NASA NTRS1986

Solenoid-Simulation Circuit

Electrical properties of solenoids imitated for tests of control circuits. Simulation circuit imitates voltage and current responses of two engine-controlling solenoids. Used in tests of programs of digital engine-control circuits, also provides electronic interface with circuits imitating electrical properties of pressure sensors and linear variable-differential transformers. Produces voltages, currents, delays, and discrete turnon and turnoff signals representing operation of solenoid in engine-control relay. Many such circuits used simulating overall engine circuitry.

Simon, R. A.↗
NASA NTRS1973

Carbon fiber internal pressure vessels

Internal pressure vessels were designed; the filament was wound of carbon fibers and epoxy resin and tested to burst. The fibers used were Thornel 400, Thornel 75, and Hercules HTS. Additional vessels with type A fiber were made. Polymeric linears were used, and all burst testing was done at room temperature. The objective was to produce vessels with the highest attainable PbV/W efficiencies. The type A vessels showed the highest average efficiency: 2.56 x 10 to the 6th power cm. Next highest efficiency was with Thornel 400 vessels: 2.21 x 10 to the 6th power cm. These values compare favorably with efficiency values from good quality S-glass vessels, but strains averaged 0.97% or less, which is less than 1/3 the strain of S-glass vessels.

Simon, R. A.↗
NASA NTRS1973

High modulus filament wound vessels for cryogenic containers in spacecraft.

Compared to metallic vessels, filament-wound vessels for containment of cryogens and high pressure gases offer high potential weight savings for NASA spacecraft applications. Since carbon fiber/epoxy resin composites exhibit high strength-to-density ratios, high-cycle fatigue life, and excellent strain compatibility with internal metallic liners, filament-wound carbon fiber/epoxy resin composites were evaluated for application to cryogenic internal pressure vessels. Compared to room temperature values, the cryogenic strengths of the composites were reduced by about 15% at -423 F (with the exception of one composite) while moduli increased as much as 25%. Filament-wound carbon fiber/epoxy resin vessel specimens, made by three fabricators, defined and solved problems in the processing of these friable high-modulus fibers into structurally efficient vessel specimens.

Simon, R. A.↗
NASA NTRS1972

Carbon fiber composites for cryogenic filament-wound vessels

Advanced unidirectional and bidirectional carbon fiber/epoxy resin composites were evaluated for physical and mechanical properties over a cryogenic to room temperature range for potential application to cryogenic vessels. The results showed that Courtaulds HTS carbon fiber was the superior fiber in terms of cryogenic strength properties in epoxy composites. Of the resin systems tested in ring composites, CTBN/ERLB 4617 exhibited the highest composite strengths at cryogenic temperatures, but very low interlaminar shear strengths at room temperature. Tests of unidirectional and bidirectional composite bars showed that the Epon 828/Empol 1040 resin was better at all test temperatures. Neither fatigue cycling nor thermal shock had a significant effect on composite strengths or moduli. Thermal expansion measurements gave negative values in the fiber direction and positive values in the transverse direction of the composites.