Ba 4 RuMn 2 O 10 : A Noncentrosymmetric Polar Crystal Structure with Disordered Trimers

Phase-pure polycrystalline Ba 4 RuMn 2 O 10 was prepared and determined to adopt the noncentrosymmetric polar crystal structure (space group Cmc2 1 ) based on results of second harmonic generation, convergent beam electron diffraction, and Rietveld refinements using powder neutron diffraction data. The crystal structure features zigzag chains of corner-shared trimers, which contain three distorted face-sharing octahedra. The three metal sites in the trimers are occupied by disordered Ru/Mn with three different ratios: Ru1:Mn1 = 0.202(8):0.798(8), Ru2:Mn2 = 0.27(1):0.73(1), and Ru3:Mn3 = 0.40(1):0.60(1), successfully lowering the symmetry and inducing the polar crystal structure from the centrosymmetric parent compounds Ba 4 T 3 O 10 (T = Mn, Ru; space group Cmca). The valence state of Ru/Mn is confirmed to be +4 according to X-ray absorption near-edge spectroscopy. Ba 4 RuMn 2 O 10 is a narrow bandgap (~0.6 eV) semiconductor exhibiting spin-glass behavior with strong magnetic frustration and antiferromagnetic interactions.

36 MATERIALS SCIENCE↗
DOE OSTI2023

IrGe 4 : A Predicted Weyl-Metal with a Chiral Crystal Structure

Polycrystalline IrGe4 was synthesized by annealing elements at 800 °C for 240 h, and the composition was confirmed by energy-dispersive X-ray spectroscopy. IrGe 4 adopts a chiral crystal structure (space group P3 1 21) instead of a polar crystal structure (P3 1 ), which was corroborated by the convergent-beam electron diffraction and Rietveld refinements using synchrotron powder X-ray diffraction data. The crystal structure features layers of IrGe 8 polyhedra along the b axis, and the layers are connected by edge- and corner-sharing. Each layer consists of corner-shared [Ir 3 Ge 20 ] trimers, which are formed by three IrGe 8 polyhedra connected by edge-sharing. Temperature-dependent resistivity indicates metallic behavior. The magnetoresistance increases with increasing applied magnetic field, and the nonsaturating magnetoresistance reaches 11.5% at 9 T and 10 K. The Hall resistivity suggests that holes are the majority carrier type, with a carrier concentration of 4.02 × 10 21 cm –3 at 300 K. In conclusion, electronic band structures calculated by density functional theory reveal a Weyl point with a chiral charge of +3 above the Fermi level.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2021

Iridate Li8IrO 6 : An Antiferromagnetic Insulator

In this work, a polycrystalline iridate Li 8 IrO 6 material was prepared via heating Li 2 O and IrO 2 starting materials in a sealed quartz tube at 650 °C for 48 h. The structure was determined from Rietveld refinement of room-temperature powder neutron diffraction data. Li 8 IrO 6 adopts the nonpolar space group $R\bar{3}$ with Li atoms occupying the tetrahedral and octahedral sites, which is supported by the electron diffraction and solid-state 7Li NMR. This results in a crystal structure consisting of LiO 4 tetrahedral layers alternating with mixed IrO 6 and LiO 6 octahedral layers along the crystallographic c -axis. The +4 oxidation state of Ir 4+ was confirmed by near-edge X-ray absorption spectroscopy. An in situ synchrotron X-ray diffraction study of Li 8 IrO 6 indicates that the sample is stable up to 1000 °C and exhibits no structural transitions. Magnetic measurements suggest long-range antiferromagnetic ordering with a Néel temperature (TN) of 4 K, which is corroborated by heat capacity measurements. The localized effective moment $μ_{\text{eff}}$ (Ir) = 1.73 $μ_{\text{B}}$ and insulating character indicate that Li 8 IrO 6 is a correlated insulator. First-principles calculations support the nonpolar crystal structure and reveal the insulating behavior both in paramagnetic and antiferromagnetic states.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Ambient and High Pressure CuNiSb 2 : Metal-Ordered and Metal-Disordered NiAs-Type Derivative Pnictides

The mineral Zlatogorite, CuNiSb 2 , was synthesized in the laboratory for the first time by annealing elements at ambient pressure (CuNiSb 2 -AP). Rietveld refinement of synchrotron powder X-ray diffraction data indicates that CuNiSb 2 -AP crystallizes in the NiAs-derived structure ( P 3 m 1, #164) with Cu and Ni ordering. The structure consists of alternate NiSb 6 and CuSb 6 octahedral layers via face-sharing. The formation of such structure instead of metal disordered NiAs-type structure ( P 6 3 / mm c, #194) is validated by the lower energy of the ordered phase by first-principle calculations. Interatomic crystal orbital Hamilton population, electron localization function, and charge density analysis reveal strong Ni-Sb, Cu-Sb, and Cu-Ni bonding and long weak Sb-Sb interactions in CuNiSb 2 -AP. The magnetic measurement indicates that CuNiSb 2 -AP is Pauli paramagnetic. First-principle calculations and experimental electrical resistivity measurements reveal that CuNiSb 2 -AP is a metal. The low Seebeck coefficient and large thermal conductivity suggest that CuNiSb 2 is not a potential thermoelectric material. Single crystals were grown by chemical vapor transport. The high pressure sample (CuNiSb 2 -8 GPa) was prepared by pressing CuNiSb 2 -AP at 700 °C and 8 GPa. However, the structures of single crystal and CuNiSb 2 -8 GPa are best fit with a disordered metal structure in the P 3 m 1 space group, corroborated by transmission electron microscopy.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