Silva, Chinthaka M.

Publications and source records attributed to Silva, Chinthaka M..

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

On the product phases and the reaction kinetics of carbothermic reduction of UO 2 +C at relatively low temperatures

The synthesis of UC using carbothermic reduction of UO 2 and C mixtures has been well studied at high temperatures. However, the product phase behavior of carbothermic reduction at low temperatures (≤1773 K) is not well studied. Such a study is important as low temperatures permit single phase UC synthesis without forming secondary higher carbides, and it further supports the knowledge base of the process that needs to be used for transuranic elements such as plutonium that have high vapor pressures at elevated temperatures. Therefore, a low temperature carbothermic reduction of two different C/UO 2 molar ratios under inert and reducing environments have been studied here. Two different sample holding crucibles, alumina (Al 2 O 3 ) and graphite, were also used here to differentiate the hypostoichiometric (UC 1-a ) and oxygen dissolved (UC 1-x O x ) uranium monocarbide phases adding more details on the two systems. Also, the reaction kinetics involved in the formation of UC via the carbothermic reduction of UO 2 +C using product phases instead of evolved gases such as carbon monoxide is reported here. Under inert atmospheres but with significant oxygen partial pressures, the low temperature carbothermic reduction of UO 2 +C produced up to 90 wt.% UC 1-x O x type oxycarbides as was confirmed by Xray powder diffraction. Reducing Ar-4%H 2 environments at these temperatures were not successful in synthesizing UC as it reduces the amount of C required for the carbothermic reduction, leaving UC phase at a non-equilibrium state. Inert atmospheres with low or negligible oxygen partial pressures on the other hand produced near stoichiometric UC at high phase purity, especially at 1673 – 1773 K temperature range. An activation energy of 377±75 kJmol -1 was also calculated using product phase concentrations of the carbothermic reduction of UO 2 +C under these inert Ar (g) atmospheres.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Preliminary Characterization and Evaluation on ShAPE Manufactured 316H and ODS Steels

This study provides the first- of- a- kind results of direct tube formation through shear assisted processing and extrusion (ShAPE) for oxide dispersion strengthened (ODS) steel material; previously only bar was successfully made. The Advanced Materials and Manufacturing Technology (AMMT) program develops cross-cutting technologies in support of a broad range of nuclear reactor technologies and maintains U.S. leadership in materials and manufacturing technologies for nuclear energy applications. The overarching vision of AMMT is to accelerate the development, qualification, demonstration, and deployment of advanced materials and manufacturing technologies to enable reliable and economical nuclear energy. Solid-state advanced manufacturing techniques can overcome some of the challenges in liquid-based additive manufacturing processes and should therefore be considered in material design and manufacturing as well. The work presented in this report forms part of a study on solid-state additive manufacturing techniques of 316 stainless steels and ODS steel components and supports the vision and goals of the AMMT program relevant to accelerate the development and deployment of advanced manufacturing processes. Achieving this can provide a safety improvement through larger safety margins, economic benefit for higher efficiency during operation, and a cost reduction through more effective manufacturing processes and less waste.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Studies on Printability Methodologies and Directed-Energy-Deposition-Fabricated Iron Alloys for Nuclear Applications

This report provides results from a printability study of laser directed energy deposition (DED)-based additive manufacturing of nuclear-grade stainless steels as well as DED process parameter development for austenitic Alloy 709 (A709) and ferritic/martensitic Grade 91 (G91) and Grade 92 (G92) steels. The printability study includes the use of machine learning and physics-based modeling via commercial software such as FLOW-3D for insights into the impact of the alloy composition, particularly the carbon content, on the printability of stainless steels during the DED process. In the DED process development work, 1 cm 3 alloy blocks were deposited with broad ranges of laser powers, scan speeds, and hatch spacings to optimize the build quality, resulting in densities of more than 99.8% for all three alloys. The microstructure and mechanical properties were characterized using electron microscopy, X-ray diffraction, and Vickers hardness measurements. Further, tensile samples were extracted from DED-fabricated alloys utilizing the optimized process parameters. The present work provides guidance and progress towards the successful deployment of the DED process for the fabrication of structural components of nuclear reactors.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Development Results on Replacement Materials for Current Scarce or High Supply Chain Risk Materials

