase total elongation, except in extreme (>800°C or >18hours) cases, but the effect of temperature was stronger. The second order cumulative annealing parameter shows a trend with tensile properties. Average grain sizes in the fusion zone and heat affected zone did not change under any of the PWHTs until the development of an undesirable blocky-alpha phase, which was only observed to form in the heat affected zones for hold times greater than 18hr at 800°C.

36 MATERIALS SCIENCE↗