NASA NTRS1997

Joining of Silicon Carbide-Based Ceramic Materials for High Temperature Applications

Joining of high temperature silicon carbide-based ceramics has been a critical issue for their successful application. An affordable, robust technique for joining silicon carbide-based ceramics has been developed and is capable of producing joints that can be tailored for thickness and composition. These joints maintain their mechanical strength up to 1350 C (2462 F) in air. This technique is suitable for the joining of large and complex shaped ceramic components and can be extended to the repair of these materials.

Singh, Mrityunjay↗

NASA NTRS1996

Modified Process For Formation Of Silicon Carbide Matrix Composites

Modified version of process for making SiC-fiber/SiC-matrix composite material reduces damage to SiC (SCS-6) fibers and to carbon-rich coatings on fibers. Modification consists of addition of second polymer-infiltration-and-pyrolysis step to increase carbon content of porous matrix before infiltration with liquid silicon or silicon alloy.

Behrendt, Donald R.↗

NASA NTRS1995

Characterization of SiC (SCS-6) Fiber Reinforced Reaction-Formed Silicon Carbide Matrix Composites

Silicon carbide (SCS-6) fiber reinforced-reaction formed silicon carbide matrix composites were fabricated using NASA's reaction forming process. Silicon-2 at a percent of niobium alloy was used as an infiltrant instead of pure silicon to reduce the amount of free silicon in the matrix after reaction forming. The matrix primarily consists of silicon carbide with a bi-modal grain size distribution. Minority phases dispersed within the matrix are niobium disilicide (NbSi2), carbon and silicon. Fiber push-out tests on these composites determined a debond stress of approx. 67 MPa and a frictional stress of approx. 60 MPa. A typical four point flexural strength of the composite is 297 MPa (43.1 KSi). This composite shows tough behavior through fiber pull out.

Singh, Mrityunjay↗

NASA NTRS1994

Reactive Melt Infiltration Of Silicon Into Porous Carbon

Report describes study of synthesis of silicon carbide and related ceramics by reactive melt infiltration of silicon and silicon/molybdenum alloys into porous carbon preforms. Reactive melt infiltration has potential for making components in nearly net shape, performed in less time and at lower temperature. Object of study to determine effect of initial pore volume fraction, pore size, and infiltration material on quality of resultant product.

Behrendt, Donald R.↗

NASA NTRS1994

Melt-Infiltration Process For SiC Ceramics And Composites

Reactive melt infiltration produces silicon carbide-based ceramics and composites faster and more economically than do such processes as chemical vapor infiltration (CVI), reaction sintering, pressureless sintering, hot pressing, and hot isostatic pressing. Process yields dense, strong materials at relatively low cost. Silicon carbide ceramics and composites made by reactive melt infiltration used in combustor liners of jet engines and in nose cones and leading edges of high-speed aircraft and returning spacecraft. In energy industry, materials used in radiant-heater tubes, heat exchangers, heat recuperators, and turbine parts. Materials also well suited to demands of advanced automobile engines.

Behrendt, Donald R.↗