In September 2020, the U.S. government issued an executive order to address the threat to the domestic supply chain from its reliance on critical minerals (CMs) from foreign competitors and to support the domestic mining and processing industry. The Advanced Materials and Manufacturing Technology (AMMT) program is addressing this executive order by evaluating advanced manufacturing (AM) and its impact on the demands of CMs for energy production in general and how the deployment of AM in nuclear energy will support the projected goals of the Paris Accord and further a net-zero carbon economy (NZE) by 2050. Three strategic reports were previously prepared by the AMMT program to date and identified two areas for more detailed exploration: (1) the replacement of high-risk CMs such as cobalt and niobium by more abundant minerals and (2) the minimization and utilization of CM waste streams. The design of nuclear materials without critical elements as alloying elements, is a part of the nuclear materials strategy to overcome the critical minerals scarcity. In this report, two approaches are evaluated namely (1) replacement of critical elements as alloying elements in nuclear materials, and (2) the design of a new alloys that does not contain critical minerals as an alloying element.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Nuclear Energy Critical Material Waste Minimization Enabled by AM Techniques

This project provides evidence of the successful recycling of solid waste offcuts resulting from conventional manufacturing processes from three relevant alloys to next-generation nuclear reactor developers, providing a potentially upscalable circular process where no critical elements will be lost. Furthermore, iMOF-based adsorbents were successfully designed for CM extraction from aqueous solution, thereby providing a pathway for future upscaling for salvaging dissolved Ni ions. This research has achieved its goal of showing the impact of novel applications of recycling technologies for solid and liquid wastes that can be upscaled for application.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2024

Formation of uranium oxy-carbide and uranium carbide via conversion of polymer covered uranium dioxide by laser-based thermal processing

Conventional formation of carbonaceous uranium compounds requires bulk processing using furnace-based approaches. Here, a methodology employing polymer covered uranium dioxide and laser-based heating is explored to enable rapid, localized formation of carbonaceous uranium compounds. Specifically, heating of poly(methyl methacrylate) covered uranium dioxide powder to high temperatures using laser irradiation in argon and methane gaseous environments was investigated. Decomposition of material and reactions induced by laser irradiation were probed in situ by residual gas analysis using a benchtop mass spectrometer. In this study, to determine the effect on the resultant material phase, three different process parameters were varied: gaseous atmosphere, laser power, and laser irradiation time. Material processed under varying conditions was analyzed using powder X-ray diffraction and scanning electron microscopy. This work realized the conversion of uranium dioxide into uranium oxy-carbide(s) and uranium carbide(s) phases, at over 60 wt.%, via the polymer surface application and laser-based thermal decomposition methodology.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Laser-Induced Thermal Decomposition of Uranium Coordination Compounds with Non-oxidic Ligands to Produce Nitride and Carbide Materials

The production of ceramics from uranium coordination compounds can be achieved through thermal processing if an excess amount of the desired atoms (i.e., C or N), or reactive gaseous products (e.g., methane or nitrogen oxide) is made available to the reactive uranium metal core via decomposition/fragmentation of the surrounding ligand groups. Here, computational thermodynamic approaches were utilized to identify the temperatures necessary to produce uranium metal from some starting compounds—UI 4 (TMEDA) 2 , UCl 4 (TMEDA) 2 , UCl 3 (pyridine) x , and UI 3 (pyridine) 4 . Experimentally, precursors were irradiated by a laser under various gaseous environments (argon, nitrogen, and methane) creating extreme reaction conditions (i.e., fast heating, high temperature profile >2000 °C, and rapid cooling). Despite the fast dynamics associated with laser irradiation, the central uranium atom reacted with the thermal decomposition products of the ligands yielding uranium ceramics. Residual gas analysis identified vaporized products from the laser irradiation, and the final ceramic products were characterized by powder X-ray diffraction. The composition of the uranium precursor as well as the gaseous environment had a direct impact on the production of the final phases.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Evaluation of printability methodologies and feasibility to down select LBPF steel and other materials for nuclear applications

In this work, new research is underway to produce alloys beyond well-known alloys with modified compositions that are better suited to be produced with additive manufacturing. These alloys can only possess improved radiation tolerance but also improved high temperature strength, creep resistance while also using elements that reduce the amount of activation after irradiation. This work package supports the vision and goals of the Advanced Materials and Manufacturing Technology (AMMT) program relevant to accelerate the development and deployment of advanced manufacturing processes. This work focuses on evaluating the methodology for designing alloys best suited for AM processes based on “printability”, literature research to evaluate and down select steel alloy systems. In this work, microstructural characterization and testing activities have been performed on certain steel alloys to support the efforts from collaborating laboratories during the evaluation and printing of the test articles. The final recommendation will be performed by all four participating laboratories.

