Sisson, R. D., Jr.

Publications and source records attributed to Sisson, R. D., Jr..

Hydrogen effects on the age hardening behavior of 2024 aluminum

It has been found that the fatigue crack growth rate in aluminum alloys increases significantly in the presence of moisture. This phenomenon along with a moisture effect observed in another context has been attributed to 'embrittlement' of the aluminum by absorbed hydrogen generated by the reaction of moisture with freshly exposed aluminum. A description is given of a number of age hardening experiments involving 2024 aluminum. These experiments show that a mechanism related to the segregation of absorbed hydrogen to the coherent theta-double-prime interfaces may account for the observed reduction in fatigue life. It is pointed out that this segregation promotes a loss of coherency in the hydrogen rich region at a fatigue crack tip. Subsequently, the loss of coherency causes local softening and reduces fatigue life.

Wagner, J. A.↗

The role of microstructure and phase distribution in the failure mechanisms and life prediction model for PSZ coatings

Partially Stabilized Zirconia (PSZ) may become widely used for Thermal Barrier Coatings (TBC). Failure of these coatings can occur due to thermal fatigue in oxidizing atmospheres. The failure is due to the strains that develop due to thermal gradients, differences in thermal expansion coefficients, and oxidation of the bond coating. The role of microstructure and the cubic, tetragonal, and monoclinic phase distribution in the strain development and subsequent failure will be discussed. An X-ray diffraction technique for accurate determination of the fraction of each phase in PSZ will be applied to understanding the phase transformations and strain development. These results will be discussed in terms of developing a model for life prediction in PSZ coatings during thermal cycling.

Sisson, R. D., Jr.↗

Hydrogen suppression of 'ductile' processes

Experimental results are reported for torsional fatigue specimens of high-strength steel 4370 and tensile bars of mild steel A-106 which present evidence of a hydrogen-induced strain-aided hardening effect. These results are consistent with the postulate that hydrogen suppresses ductile processes required for crack initiation at large plastic strains.