Singh, Chandra Veer | Search NASA

DOE OSTI2021

Deciphering Interfacial Chemical and Electrochemical Reactions of Sulfide-Based All-Solid-State Batteries

Large interfacial resistance resulting from interfacial reactions is widely acknowledged as one of the main challenges in sulfide electrolytes (SEs)-based all-solid-state lithium batteries (ASSLBs). However, the root cause of the large interfacial resistance between the SEs and typical layered oxide cathodes is not fully understood yet. Here we deciphered that interfacial oxygen loss from single-crystal LiNi 0.5 Mn 0.3 Co 0.2 O 2 (SC-NMC532) chemically oxidizes Li 10 GeP 2 S 12 , generating oxygen-containing interfacial species. Meanwhile, the interfacial oxygen loss also induces a structural change of oxide cathodes (layered-to-rocksalt). Besides, the high operation voltage can electrochemically oxidize SEs to form non-oxygen species (e.g. polysulfides). These chemically and electrochemically oxidized species, together with the interfacial structural change, are responsible for the large interfacial resistance at the cathode interface. More importantly, the widely adopted interfacial coating strategy is effective in suppressing chemically oxidized oxygen-containing species and mitigating the coincident interfacial structural change but is unable to prevent electrochemically induced non-oxygen species. These findings provide a deeper insight into the large interfacial resistance between the typical SE and layered oxide cathodes, which may be of assistance for the rational interface design of SE-based ASSLBs in future.

25 ENERGY STORAGE↗

DOE OSTI2020

Electrolyte-phobic Surface for the Next-Generation Nanostructured Battery Electrodes

Nanostructured electrodes are among the most important candidates rationally designed to enable high capacity battery chemistry. Nanostructures can solve issues such as the volume change and mechanical fragmentations. However, the high surface area they usually possess would decrease the Coulombic efficiencies, since the side chemical reactions scale with surface area. Moreover, electrodes comprised of nanomaterials have significant intakes of liquid electrolytes, which reduces the overall energy density and increases the cost of the battery. Here we present a new strategy of limiting effective surface area by introducing an “electrolyte-phobic surface”. In this study, a porous Si anode functions as a model material to demonstrate this concept. Silicon boasts high theoretical capacity, but experiences large volume change during its lithiation and delithiation processes. Porous Si can address this volume change problem with the buffer effect of its inner pores. However, porous silicon shows low initial Coulombic efficiencies and high irreversible lithium loss, owing to its intrinsic high surface area. In this report, a covalently linked perfluorinated surface coating layer on porous Si particles serves as an electrolyte-phobic protection layer, minimizing the accessible surface area for the electrolytes, decreasing the side reactions between the electrolyte and Si surface, and thus significantly enhancing the initial Coulombic efficiencies, up to ~88% compared to ~60% for the pristine porous silicon. Meanwhile, the electrolyte-phobic protection layer of Si particles keeps the silicon surface compatible with the conventional polyvinylidene fluoride (PVDF) binder, which helps to stabilize the Si electrode for long-term battery cycling.

Qian, Chenxi↗