316L↗
DOE OSTI2023

Crystallographic Study of Product Phases of Carbothermic Reduction and Nitridation of Hafnium Dioxide

Details of the carbothermic reduction/nitridation to synthesize hafnium nitride (HfN) and hafnium carbide (HfC) are scarce in the literature. Therefore, this current study was carried out to evaluate two pathways for synthesizing these two refractory materials: direct nitridation and carbothermic reduction/nitridation. Two mixtures of hafnium dioxide and carbon with C/HfO 2 molar ratios of 2.15 and 3.1 were nitridized directly using flowing nitrogen gas at elevated temperatures (1300–1700 °C). The 3.1 C/HfO 2 molar ratio mixture was also carbothermically reduced under flowing argon gas to synthesize HfC, which was converted into HfN by introducing a nitridation step under both N 2(g ) and N 2(g) -10% H 2(g) . X-ray diffraction results showed the formation of HfN at 1300 and 1400 °C and HfC 1–y N y at ≥1400 °C under direct nitridation of samples using a C/HfO 2 molar ratio of 2.15. These phase analysis data together with lower lattice strain and greater crystallite sizes of HfC 1–y N y that formed at higher temperatures suggested that the HfC 1–y N y phase is preferred over HfN at those temperatures. Carbothermic reduction of 3.1 C/HfO 2 molar ratio samples under an inert atmosphere produced single-phased HfC with no significant levels of dissolved oxygen. In conclusion, carbothermic reduction nitridation made two phases of different carbon levels (HfC 1–y N y and HfC 1–y 'N y ', where y' < y), while direct nitridation produced a single HfC 1–y N y phase under both N 2 and N 2 -10% H 2 cover gas environments.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Unconventional Pathways to Carbide Phase Synthesis via Thermal Decomposition of UI 4 (1,4-dioxane) 2

UI4(1,4-dioxane) 2 was subjected to laser-based heating-a method that enables localized, fast heating (T > 2000 °C) and rapid cooling under controlled conditions (scan rate, power, atmosphere, etc.)-to understand its thermal decomposition. A predictive computational thermodynamic technique estimated the decomposition temperature of UI 4 (1,4-dioxane) 2 to uranium (U) metal to be 2236 °C, a temperature achievable under laser irradiation. Dictated by the presence of reactive, gaseous byproducts, the thermal decomposition of UI 4 (1,4-dioxane) 2 under furnace conditions up to 600 °C revealed the formation of UO 2 , UI x , and U(C 1–x O x ) y , while under laser irradiation, UI 4 (1,4-dioxane) 2 decomposed to UO 2 , U(C 1–x O x ) y , UC 2–z O z , and UC. Despite the fast dynamics associated with laser irradiation, the central uranium atom reacted with the thermal decomposition products of the ligand (1,4-dioxane = C 4 H 8 O 2 ) instead of producing pure U metal. In conclusion, the results highlight the potential to co-develop uranium precursors with specific irradiation procedures to advance nuclear materials research by finding new pathways to produce uranium carbide.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Impact of Low-Temperature Neutron Irradiation on Tensile Behavior of Base Metal and Electron-Beam Welded 316L Stainless Steel

Here, a study of 316L type stainless steel in its base metal and electron-beam (e-beam) welded conditions was performed to observe the effects of low-temperature (60 °C to 100 °C) neutron irradiation on the tensile behavior of the samples. Fractography was used in understanding the tensile-tested fracture surfaces of the 316L samples in these different forms with the characterization of the both base metal and welded samples using electron microscopy. Irradiation of the tensile specimens made free of defects of cutting and mechanical polishing showed a reduction in their tensile ductility with increased radiation-induced hardening up to 1.40 × 10 19 n/cm 2 (E > 0.1 MeV) fluence that corresponds to 1.1x 10 -2 dpa, even at the low irradiation temperatures. These low-temperature neutron irradiated base metal and e-beam welded 316L specimens also consisted of closely similar fracture surfaces characteristic of ductile rupture.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Dynamic substrate reactions during room temperature heavy ion irradiation of CoCrCuFeNi high entropy alloy thin films

Abstract High entropy alloys (HEAs) are promising materials for various applications including nuclear reactor environments. Thus, understanding their behavior under irradiation and exposure to different environments is important. Here, two sets of near-equiatomic CoCrCuFeNi thin films grown on either SiO 2 /Si or Si substrates were irradiated at room temperature with 11.5 MeV Au ions, providing similar behavior to exposure to inert versus corrosion environments. The film grown on SiO 2 had relatively minimal change up to peak damage levels above 500 dpa, while the film grown on Si began intermixing at the substrate–film interface at peak doses of 0.1 dpa before transforming into a multi-silicide film at higher doses, all at room temperature with minimal thermal diffusion. The primary mechanism is radiation-enhanced diffusion via the inverse Kirkendall and solute drag effects. The results highlight how composition and environmental exposure affect the stability of HEAs under radiation and give insights into controlling these behaviors.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Radiation-Induced Changes in Single Crystal Calcite and Dolomite: Mineral Analogues of Light Water Reactor, Nuclear Power Plant Concrete Aggregates

