Correlation among porosity, mechanical properties, morphology, electronic conductivity and electrochemical kinetics of dry-processed electrodes

Dry processing (DP) has received great interest recently, which poses many advantages over the conventional slurry-based processing. Here, this work investigates the effect of compression on electrode mechanical properties, morphology, electronic conductivity, and electrochemical kinetics. Similar to the slurry-based electrodes, LiNi 0.8 Mn 0.1 Co 0.1 O 2 (NMC) cathodes with intermediate porosity (i.e., 32%) demonstrate lowest charge transfer resistance, highest electronic conductivity and best rate performance. Fracture of NMC secondary particles is observed in the dry processed NMC cathodes. Reducing electrode porosity results in more fracture in the NMC secondary particles.

25 ENERGY STORAGE↗

DOE OSTI2023

High-throughput and high-performance lithium-ion batteries via dry processing

A scalable powder-to-electrode dry processing strategy mainly based on powder dry mixing and rolling/calendering is rationally designed. The dry processed electrodes show lower tortuosity compared to that of conventional slurry-based electrodes. The dry-processed high-loading graphite anodes (6.6 mAh cm -2 ) and LiNi 0.6 Mn 0.2 Co 0.2 O 2 cathodes (6.0 mAh cm -2 ) exhibit promising electrochemical performance in half-cells and full-cells. The full-cells with both electrodes from dry processing demonstrates superb rate performance to their counterpart with conventional slurry-based electrodes and delivers of capacity retentions of 74.1 % and 63.6 % over 400 and 800 cycles, respectively. Notably, the initial Coulombic efficiency of the dry processed graphite anodes is low ascribed to polytetrafluoroethylene binder. Finally, the results suggest that dry processing is promising for future lithium-ion battery manufacturing and also pinpoint the needs of modification for the polytetrafluoroethylene binder in the graphite anodes.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