CdTe-based thin film photovoltaics: Recent advances, current challenges and future prospects

Cadmium telluride (CdTe)-based cells have emerged as the leading commercialized thin film photovoltaic technology and has intrinsically better temperature coefficients, energy yield, and degradation rates than Si technologies. More than 30 GW peak (GWp) of CdTe-based modules are installed worldwide, multiple companies are in production, modules are shipping at up to 18.6% efficiency, and lab cell efficiency is above 22%. We review developments in the science and technology that have occurred over approximately the past decade. These achievements were enabled by manufacturing innovations and scaling module production, as well as maximizing photocurrent through window layer optimization and alloyed CdSe x Te 1-x (CST) absorbers. Improved chlorine passivation processes, film microstructure, and serendipitous Se defect passivation significantly increased minority carrier lifetime. Efficiencies >22% have been realized for both Cu and As doped CST-based cells. The path to further efficiency gains hinges primarily on increasing open circuit voltage (V oc ) and fill factor (FF) through innovations in materials, fabrication methods, and device stacks. Replacing the longstanding Cu doping with As doping is resulting in better module stability and is being translated to large-scale production. To realize 25% efficiency and >1 V V oc , research and development is needed to increase the minority carrier lifetime beyond 100 ns, reduce grain boundary and interface recombination, and tailor band diagrams at the front and back interfaces. Many of these goals have been realized separately however combining them together using scalable manufacturing approaches has been elusive to date. We review these achievements and outstanding opportunities for this remarkable photovoltaic technology.

14 SOLAR ENERGY↗

Sputter-deposited CdMgTe for rear contact to CdSeTe/CdTe solar cells

CdTe-based photovoltaic device performance improvement is predominantly limited by open-circuit voltage. This work approaches the voltage deficit challenge through the incorporation of a cadmium magnesium telluride (CdMgTe) electron reflector layer at the back of 1.5- μm CdSeTe/CdTe absorbers to reduce back-surface recombination through a conduction band offset. A sputtered CdMgTe electron reflector layer permitted low fabrication temperatures and circumvented the intolerance of CdMgTe to thermal processing present in traditional close-space sublimation (CSS)-deposited CdMgTe devices. Here, we demonstrate that sputtered CdMgTe simultaneously promotes the retention of chlorine passivation and magnesium which is not feasible with CSS fabrication. We also show the importance of the Cu and Te back contact order in CdMgTe devices. Through the optimization of the sputtered CdMgTe substrate temperature, doping, and back structure configuration, 1.5 μm CdSeTe/CdTe devices with a sputtered CdMgTe layer achieved an efficiency of 16.0%, significantly higher than with CSS CdMgTe, and demonstrated partial enactment of electron-reflector behavior.

14 SOLAR ENERGY↗

Mitigation of J–V distortion in CdTe solar cells by Ga-doping of MgZnO emitter

Distortions in the current–voltage curves of CdTe-based thin-film solar cells with MgZnO emitter layers are not uncommon. Even when such distortions are very subtle with standard sunlight, they can be greatly accentuated by the removal of short-wavelength photons with optical filters, and the dark-curve turn-on voltage can be noticeably increased. The strong suggestion is that good J–V curves with full-spectrum light often rely on photogeneration of electrons from trap states in the MgZnO emitter. When the carrier concentration of the CdTe absorber is increased with external doping, there is a corresponding need for a larger MgZnO carrier concentration. Based on the assumption that the emitter carrier concentration needs to be comparable to that of the absorber, Ga-doping of the MgZnO was shown to very nearly eliminate the large filtered-light distortions and is arguably superior to MgZnO that relies on photogeneration. In addition, it was shown that photogeneration and recovery in MgZnO is relatively slow, so that without Ga-doping, the cell efficiency improves gradually for most of an hour in the light, and the turn-on voltage of the dark curve increases on a similar time scale when the light is removed.

36 MATERIALS SCIENCE↗

CdTe‐Based Solar Cells with Variations in Mg Concentration in the MgZnO Emitter

The optimal fraction of Mg incorporation in sputter-deposited Mg X Zn 1−X O (MZO) emitters for thin-film CdTe-based solar cells is evaluated by varying it over a range of x from 0 to 0.35. This range allows a variation in the conduction band offset from −0.1 eV (cliff like) to +0.32 eV (spike like). Here, a maximum efficiency of 18.5% for cells with the bilayer CdSeTe/CdTe absorber occurs at x = 0.15, which corresponds to a spike-like band offset near 0.2 eV, as confirmed by X-ray photoelectron spectroscopy. In addition, good cell performance is seen over a fairly broad range of x extending from 0.1 to 0.25. The MZO optical bandgap increases with the Mg fraction, consistent with an increasing conduction band offset. Temperature-dependent current−voltage measurements and time-resolved photoluminescence show improvement in the emitter/absorber interface with the incorporation of Mg. Capacitance−voltage measurements show that the depletion region extends further into the absorber with more Mg, and X-ray diffraction confirms a change from a hexagonal-dominant crystal structure toward zinc blende at x = 0.35.

14 SOLAR ENERGY↗

Impact of Carrier Concentration and Carrier Lifetime on MgZnO/CdSeTe/CdTe Solar Cells

Here, the performance impact of multiple parameters related to the use of MgZnO (MZO) as the emitter for bilayer CdSeTe/CdTe solar cells has been investigated in detail through numerical simulations. Such a comprehensive study is particularly important, because while cell fabrication using MZO has been highly successful in some cases, it has been less so in others, and it has not been clear which combinations of parameter values are most effective. The parameters considered here include the recombination velocity at the emitter/absorber interface, bulk recombination lifetime, and the carrier concentrations of the emitter and absorber. The ranges chosen for the simulation parameters are those most likely to be found experimentally. The primary finding is that independent of the interfacial recombination velocity and bulk recombination lifetime, the MZO carrier density should be > 1017 cm-3 and in any case greater than that of the absorber to reduce interface recombination. At the same time, a shallow dopant the order of 50 meV or less should reduce SRH recombination in the bulk and enable VOC > 1V.

14 SOLAR ENERGY↗

Close-Space Sublimation-Deposited Ultra-Thin CdSeTe/CdTe Solar Cells for Enhanced Short-Circuit Current Density and Photoluminescence

This work describes the complete fabrication process of thin-absorber cadmium selenium telluride/cadmium telluride photovoltaic devices for enhanced efficiency. Here, the process utilizes an automated in-line vacuum system for close-space sublimation deposition which is scalable from fabrication of small area research devices to large-scale modules.