Two analogues of aggregates (calcite and dolomite) found in nuclear power plant (NPP) concrete have been neutron irradiated to fluences up to 2 × 10 20 n/cm 2 at 52 °C and 4 × 10 19 n/cm 2 at 95 °C (E > 0.1 MeV). X-ray diffraction studies showed that these aging conditions affected crystallography of both calcite and dolomite, with both showing a growth in their unit cells compared to that of the unirradiated samples. Only dolomite samples showed a continuous increase of its lattice parameters with the increase in irradiation. In calcites, the lattice growth with irradiation dissipated after a fluence of 5 × 10 18 n/cm 2 . Radiation-induced disordering of the crystal structure was observed in both materials, while a healing effect of irradiation temperature was mainly observed in calcites. Dislocation densities calculated by using XRD data also supported these observations. Insights made into the unit cells of both minerals by using Fourier synthesis showed that the Mg sites are more prone to the neutron irradiation than the Ca sites, resulting in larger radiation effects and higher disruption in the crystal structure of dolomite than that of calcite. Furthermore, other than the polycrystalline characteristics observed by using TEM, these minerals did not show complete amorphization or significant structural decomposition at the studied irradiation fluences.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Effects of low-temperature neutron irradiation on the microstructure and tensile properties of duplex 2304 stainless steel and its electron-beam welds

A lean duplex stainless steel material (2304-grade) in its base metal and electron beam (e-beam) welded conditions were studied microstructurally and mechanically as a function of irradiation conditions to evaluate its use as a structural material at low temperatures (60–100 °C). Neutron irradiation up to a fluence of 1.40 × 10 19 n/cm 2 (E > 0.1 MeV) or ~0.011 dpa decreased the total elongation of both base metal and e-beam welded samples. Overall, radiation hardening was observed in all the samples. The transversely cut irradiated samples showed some nonuniform quasi-cleavage and shearing in their fracture surfaces, indicating the variance of ductile nature of the two-phased (deformable austenite and harder ferrite) duplex structure. The e-beam welded samples also showed quasi-cleavage fracture, which is a characteristic of radiation-induced embrittlement. Furthermore, these observations of the e-beam welded samples were attributed to the formation of coarse ferrites, grain boundary and intragranular phases such as γ 2 and γ 3 , and minor impurity phases such as CrN and Cr 2 N in the weld pool and/or heat-affected zone of the samples. Radiation-induced elemental segregation was also identified in the post-irradiated base metal.

36 MATERIALS SCIENCE↗
DOE OSTI2021

An evaluation of tri-valent oxide (Cr 2 O 3 ) as a grain enlarging dopant for UO 2 nuclear fuels fabricated under reducing environment

A study was performed to evaluate the microstructure and crystallography of nominally 500–2000 Cr 2 O 3 -doped UO 2 fabricated in a temperature range of 1150–1750°C under reducing experimental conditions. We observed an increase in grain size of the samples with the increase in heat treating temperature as expected. For a given sintering temperature (1700–1750°C), an increase in the grain size was also observed with the increase in Cr 2 O 3 concentration up to a value of ~1000–1200 wppm. A decrease in fission gas release as a function of grain size was estimated for the Cr 2 O 3 -doped UO 2 samples assuming specified post-irradiation annealing conditions. A nearly linear decrease was obtained in the lattice parameter of the Cr 2 O 3 -doped UO 2 fcc phase with the increase in Cr 2 O 3 concentration, especially up to a nominal value of 1000 wppm. The lattice parameter decrease was also persistent with the increase in the average grain size as a result of addition of Cr 2 O 3 into the UO 2 lattice. An increase in the crystallite size and a decrease in the microstrain of the $fcc$ phase were observed with the increase in the average grain size of the samples, indicating a higher crystallinity of the Cr 2 O 3 -doped samples than that of the undoped UO 2 sample.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2021

Microstructural and crystallographic effects of sol-gel synthesized Ti-doped UO 2 sintered under reducing conditions

Titanium (Ti)-doped UO 2 microspheres of three different Ti concentrations (1000, 2000, and 4000 wppm) were synthesized using an internal gelation process. The microspheres were pressed into pellets, and a two-step heat treatment was applied to form monolithic cylindrical pellets with high densities (≥95%TD). Microstructure of these samples consisted of equiaxed grains with >300% increase in average grain size compared to the undoped UO 2 pellets. Secondary Ti-rich chemical phases corresponding to a liquid eutectic formed during sintering were observed at grain boundaries of UO 2 for samples doped with 4000 wppm Ti. Furthermore, these Ti-rich chemical phases were not observed in 1000 or 2000 wppm Ti samples at microscale using electron microscopy investigations. The 0.02–0.04% lower lattice parameter values for the Ti-doped UO 2 samples compared to the undoped UO 2 confirms the incorporation of Ti into the UO 2 lattice.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